1、Designation: D6665 09 (Reapproved 2014)Standard Practice forEvaluation of Aging Resistance of Pre-stressed PrepaintedMetal in a Boiling Water Test1This standard is issued under the fixed designation D6665; the number immediately following the designation indicates the year oforiginal adoption or, in
2、 the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This practice can be used to evaluate the resistance of apre-stressed prepainted me
3、tal panel to cracking and loss ofadhesion, or both, after accelerated aging by boiling water.Most coil coated products are formed and bent into specificshapes to produce a final product. These operations introducestresses, which may be relieved by cracking of the coating afteraging.1.2 This standard
4、 does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM
5、Standards:2D2794 Test Method for Resistance of Organic Coatings tothe Effects of Rapid Deformation (Impact)D4145 Test Method for Coating Flexibility of PrepaintedSheetE643 Test Method for Ball Punch Deformation of MetallicSheet Material3. Apparatus3.1 Boiling water bath big enough to hold formed tes
6、tspecimens.3.2 10 magnifier (optional).3.3 Scotch #610 adhesive tape or equivalent.4. Reagents4.1 Deionized or other water, as agreed upon by customerand vendor.5. Test Specimen5.1 Bumped, bent, drawn or otherwise deformed samples, tobe agreed upon between customer and vendor. These should beprepare
7、d according to Test Methods D2794, D4145, E643,and/or prepared in a manner agreed upon by customer andvendor.6. Procedure6.1 Examine the test specimens for cracking, flowering andtape pick-off (adhesion loss), and record the results.6.2 Place the formed test specimens in the boiling waterbath for on
8、e (1) min. Different times may be used if agreedupon by customer and vendor.6.3 Remove the test specimens and allow them to air dryand cool to room temperature.6.4 Inspect the test specimens for cracking, flowering andadhesion loss, then repeat the tape adhesion test.7. Report7.1 Report the observat
9、ions regarding cracking, floweringand adhesion loss.7.2 The degree of cracking, flowering and tape pick-offallowed should be agreed upon by customer and vendor.Report cracking, flowering and tape pick-off noted beforeboiling water aging, and cracking and tape pick-off noted afterboiling water aging.
10、 When known, report substrate,pretreatment, coating system, production or preparation dateand any other information request agreed upon between vendorand customer.8. Keywords8.1 aging; bend; boiling water; coil; cracking; deformation;drawn metal; fabrication; flexibility; flowering; impact; pick-off
11、; prepaint; stresses; tape-off1This practice is under the jurisdiction of ASTM Committee D01 on Paint andRelated Coatings, Materials, and Applications and is the direct responsibility ofSubcommittee D01.53 on Coil Coated Metal.Current edition approved July 1, 2014 Published July 2014. Originally app
12、rovedin 2001. Last previous edition approved in 2009 as D6665 09. DOI: 10.1520/D6665-09R14.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Su
13、mmary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of t
14、his standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five y
15、ears andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical comm
16、ittee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19
17、428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 09 (2014)2