1、Designation: D5336 09D5336 15Standard Classification System and Basis for Specification forPolyphthalamide (PPA) Injection Molding Materials1This standard is issued under the fixed designation D5336; the number immediately following the designation indicates the year oforiginal adoption or, in the c
2、ase of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers polyphthalamide materials suitable for injection molding.1.2 T
3、he properties included in this specification are those required to identify the compositions covered. Other requirementsnecessary to identify particular characteristics important to specialized applications are to be specified by using suffixes as givenin Section 5. See Guide D5740.1.3 This specific
4、ation allows for the use of recycled materials provided that all specification requirements are met.1.4 This specification is intended to be a means of calling out plastics materials used in the fabrication of end items or parts.It is not intended for the selection of materials. Material selection c
5、an be made by those having expertise in the plastics field onlyafter careful consideration of the design and the performance required of the part, the environment to which it will be exposed,the fabrication process to be employed, the costs involved, and the inherent properties of the material other
6、 than those covered bythis specification.1.5 The values stated in SI units are to be regarded as the standard (see IEEE/ASTM SI-10). The values given in parenthesesare for information only.1.6 The following precautionary caveat pertains only to the test methods portion, Section 12, of this specifica
7、tion: This standarddoes not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of thisstandard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.Specific precau
8、tionary statements are given in Note 6.NOTE 1There is no known ISO equivalent to this specification.2. Referenced Documents2.1 ASTM Standards:2D256 Test Methods for Determining the Izod Pendulum Impact Resistance of PlasticsD618 Practice for Conditioning Plastics for TestingD638 Test Method for Tens
9、ile Properties of PlasticsD648 Test Method for Deflection Temperature of Plastics Under Flexural Load in the Edgewise PositionD790 Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating MaterialsD792 Test Methods for Density and Specific Gravity (Relat
10、ive Density) of Plastics by DisplacementD883 Terminology Relating to PlasticsD1600 Terminology for Abbreviated Terms Relating to PlasticsD2857 Practice for Dilute Solution Viscosity of PolymersD3418 Test Method for Transition Temperatures and Enthalpies of Fusion and Crystallization of Polymers by D
11、ifferentialScanning CalorimetryD3641 Practice for Injection Molding Test Specimens of Thermoplastic Molding and Extrusion MaterialsD3801 Test Method for Measuring the Comparative Burning Characteristics of Solid Plastics in a Vertical PositionD3835 Test Method for Determination of Properties of Poly
12、meric Materials by Means of a Capillary RheometerD3892 Practice for Packaging/Packing of Plastics1 This specificationstandard is under the jurisdiction of ASTM Committee D20 on Plastics and is the direct responsibility of Subcommittee D20.15 on ThermoplasticMaterials (Section D20.15.09).Current edit
13、ion approved Sept. 1, 2009April 1, 2015. Published September 2009April 2015. Originally approved in 1992. Last previous edition approved in 20032009 asD5336 - 03.D5336 - 09. DOI: 10.1520/D5336-09.10.1520/D5336-15.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Cus
14、tomer Service at serviceastm.org. ForAnnual Book ofASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the
15、 previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary o
16、f Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1D4000 Classification System for Specifying Plastic MaterialsD5225 Test Method for Measuring Solution Viscosity of Polymers with a Dif
17、ferential ViscometerD5630 Test Method for Ash Content in PlasticsD5740 Guide for Writing Material Standards in the Classification FormatD6869 Test Method for Coulometric and Volumetric Determination of Moisture in Plastics Using the Karl Fischer Reaction (theReaction of Iodine with Water)E29 Practic
18、e for Using Significant Digits in Test Data to Determine Conformance with SpecificationsIEEE/ASTM SI-10 Standard for Use of the International System of Units (SI): The Modern Metric System2.2 Underwriters Laboratories Standard:UL94 Standard for Tests for Flammability of Plastic Materials32.3 ISO Sta
19、ndards:4ISO 75-1 Determination of Temperature of Deflection Unnder Load Part 1:General Test MethodsISO 75-2 Determination of Temperature of Deflection Unnder Load Part 2: Plastics and EboniteISO 179-1 Determination of Charpy Impact StrengthPart 1: Non-Instrumented Impact TestISO 294-1 Injection Moul
20、ding of Test Specimens of Thermoplastic MaterialsPart 1: General Principles, Multipurpose-TestSpecimens and BarsISO 527-1 Determination of Tensile PropertiesPart 1: General PrinciplesISO 527-2 Determination of Tensile PropertiesPart 2: Testing ConditionsISO 3451-1 Determination of Ash General Method
21、sISO 3451-4 Determination of Ash, PolyamidesISO 15512 Determination of Water Content3. Terminology3.1 DefinitionsThe terminology used in this specification is in accordance with Terminologies D883 and D1600.3.2 Definitions of Terms Specific to This Standard:3.2.1 polyphthalamide, PPA, na polyamide i
22、n which residues of terephthalic acid or isophthalic acid or a combination of thetwo comprise at least 55 molar percentage of the dicarboxylic acid portion of the repeating structural units in the polymer chain.4. Classification4.1 The polyphthalamide materials will be designated“ PPA,” as specified
23、 in Terminology D1600.4.2 Unreinforced polyphthalamide materials are classified into groups according to crystallinity. These groups are subdividedinto classes and grades as shown in Table PPA.NOTE 2An example of this classification system is as follows:The designation PPA0121 would indicate from Ta
24、ble PPA:PPA = Polyphthalamide as found in Terminology D160001 (Group) = Semicrystalline PPA2 (Class) = Low-temperature molding material1 (Grade) = With the corresponding requirements shown in Table PPA4.2.1 To facilitate the incorporation of future or special materials, the “other/unspecified” categ
25、ory (00) for group, (0) for class,and (0) for grade is shown. The basic properties of the material can be obtained from Table A as they apply.4.3 Reinforced and lubricated versions of the polyphthalamide materials are classified in accordance with Tables PPA and A,where Table PPA specifies the unrei
26、nforced material and Table A the properties after the addition of reinforcements or lubricantsat the nominal level indicated (see 4.3.1).4.3.1 A single letter shall be used to indicate the major reinforcement, or filler, or combinations of reinforcements or fillers, orboth, along with two digits tha
27、t indicate the percentage of additive(s) by total mass, with tolerances as tabulated as follows:Symbol Material Tolerance (Based on the Total Mass)C Carbon or graphite fiber 3 %G Glass reinforced 3 %L Lubricants by agreement between the supplier andthe userM Mineral 3 %R Combinations ofreinforcement
28、s or fillers, orboth3 % for the total reinforcement or filler,or both3 Available from Underwriters Laboratories (UL), 333 Pfingsten Rd., Northbrook, IL 60062-2096, http:/.4 Available from American National Standards Institute (ANSI), 25 W. 43rd St., 4th Floor, New York, NY 10036, http:/www.ansi.org.
29、D5336 152TABLE PPA Requirements for Unreinforced Polyphthalamide ResinsGroup Description Class Description Grade DescriptionInherentViscosityAdL/gMeltingTemperature,BCGlassTransitionB ,Tg, C01 semicrystalline 1 high-temperature molding 1 0.80-1.06 305-320 115-1302 0.70-1.00 315-330 115-130PPA 0 Othe
30、r2 low-temperature molding 1 0.80-1.05 320-335 90-1052 0.85-0.95 290-305 85-953 0.85-1.05 300-315 85-950 Other0 Other 0 Other00 Other 0 Other 0 OtherAPractice D2857 or Test Method D5225 with conditions as specified in 12.7 of this specification.BTest Method D3418 using a heating rate of 10C/min.TABL
31、E A Detail Requirements of Special Reinforced PPAs Using ASTM MethodsNOTEAll mechanical properties are determined on dry-as-molded injection molded specimens.Property 0 1 2 3 4 5 6 7 8 9Inherent viscosity,A Test Method D2857,dL/g, minB 0.60 0.7 0.75 0.8 0.85 0.9 0.95 1 CTensile strength, Test Method
32、 D638D ,MPaE (psi), minB 45 (6500) 75 (10 900) 90 (13 000) 100 (14 500) 135 (19 600) 200 (29 000) 230 (33 400) 255 (37 000) CFlexural modulus, Test Method D790F ,GPA (kpsi), minB 1.5 (218) 2.5 (363) 3.0 (435) 5.5 (798) 6.5 (943) 10.0 (1450) 13.5 (1958) 15.0 (2175) CIzod impact, Test Method D256G J/m
33、H(ft-lbf/in), minB 20 (0.38) 40 (0.75) 60 (1.1) 90 (1.6) 100 (1.9) 350 (6.6) 500 (9.4) 650 (12.1) CDeflection Temperature Test MethodD648I , C, minB 100 125 160 185 210 235 260 285 CASee 12.7 of this specification for specific conditions.BUnspecified requirement.CSpecific value must be given in call
34、-out.DTest Method D638, Type I tensile bar. The speed of testing shall be as described in 12.2 of this specification.EMPa 145 = psi.FTest Method D790 with a 1-mm (0.05-in.)/min testing speed.GTest Methods D256, Test Method A.HJ/m 0.01873 = ft-lb/in.ITest Method D648, using 1820-kPa (264-psi) stress.
35、TABLE B Detail Requirements of Special Reinforced PPAs Using ISO MethodsNOTEAll mechanical properties are determined on dry-as-molded injection molded specimens.Property 0 1 2 3 4 5 6 7 8 9Tensile strength, ISO 527 MPa minA B 45 75 90 100 135 200 230 255 CTensile modulus, ISO 527 GPa minD B 1.5 3.5
36、5.5 7.5 9.5 12.0 14.0 18.0 CCharpy, ISO 179-1, J/m2, minE B 2.0 4.0 5.5 7.5 9.0 11.0 13.0 15.0 CDeflection Temperature Under Load,ISO 75-2 method Af, C, minFB 100 125 160 185 210 235 260 285 CTo be determined BAISO 527, Type IA tensile bar. The speed of testing shall be as described in 12.2 of this
37、specification.BUnspecified requirement.CSpecific value must be given in call-out.DISO 527, Type 1A tensile bar. The Speed of testing shall be 1 mm/min.EISO 179-1, Test specimen shall be taken from the center portion of multipurpose tensile bar.FISO 75-2, The test specimen shall be taken from the cen
38、ter portion of the multipurpose tensile bar, 4 mm thick, and tested in the flatwise position.4.3.1.1 This part of the specification uses the type and percentage of additive to designate the modification of the basic material.To facilitate this designation, the type and percentage of additive can be
39、shown on the suppliers technical data sheet unless it isproprietary in nature. If necessary, additional requirements shall be indicated by use of the suffix part of the system, as given inSection 5.4.3.2 Tables A and B Detail RequirementsAn identifying number is made up of the letter “A” or “B,” dep
40、ending on whetherASTM or ISO test methods are used, and five digits comprising the cell numbers in the order in which the properties appear.4.3.2.1 Although the values listed in Tables A and B are necessary to include the range of properties available in existingmaterials, this does not imply that e
41、very possible combination of the properties exists or can be obtained.4.3.3 An example of this classification system for a 33 % glass-reinforced polyphthalamide material, usingASTM test methods(Table A) is as follows:PPA0121G33A56577PPA0121 = Semicrystalline, low-temperature molding grade polyphthal
42、amidefrom Table PPA,G33 = Glass reinforced at 33 % nominal,A = Table A property requirements,5 = Inherent viscosity, min 0.85 dL/g,D5336 1536 = Tensile strength, min 200 MPa,5 = Flexural modulus, min 6.5 GPa,7 = Izod impact, min 500 J/m,7 = Deflection temperature, min 260C, andIf no properties are s
43、pecified, the designation would be PPA0121G33.5. Suffixes5.1 When additional requirements are needed for the materials covered in this specification that are not covered in Tables PPA,A, or B, then those requirements shall be designated through the use of suffixes.5.1.1 A list of suffixes found in C
44、lassification System D4000 (Table 3) is useful for additional requirements as appropriate.5.2 Flammability callouts were changed in 2007. Therefore callouts written before 2007 are different from those written in 2007and later.5.2.1 If the requirements for the polyphthalamide material in 4.3.3 also
45、included flammability requirements, the followingexample illustrates the call-out based on ASTM D4000-04:PPA0121G33A06577FL34PPA0121G33A06577 = Same as 4.3.3F = Flammability requirementsL = UL94 recognition required3 = UL recognition at 0.80-mm min thickness4 = UL rating 94V-05.2.2 The following exa
46、mple illustrates the call-out based on ASTM D4000-07:PPA0121G33A06577FF003PPA0121G33A65770 = Same as 4.3.3F = Flammability requirementsF = Vertical burn rate by ASTM D3801 or UL 94V0 = Rating of designation V-003 = 0.80 mm minimum specimen thickness6. Basic Requirements6.1 Basic requirements from Ta
47、bles PPAandAor B, as they apply, are always in effect unless these requirements are supersededby specific suffix requirements, which always take precedence. Properties in Tables A and B supersede properties in Table PPAwhen reinforced or filled materials are specified.7. General Requirements7.1 The
48、material compositions shall be uniform and shall conform to the requirements specified herein.8. Detail Requirements8.1 Test specimens for the various materials shall conform to the requirements prescribed in Tables PPA and A or B, and thesuffix requirements as they apply.8.2 For the purpose of dete
49、rmining conformance, all specified limits in this specification are absolute limits, as defined inPractice E29.8.2.1 With the absolute method, an observed value or a calculated value is not rounded, but is to be compared directly to thespecified limiting value. Conformance or nonconformance with this specification is based on this comparison.9. Sampling9.1 Sampling shall be statistically adequate to satisfy the requirements of 13.4. A lot of material shall be considered as a unitof manufacture as prepared for shipment, and is permitted to