1、Designation: D 6298 05e1Standard Specification forFiberglass Reinforced Styrene-Butadiene-Styrene (SBS)Modified Bituminous Sheets with a Factory Applied MetalSurface1This standard is issued under the fixed designation D 6298; the number immediately following the designation indicates the year oforig
2、inal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.e1NOTETable 1 was editorially corrected in March 2008.1. Scope1.1 This spe
3、cification covers fiberglass reinforced modifiedbituminous sheet materials that use styrene-butadiene-styrene(SBS) thermoplastic elastomer as the primary modifier and aresurfaced with a factory applied continuous metal foil. Thesematerials are intended for use in the fabrication of multiple plyroofi
4、ng and waterproofing membranes and flashings.1.2 This specification is intended as a material specificationonly. Questions regarding the suitability of the specific roofconstructions or application techniques are beyond the scope ofthis specification.1.3 The specified tests and property limits are i
5、ntended toestablish minimum properties. In place roof system designcriteria such as fire resistance, field strength, impact/punctureresistance, material compatibility, uplift resistance, and others,are factors beyond the scope of this specification.1.4 The values stated in SI units are to be regarde
6、d as thestandard. The inch-pound units given in parentheses are forinformation only.1.5 The following precautionary statement pertains to thetest method portion only, Section 8 of this Specification: Thisstandard does not purport to address all of the safety concerns,if any, associated with its use.
7、 It is the responsibility of the userof this standard to establish appropriate safety and healthpractices and determine the applicability of regulatory limita-tions prior to use.2. Referenced Documents2.1 ASTM Standards:2D 1079 Terminology Relating to Roofing and Waterproof-ingD 5147 Test Methods fo
8、r Sampling and Testing ModifiedBituminous Sheet MaterialD 7051 Test Method for Cyclic Thermal Shock of SBS-Modified Bituminous Roofing Sheets with Factory-Applied Metal Surface3. Terminology3.1 DefinitionsFor definitions of terms used in this speci-fication, refer to Terminology D 1079.4. Materials
9、and Manufacture4.1 In the process of manufacture, the fiberglass reinforce-ment is impregnated and coated on both sides with a SBSmodified bituminous coating. The sheet is surfaced with acontinuous metal foil except for any selvage. The SBS modi-fied bituminous coating shall be permitted to be compo
10、undedwith a mineral stabilizer.4.2 The metal surfacing shall be omitted on any selvage. Toprevent sticking in the roll, the reverse side and any selvageshall be permitted to be covered with a fine mineral surfacingor any other surfacing that will not interfere with adhesion orbonding of the lap duri
11、ng application.1This specification is under the jurisdiction of ASTM Committee D08 onRoofing and Waterproofing and is the direct responsibility of Subcommittee D08.04on Felts and Fabrics.Current edition approved Sept. 1, 2005. Published September 2005. Originallyapproved in 1998. Last previous editi
12、on approved in 2000 as D 6298 00.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM Internationa
13、l, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.4.3 Foil-faced products intended for use where the applica-tion is to be by heat welding (torching) shall meet the minimumback surface coating requirement found in Table 1.5. Physical Properties5.1 The sheet mater
14、ial shall conform to the physical prop-erties prescribed in Table 1.5.2 The finished product shall not crack nor be so sticky asto cause other material damage upon being unrolled at producttemperatures between 4 and 60C (40 and 140F).6. Dimensions, Mass, and Permissible Variations6.1 The width of th
15、e roll shall be as agreed between thepurchaser and the seller and shall not vary more than 61%.6.2 The area of the roll shall not be less than as agreed uponbetween the purchaser and seller.6.3 The selvage width shall be within 66.4 mm (14 in.) ofthe nominal value and shall not be less than 57 mm (2
16、.25 in.).7. Workmanship, Finish and Appearance7.1 The finished product shall be completely coated in acontinuous, unbroken film and shall be free of such defects asholes, ragged or untrue edges, breaks, cracks, tears, protru-sions, delaminations, and indentations.7.2 The metal surface shall be unifo
17、rm in surface andtexture, that is, free from such defects as holes, breaks tears,protrusions, and indentations (except for intended factoryembossing pattern).7.3 The line of demarcation between the metal-surfacedportion of the weather side and any selvage shall be straightand parallel to the edge of
18、 the sheet.7.4 When unrolled on a smooth plane, the sheet shall be flat,straight, and true so the lap will mate with the adjacent sheetwithin the tolerance of the lap without wrinkles, buckles, orfishmouths.8. Sampling and Test Methods8.1 Sample the material and determine the properties de-scribed i
19、n this specification in accordance with Test MethodD 5147 unless otherwise indicated.8.2 Cyclic Thermal ShockSample and test the material inaccordance with Test Method D 7051.9. Inspection9.1 InspectionInspection shall be in accordance with therequirements of this specification.9.2 Inspection Altern
20、ativesAlternative inspection require-ments shall be determined by and as agreed upon between thepurchaser and supplier.10. Rejection and Resubmittal10.1 Failure to ConformFailure to conform to any of therequirements as stated in this specification constitutes groundsfor rejection.10.2 Rejection Redr
21、essThe supplier shall have the right toinspect the rejected materials. The supplier and the purchasershall agree to the quantity of rolls deemed unacceptable. Thesupplier shall then have the right to submit the same number ofnew rolls as replacement.11. Packaging and Package Marking11.1 The finished
22、 material shall be furnished as rolls. Therolls shall be securely wrapped to prevent shifting of materialand to permit normal handling. There shall be no manufactur-ing splices in the roll, and there shall be no more than twopieces.11.2 Unless otherwise agreed upon by the seller and pur-chaser, each
23、 product package shall be plainly marked with thesuppliers name, the product brand, the ASTM designation, thenet coverage area, and the type bitumen if not evident in thelabel name of the product.12. Keywords12.1 glass reinforcement; metal foil surface; modified bitu-minous sheet; styrene-butadiene-
24、styrene (SBS); thermoplasticelastomerTABLE 1 Properties of SBS Modified Bituminous Sheet MaterialsSurfaced With a Factory Applied Metal FoilDescriptionThickness, min 3.4 (134)mm (mils)Net Mass per Unit 3.9 (80)Area, min kg/m2(lb/100 ft2)Back Surface Coating Thickness 1 (40)min, mm (mils)Peak Load 0F
25、 28.0 (160)min. valuekN/m (lbf/in.) 73F 14.9 (85)Elongation at 0F . . . 3Peak Loadmin value % 73F . . . 5Ultimate Elongation 73F . . . 25min value %Tensile-TearStrength, min. 0.53 (120)kN (lbf)Low Temp. Flex 18 (0)max C (F)DimensionalStability, max (%) . . . 0.2Compound Stability 107 (225)min passin
26、g C (F)Cyclic Thermal Shock, 2 (0.2)max. % (mm/m)Water Absorption . . . 1.0max (%)Moisture Content . . . 0.2(max %)D629805e12ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are ex
27、pressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revi
28、sed, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you ma
29、y attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D629805e13