1、Designation: E 328 02 (Reapproved 2008)Standard Test Methods forStress Relaxation for Materials and Structures1This standard is issued under the fixed designation E 328; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of l
2、ast revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.INTRODUCTIONThese test methods cover a broad range of testing activities. To aid in locating the subject matterpertinent to a parti
3、cular test, the standard is divided into a general section, which applies to all stressrelaxation tests for materials and structures. This general section is followed by letter-designated partsthat apply to tests for material characteristics when subjected to specific, simple stresses, such asunifor
4、m tension, uniform compression, bending or torsion. To choose from among these types ofstress, the following factors should be considered:(1) When the material data are to be applied to the design of a particular class of component, thestress during the relaxation test should be similar to that impo
5、sed on the component. For example,tension tests are suitable for bolting applications and bending tests for leaf springs.(2) Tension and compression relaxation tests have the advantage that the stress can be reportedsimply and unequivocally. During bending relaxation tests, the state of stress is co
6、mplex, but can beaccurately determined when the initial strains are elastic. If plastic strains occur on application offorce, stresses can usually be determined within a bounded range only. Tension relaxation tests, whencompared to compression tests, have the advantage that it is unnecessary to guar
7、d against buckling.Therefore, when the test method is not restricted by the type of stress in the component, tension testingis recommended.(3) Bending tests for relaxation, when compared to tension and compression tests, have theadvantage of using lighter and simpler apparatus for specimens of the s
8、ame cross-sectional area.Strains are usually calculated from deflection or curvature measurements. Since the specimens canusually be designed so that these quantities are much greater than the axial deformation in a directstress test, strain is more easily measured and more readily used for machine
9、control in the bendingtests. Due to the small forces normally required and the simplicity of the apparatus when static fixturesare sufficient, many specimens can be placed in a single oven or furnace when tests are made atelevated temperatures.1. ScopeNOTE 1The method of testing for the stress relax
10、ation of plastics hasbeen withdrawn from this standard, and the responsibility has beentransferred to Practice D 2991.1.1 These test methods cover the determination of the timedependence of stress (stress relaxation) in materials andstructures under conditions of approximately constant con-straint,
11、constant environment, and negligible vibration. In theprocedures recommended, the material or structure is initiallyconstrained by externally applied forces, and the change in theexternal force necessary to maintain this constraint is deter-mined as a function of time.1.2 Specific methods for conduc
12、ting stress relaxation testson materials subjected to tension, compression, bending andtorsion stresses are described in Parts A, B, C, and D,respectively. These test methods also include recommendationsfor the necessary testing equipment and for the analysis of thetest data.1.3 It is recognized tha
13、t the long time periods required forthese types of tests are often unsuited for routine testing or forspecification in the purchase of material. However, these testsare valuable tools in obtaining practical design information onthe stress relaxation of materials subjected to the conditionsenumerated
14、, and in investigations of the fundamental behaviorof materials.1These test methods are under the jurisdiction of ASTM Committee E28 onMechanical Testing and is the direct responsibility of Subcommittee E28.04 onUniaxial Testing.Current edition approved May 1, 2008. Published December 2008. Original
15、lyapproved in 1967. Last previous approved in 2002 as E 32802.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.1.4 UnitsThe values stated in inch-pound units are to beregarded as standard. The values given in parentheses aremathematic
16、al conversions to SI units that are provided forinformation only and are not considered standard.1.5 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health
17、practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D 2991 Recommended Practice for Testing Stress-Relaxation of Plastics3E4 Practices for Force Verification of Testing MachinesE 8/E 8M Test Methods for Tension Testing of Metal
18、licMaterialsE9 Test Methods of Compression Testing of Metallic Ma-terials at Room TemperatureE83 Practice for Verification and Classification of Exten-someter SystemsE 139 Test Methods for Conducting Creep, Creep-Rupture,and Stress-Rupture Tests of Metallic MaterialsE 1012 Practice for Verification
19、of Test Frame and Speci-men Alignment Under Tensile and Compressive AxialForce Application3. Terminology3.1 Definitions:3.1.1 stress relaxationthe time-dependent decrease instress in a solid under given constraint conditions.3.1.1.1 DiscussionThe general stress relaxation test isperformed by isother
20、mally applying a force to a specimen withfixed value of constraint. The constraint is maintained constantand the constraining force is determined as a function of time.The major problem in the stress relaxation test is that constantconstraint can be very difficult to maintain. The effects on testres
21、ults are very significant and considerable attention must begiven to minimize the constraint variation.Also, experimentersshould determine and report the extent of variation in eachstress relaxation test so that this factor can be taken intoconsideration.3.1.2 initial stress FL2the stress introduced
22、 into aspecimen by imposing the given constraint conditions beforestress relaxation begins.3.1.2.1 DiscussionThere are many methods of performingthe stress relaxation test, each with a different starting proce-dure. However, the constraint is usually obtained initially bythe application of an extern
23、al force at either a specific forceapplication rate or a specific strain rate. The two methods willproduce the characteristic behavior shown in Fig. 1 when theinitial stress, s0, exceeds the proportional limit. Some testingmachines, while reaching the constraint value, do not produce2For referenced
24、ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Withdrawn. The last approved version of this historical standard is referenc
25、edon www.astm.org.FIG. 1 Characteristic Behavior During Force Application Period in a Relaxation TestE 328 02 (2008)2either a constant force application rate or constant strain rate,but something in between. However, the general characteristicsof the data will be similar to those indicated. The stre
26、ssapplication rate in either case should be reasonably rapid, butwithout impact or vibration, so that any relaxation during thestress application period will be small.3.1.3 zero time, t0the time when the given stress orconstraint conditions are initially obtained in a stress relaxationtest.3.1.3.1 D
27、iscussionThe stress relaxation test is consideredto have started at zero time, t0in Fig. 1. This is the referencetime from which the observed reduction in force to maintainconstant constraint is based. Selection of this time does notimply that the force application procedure or period, or both,are n
28、ot significant test parameters. These must always beconsidered in the application of the data.3.1.4 relaxation ratethe absolute value of the slope of therelaxation curve at a given time.3.1.5 spherometeran instrument used to measure circularor spherical curvature.3.1.6 indicated nominal temperature
29、or indicatedtemperaturethe temperature that is indicated by thetemperature-measuring device.4. Summary of Test Methods4.1 In each of the various methods of stress applicationdescribed in the applicable specific sections, the specimen issubjected to an increasing force until the specified initial str
30、ainis attained (see zero time in 3.1.3 and in Fig. 1). For theduration of the test, the specimen constraint is maintainedconstant. The initial stress is calculated from the initial force(moment, torque) as measured at zero time, the specimengeometry, and the appropriate elastic constants, often usin
31、gsimple elastic theory. The remaining stress may be calculatedfrom the force (moment or torque) determined under constraintconditions either continuously (4.1.1), periodically (4.1.2), orby elastic springback at the end of the test period 4.1.3 (seeFig. 3).4.1.1 Readings are taken continuously from
32、a force indica-tor while the apparatus adjusts the force to maintain constraintwithin specified bounds.NOTE 2Most force, moment, or torque measuring devices depend onthe devices elasticity to measure the quantities involved. Therefore, it isnecessary that when using such devices, to maintain the tot
33、al strainconstant within an upper and lower bound as shown in Fig. 4.4.1.2 The force required to lift the specimen just free of oneor more constraints during the test period is measured.4.1.3 The elastic springback is measured after removing thetest stress at the end of the test period.4.2 With 4.1.
34、1 and 4.1.2, a single specimen can be used toobtain data for a curve of stress versus time. With 4.1.3, thesame specimens may be used to determine the remaining orrelaxed stress after various time intervals, if it can be demon-strated for a given material that identical results are obtained ineither
35、 using virgin or reloaded specimens. Otherwise, indi-vidual specimens must be used for each point on the curve.5. Significance and Use5.1 Relaxation test data are necessary when designing mostmechanically fastened joints to assure the permanent tightnessof bolted or riveted assemblies, press or shri
36、nk-fit components,rolled-in tubes, etc. Other applications include predicting thedecrease in the tightness of gaskets, in the hoop stress ofsolderless wrapped connections, in the constraining force ofsprings, and the stability of wire tendons in prestressedconcrete.5.2 The ability of a material to r
37、elax at high-stress concen-trations such as are present at notches, inclusions, cracks,holes, fillets, etc., may be predicted from stress relaxation data.Such test data are also useful to judge the heat-treatmentcondition necessary for the thermal relief of residual internalstresses in forgings, cas
38、tings, weldments, machined or cold-worked surfaces, etc. The tests outlined in these methods arelimited to conditions of approximately constant constraint andenvironment.5.3 The test results are highly sensitive to small changes inenvironmental conditions and thus require precise control oftest cond
39、itions and methods.5.4 The reproducibility of data will depend on the mannerwith which all test conditions are controlled. The effects ofFIG. 2 Typical Relaxation CurvesFIG. 3 Stress-Strain Diagram for Determining Relaxation inStressE 328 02 (2008)3aging or residual stress may significantly affect r
40、esults, as mayvariations in material composition.6. Apparatus6.1 See the appropriate paragraph under each section.6.2 It is recommended that the equipment be located in adraft-free, constant-temperature environment, 6 5F (3C).7. Temperature Control and Measurement7.1 The test space (controlled tempe
41、rature room, furnace, orcold box) should be capable of being maintained at a constanttemperature by a suitable automatic device. This is the mostimportant single factor in a stress relaxation test since the stressrelaxation rate, dimensions, and constraint conditions of thespecimen are dependent upo
42、n the test temperature.Any type ofheating or cooling which permits close temperature control ofthe test space environment is satisfactory.7.2 The temperature should be recorded, preferably continu-ously or at least periodically. Temperature variations of thespecimens from the indicated nominal test
43、temperature due toall causes, including cycling of the controller or position alongthe specimen gage length, should not exceed 6 5F (3C) or61/2 %, whichever is greater. These limits should applyinitially and for the duration of the test.7.3 The combined strain resulting from differential thermalexpa
44、nsion (associated with normal temperature variation of theenvironment) between the test specimen and the constraint andother variations in the constraint (such as elastic follow up)should not exceed 60.000025 in./in. (mm/mm).7.4 Temperature measurement should be made in accor-dance with Practice E 1
45、39.8. Vibration Control8.1 Since stress relaxation tests are quite sensitive to shockand vibration, the test equipment and mounting should belocated so that the specimen is isolated from vibration.9. Test Specimens9.1 The test specimens should be of a shape most appropri-ate for the testing method a
46、nd end use. Wire may be tested inthe “as-received” condition and in the case of metal plate,sheet, strip, bar, or rod, they may be machined to the desiredshape.9.2 Residual stresses may significantly alter the stress relax-ation characteristics of the material and care should be exer-cised in machin
47、ing to prevent alteration of the residual stresses.9.3 Specimens for testing must have a uniform cross-sectionthroughout the gage length and meet the following tolerances:Nominal Diameter or WidthTolerance, % of Diameteror Width0.100 in. (2.5 mm) 60.50.250 in. (6.4 mm) 60.40.375 in. (9.5 mm) 60.30.5
48、00 in. (12.7 mm) 60.210. Environment10.1 If the test temperature is different from ambient,specimens previously fitted with strain gages or extensometersshould be exposed to the test temperature for a period of timesufficient to obtain dimensional stability before starting thetests.10.2 The stress r
49、elaxation test may be started immediatelyupon achieving thermal equilibrium.11. Guide for Processing Test Data11.1 The remaining stress, relaxed stress, or applied forcemay be plotted against time or log time. Log stress versus logtime plots may also be employed.11.2 For convenience in comparing the relative relaxationcharacteristics of materials, the ratio “Fraction Initial StressRelaxed” may be plotted against time. This ratio is thedifference between the initial stress and the remaining stress atany time divided by the initial stress.12. Report12.1 It is re