1、Designation: D6602 03b (Reapproved 2010)1Standard Practice forSampling and Testing of Possible Carbon Black FugitiveEmissions or Other Environmental Particulate, or Both1This standard is issued under the fixed designation D6602; the number immediately following the designation indicates the year ofo
2、riginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1NOTEEditorially corrected Annex A1 in May 2010.1. Scope1.1 This practic
3、e covers sampling and testing for distin-guishingASTM type carbon black, in the N100 to N900 series,from other environmental particulates.1.2 This practice requires some degree of expertise on thepart of the microscopist. For this reason, the microscopist musthave adequate training and substantial o
4、n-the-job experience inidentifying the morphological parameters of carbon black. Insupport of this analysis, Donnets book2is highly recom-mended to be used as a technical reference for recognizing andunderstanding the microstructure of carbon black.1.3 The values stated in SI units are to be regarde
5、d asstandard. No other units of measurement are included in thisstandard.1.4 This standard may involve hazardous materials, opera-tions, and equipment. This standard does not purport toaddress all of the safety concerns, if any, associated with itsuse. It is the responsibility of the user of this st
6、andard toestablish appropriate safety and health practices and deter-mine the applicability of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:3D1619 Test Methods for Carbon BlackSulfur ContentD3053 Terminology Relating to Carbon BlackD3849 Test Method for Carbon BlackM
7、orphologicalCharacterization of Carbon Black Using Electron Micros-copy3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 aciniformshaped like a cluster of grapes.3.1.1.1 DiscussionThe spheroidal primary particles ofcarbon black are fused into aggregates of colloidal dimensionfor
8、ming an acinoform morphology.3.1.2 aciniform carboncolloidal carbon having a mor-phology consisting of spheroidal primary particles (nodules)fused together in aggregates of colloidal dimension in a shapehaving grape-like clusters or open branch-like structures3.1.3 carbon black, nan engineered mater
9、ial, primarilycomposed of elemental carbon, obtained from the partialcombustion or thermal decomposition of hydrocarbons, exist-ing in the form of aggregates of aciniform morphology whichare composed of spheroidal primary particles characterized byuniformity of primary particle sizes within a given
10、aggregateand turbostratic layering within the primary particles.3.1.3.1 DiscussionParticle size and aggregate size (num-ber of particles per aggregate) are distributional properties andvary depending on the carbon black grade. Transmissionelectron micrographs shown in Annex 1 of Practice D6602demons
11、trate that while particle and aggregate sizes vary greatlywithin a given grade of carbon black, the primary particle sizeis essentially uniform within an individual aggregate.3.1.4 chain of custodya document describing the condi-tion of a sample during its collection, analysis, and disposal.3.1.5 ch
12、ara particulate larger than 1 m made by incom-plete combustion which may not deagglomerate or disperse byordinary techniques, may contain material which is not black,and may contain some of the original materials cell structure,minerals, ash, cinders, and so forth.3.1.6 fugitive dusttransitory, flee
13、ting material comprisedof particulates foreign to the surface of deposition.3.1.7 fungus, sooty mold, mildewparticulates from a su-perficial growth that grows on living and decaying organicmatter.1This practice is under the jurisdiction of ASTM Committee D24 on CarbonBlack and is the direct responsi
14、bility of Subcommittee D24.66 on Environment,Health, and Safety.Current edition approved Jan. 1, 2010. Published May 2010. Originally approvedin 2000. Last previous edition approved in 2003 as D6602 03b1. DOI: 10.1520/D660203BR10E01.2Hess, W.M. and Herd, C.R., Carbon Black Science and Technology, Ed
15、ited byDonnet, J.B., Bansal, R.C., and Wang, M.J., Marcel Dekker, Inc., New York, NY,1993, pp. 89173.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards D
16、ocument Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.3.1.8 mineral and urban dustairborne, naturally occurringinorganic particulates inherent to the area.3.1.9 pollenparticulates from a mass of micr
17、ospores in aseed plant.3.1.10 rubber dustfinely divided soft particulates abradedfrom rubber.3.1.11 samplea small fractional part of a material or aspecified number of objects that are selected for testing,inspection, or specific observations of particular characteris-tics.3.1.12 soota submicron bla
18、ck powder generally producedas an unwanted by-product of combustion or pyrolysis. Itconsists of various quantities of carbonaceous and inorganicsolids in conjunction with adsorbed and occluded organic tarsand resins.3.1.12.1 DiscussionThe carbonaceous portion also is col-loidal and often has the aci
19、niform morphology. Soot may haveseveral carbon morphologies. Examples of soot are carbonresidues from diesel and gasoline engines, industrial flares,sludge pits, burning tires, and so forth.3.1.13 sticky tapea section of tape with a sticky, solvent-soluble adhesive used in the collection of particle
20、s fromsurfaces.3.1.14 surfacethe outer surface, facing, or exterior bound-ary of an object capable of supporting carbon and other fugitiveand natural occurring dusts and particulates.3.1.15 turbostratica type of graphitic crystallographicstructure in which there is no symmetry along the z-axis.3.2 A
21、cronyms:3.2.1 EDSenergy dispersive spectroscopy associated withSEM and TEM for the identification of elemental composition,3.2.2 LMlight microscope,3.2.3 PLMpolarizing light microscope,3.2.4 SEMscanning electron microscope,3.2.5 TEMtransmission electron microscope.NOTE 1Standard terminology relating
22、 to carbon black can be found inTerminology D3053.4. Summary of Practice4.1 This practice describes the procedures and protocols tofollow in order to collect fugitive emission/environmentalsamples and identify if these samples contain materials con-sistent or inconsistent with manufactured carbon bl
23、ack (re-ferred to simply as carbon black).4.2 Section 6 provides guidelines for proper sampling andhandling of fugitive emission/environmental samples. Section7 describes the analysis of the sample using transmissionelectron microscopy (TEM). This analysis is critical in deter-mining if the collecte
24、d sample is consistent or inconsistent withthe morphology of carbon black. Use of this analysis ismandatory in applying this practice. Section 8 describesadditional ancillary techniques that may be included in asample analysis for purposes of providing supporting informa-tion as to the nature of the
25、 sample material. These aresituation-dependent methods and can provide critical identifi-cation information in certain cases.4.3 A block diagram is presented in Fig. 1 to give a possiblescheme to follow in performing this analysis. However, itshould be noted that this scheme is a suggestion, not are
26、quirement.5. Significance and Use5.1 Particulate emissions are major contributors to air con-tamination in industrial and urban environments. Soot isformed as an unwanted by-product of combustion and conse-quently varies widely with the type of fuel and combustionconditions. Carbon black, on the oth
27、er hand, is purposelyproduced under a controlled set of conditions. Therefore, it isimportant to be able to distinguish carbon black from soot, aswell as other environmental contaminants.6. Sampling6.1 The area to be sampled must be representative of thecontaminated area. For sampling, choose an are
28、a that appearsto contain black particulates. The same general surface shouldbe used for gathering all test samples for each property sitelocation.6.2 Equipment:6.2.1 Polyester/Cotton Balls or Glass Fiber Pads.FIG. 1 Block Diagram of Suggested Analysis Scheme forSamplesD6602 03b (2010)126.2.2 Sticky
29、tape (Scotch Crystal Clear Tape, No. 25 orequivalent).6.2.3 Petri Dishes or Polyethylene Bags.6.3 Samples are to be collected by the following twotechniques in accordance with 6.3.1 and 6.3.2. Precautionsshould be taken to carefully collect, handle, and transportsamples in a manner that will not cau
30、se further contamination.6.3.1 Technique I:Collect the sample by rubbing the surface to be sampled witha pre-weighed polyester ball or glass fiber filter pad with a lightback-and-forth motion to remove surface particulates andsolids. Do not try to remove “old” or aged contaminants fromthe surface. L
31、ight pressure on the ball or pad should besufficient. Place the exposed ball or pad in a plastic bag andlabel.6.3.2 Technique II:Remove particulates and solids from surfaces by placing anappropriate length of sticky tape on the surface to be sampled.Carefully remove the tape and place across a petri
32、 dish openingor in a polyethylene bag. All samples collected must be clearlyidentified at the time of collection. This technique may be usedfor samples intended for further examination via light micros-copy or X-ray spectroscopy or both.6.3.3 All collected samples must be clearly identified at theti
33、me of collection. Measure the surface area sampled to thenearest 60.25 cm2(each measurement has to be taken to thenearest 60.5 cm) and record the measurement in Table 1.These samples may be used for microscopy and TGA analysis.Please note that if TGA analysis is a possibility, the samplesshould be c
34、ollected on the fiber pad instead of the polyesterball.6.4 At the time of sample collection, complete a samplingand meteorology record (Table 2) and also complete a chain ofcustody record (Table 1).6.5 This practice does not preclude examination of samplescollected by other means than the preceding,
35、 such as polyeth-ylene glove wipes, filter paper, samples of clothing, and soforth, or a large sample taken in other containers at a spill site.However, these samples always require thorough identificationtaken at the time of sample collection.6.6 It is advisable in the case of repeated incidents to
36、 cleanthe surface between sampling.7. Examination by Transmission Electron Microscopy(TEM)7.1 Summary of Test Method:7.1.1 This test method is a mandatory evaluation of theaciniform materials present in the sample to determine prima-rily if their morphology is consistent with grape-like orbranch-lik
37、e structures typically associated with carbon blackand soots. In order to discriminate discrete morphologicalparameters, the resolving power of a TEM is required. Inaddition to TEM examination, the ancillary methods in accor-dance with Section 8 may provide supporting information as tothe nature and
38、 amount of the material.7.1.2 The sample is extracted into chloroform by sonication.The resulting suspension is deposited onto a prepared substrateattached to a 200 or 300-mesh copper grid. The grid is placedinto the transmission electron microscope (TEM) and repre-sentative fields are examined. The
39、 aciniform materials are thenevaluated for overall morphology.7.2 Apparatus and Chemicals:7.2.1 Transmission Electron Microscope, equipped with asuitable camera.7.2.2 Ultrasonic Bath or Ultrasonic Probe, of satisfactorypower to disperse the particles.7.2.3 Copper TEM Grids, 3-mm 200 or 300-mesh, wit
40、hcarbon substrate.7.2.4 Scissors.7.2.5 Glass Test Tubes,10by75mm,orGlass Vial,3by5cm.7.2.6 Pipettes, disposable.7.2.7 Chloroform, spectrophotometric grade.7.2.8 Polyester Balls or Glass Fiber Filter Pad.7.3 Procedure:TABLE 1 Chain of Custody RecordSample ID Date Sampled Sampled BySurface AreaSampled
41、Sample Container Comments1.2.3.4.5.SampleNumberRelinquished By Received By Time Date Reason for Change:1.2.3.4.5.Comments:D6602 03b (2010)137.3.1 Snip off an appropriate soiled portion of the polyester/cotton ball or fiber filter pad with a clean pair of scissors andplace in a freshly cleaned test t
42、ube or vial.7.3.2 Add 1 to 4 cm3of chloroform to a test tube or 10 to 20cm3to a glass vial until the entire sample is totally immersedin chloroform.7.3.3 An ultrasonic probe or bath may be used to dispersethe material into chloroform. If an ultrasonic probe is used, setthe vial into a container fill
43、ed with ice and water. Ultrasonicatea sufficient amount of time (typically 10 min) to disperse thematerial. If the sample under examination is not dispersed well,re-prepare the sample using more ultrasonic energy or dilutethe suspension.7.3.4 Place a copper grid with the carbon substrate upwardon a
44、filter membrane. Place the filter membrane in a hood.7.3.5 Using a volumetric pipette, deliver from 5 to 10mm3(L) of the suspension onto the center of the grid and letthe solvent evaporate. When the liquid drop is placed on thegrid it overlaps onto the filter paper resulting in a spot size thatis la
45、rger than the size of the grid.7.3.6 If the spot is exceptionally light, repeat 7.3.5 withadditional drops. Place the remaining suspension back into thetest tube, stopper, and place in the hood.7.3.7 Place the grid on the microscope sample holder andinsert the holder into the column.Atypical acceler
46、ating voltageof 80 KV is sufficient for carbon black. Determine an appro-priate magnification for the particles between 5 000 and100 0003 magnification.7.4 Material Identification:7.4.1 Classify the aggregates as being consistent with orinconsistent with the morphology of aciniform material. Car-bon
47、 black and some soot(s) are considered to contain beaciniform in nature.NOTE 2It is highly recommended to take into consideration thegrades of carbon black manufactured in the area sampled. If acinoformmaterial is found in the sample, it is advisable to also examine possiblemanufactured carbon black
48、s from the area to be used as controls versus theenvironmental sample.7.4.2 If the aggregates are aciniform, then continue with theidentification process. Examine the overall morphology of theaggregate in the magnification range of 30 0003 to 50 0003and examine the microstructure of the primary part
49、icles in therange of 100 0003. In support of the analysis, it is recom-mended to generate photomicrographs of representative fields.Refer to Annex A1 to aid in particle identification.7.4.3 Elemental identification of the aciniform material isassumed to be predominately carbonaceous. If this is notTABLE 2 Sampling and Meteorology RecordSample Identification Number: _Complainant: _Date of Complaint: _