1、Designation: E 648 06aAn American National StandardStandard Test Method forCritical Radiant Flux of Floor-Covering Systems Using aRadiant Heat Energy Source1This standard is issued under the fixed designation E 648; the number immediately following the designation indicates the year oforiginal adopt
2、ion or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1.
3、Scope1.1 This fire-test-response standard covers a procedure formeasuring the critical radiant flux of horizontally mountedfloor-covering systems exposed to a flaming ignition source ina graded radiant heat energy environment in a test chamber. Aspecimen is mounted over underlayment, a simulated con
4、cretestructural floor, bonded to a simulated structural floor, orotherwise mounted in a typical and representative way.1.2 This fire-test-response standard measures the criticalradiant flux at flame-out. It provides a basis for estimating oneaspect of fire exposure behavior for floor-covering system
5、s.The imposed radiant flux simulates the thermal radiation levelslikely to impinge on the floors of a building whose uppersurfaces are heated by flames or hot gases, or both, from a fullydeveloped fire in an adjacent room or compartment. Thestandard was developed to simulate an important fire exposu
6、recomponent of fires that develop in corridors or exitways ofbuildings and is not intended for routine use in estimatingflame spread behavior of floor covering in building areas otherthan corridors or exitways. See Appendix X1 for informationon proper application and interpretation of experimental r
7、esultsfrom use of this test.1.3 The values stated in SI units are to be regarded as thestandard. The values given in parentheses are for informationonly.1.4 The text of this standard references notes and footnotesthat provide explanatory information. These notes and foot-notes, excluding those in ta
8、bles and figures, shall not beconsidered as requirements of this standard.1.5 This standard is used to measure and describe theresponse of materials, products, or assemblies to heat andflame under controlled conditions but does not by itselfincorporate all factors required for fire-hazard or fire-ri
9、skassessment of materials, products, or assemblies under actualfire conditions1.6 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and deter
10、mine the applica-bility of regulatory limitations prior to use. Specific hazardstatements are given in Section 7.2. Referenced Documents2.1 ASTM Standards:2C 1186 Specification for Flat Non-Asbestos Fiber-CementSheetsE 122 Practice for Calculating Sample Size to Estimate,With a Specified Tolerable E
11、rror, the Average for aCharacteristic of a Lot or ProcessE 136 Test Method for Behavior of Materials in a VerticalTube Furnace at 750CE 171 Specification for Atmospheres for Conditioning andTesting Flexible Barrier MaterialsE 176 Terminology of Fire Standards3. Terminology3.1 DefinitionsSee Terminol
12、ogy E 176 for additional defi-nitions.3.2 Definitions of Terms Specific to This Standard:3.2.1 blackbody temperature, nthe temperature of a per-fect radiatora surface with an emissivity of unity and,therefore, a reflectivity of zero.3.2.2 corridor, nan enclosed space connecting a room orcompartment
13、with an exit. The corridor includes normalextensions, such as lobbies and other enlarged spaces, wherepresent.3.2.3 critical radiant flux, nthe level of incident radiantheat energy on the floor covering system at the most distantflame-out point. It is reported as W/cm2(Btu/ft2s).3.2.4 flame-out, nth
14、e time at which the last vestige offlame or glow disappears from the surface of the test specimen,1This test method is under the jurisdiction of ASTM Committee E05 on FireStandards and is the direct responsibility of Subcommittee E05.22 on SurfaceBurning.Current edition approved April 1, 2006. Publi
15、shed May 2006. Originallyapproved in 1978. Last previous edition approved in 2006 as E 648 06.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document
16、 Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.frequently accompanied by a final puff of smoke; Time 0 is thetime at which the specimen is moved into the chamber and thedoor closed. (See 12.3.)3.2.5
17、floor covering, nan essentially planar material hav-ing a relatively small thickness in comparison to its length orwidth, which is laid on a floor to enhance the beauty, comfort,and utility of the floor.3.2.6 floor covering system, na single material, compositeor assembly comprised of the floor cove
18、ring and relatedinstallation components (adhesive, cushion, etc.), if any.3.2.7 flux profile, nthe curve relating incident radiant heatenergy on the specimen plane to distance from the point ofinitiation of flaming ignition, that is, 0 cm.3.2.8 total flux meter, nthe instrument used to measure thele
19、vel of radiant heat energy incident on the specimen plane atany point.4. Summary of Test Method4.1 The basic elements of the test chamber, Fig. 1, are (1)anair-gas fueled radiant heat energy panel inclined at 30 to anddirected at (2) a horizontally mounted floor covering systemspecimen, Fig. 2. The
20、radiant panel generates a radiant energyflux distribution ranging along the 100-cm length of the testspecimen from a nominal maximum of 1.0 W/cm2to aminimum of 0.1 W/cm2. The test is initiated by open-flameignition from a pilot burner. The distance burned to flame-outis converted to watts per square
21、 centimetre from the flux profilegraph, Fig. 3, and reported as critical radiant flux, W/cm2.5. Significance and Use5.1 This fire test response standard is designed to provide abasis for estimating one aspect of the fire exposure behavior ofa floor-covering system installed in a building corridor. T
22、he testenvironment is intended to simulate conditions that have beenobserved and defined in full scale corridor experiments.5.2 The test is intended to be suitable for regulatory statutes,specification acceptance, design purposes, or development andresearch.5.3 The fundamental assumption inherent in
23、 the test is thatcritical radiant flux is one measure of the sensitivity to flamespread of floor-covering systems in a building corridor.5.4 The test is applicable to floor-covering system speci-mens that follow or simulate accepted installation practice.Tests on the individual elements of a floor s
24、ystem are of limitedvalue and not valid for evaluation of the flooring system.FIG. 1 Flooring Radiant Panel Tester ApparatusE 648 06a2NOTE 1In this procedure, the specimens are subjected to one or morespecific sets of laboratory fire test exposure conditions. If different testconditions are substitu
25、ted or the anticipated end-use conditions arechanged, it may not be possible by or from this test to predict changes inthe performance characteristics measured. Therefore, the results arestrictly valid only for the fire test exposure conditions described in thisprocedure.If the test results obtained
26、 by this method are to be considered in theFIG. 2 Flooring Radiant Panel Test Showing Carpet Specimen and Gas Fueled PanelFIG. 3 Standard Radiant Heat Energy Flux ProfileE 648 06a3total assessment of fire risk, then all pertinent established criteria for firerisk assessment developed by Committee E0
27、5 must be included in theconsideration.6. Flooring Radiant Panel Test ChamberConstructionand Instrumentation6.1 The flooring radiant panel test chamber employed forthis test shall be located in a draft-protected laboratory.6.1.1 The flooring radiant panel test chamber, Fig. 4 andFig. 5, shall consis
28、t of an enclosure 1400 mm (55 in.) long by500 mm (1912 in.) deep by 710 mm (28 in.) above the testspecimen. The sides, ends, and top shall be of 13-mm (12-in.)calcium silicate, 0.74 g/cm3(46 lb/ft3) nominal density, insu-lating material with a thermal conductivity at 177C (350F) of0.128 W/(mK) 0.89
29、Btuin./(hft2F). One side shall beprovided with an approximately 100 by 1100-mm (4 by 44-in.)draft-tight fire-resistant glass window so the entire length of thetest specimen will be observable from outside the fire testchamber. On the same side and below the observation windowis a door that, when ope
30、n, allows the specimen platform to bemoved out for mounting or removal of test specimens. Whenrequired for observation, a draft-tight fire-resistant windowshall be installed at the low flux end of the chamber.6.1.2 The bottom of the test chamber shall consist of asliding steel platform that has prov
31、isions for rigidly securingthe test specimen holder in a fixed and level position. The free,or air access, area around the platform shall be in the rangefrom 2580 to 3225 cm2(400 to 500 in.2).6.1.3 When the rate of flame front advance is to bemeasured, a metal scale marked with 10-mm intervals shall
32、 beinstalled on the back of the platform or on the back wall of thechamber.6.1.4 When the extent of flame travel is to be measured aftera prescribed burning period, for example, 15 min, the metalscale described in 6.1.3 shall be used.6.1.5 The top of the chamber shall have an exhaust stackwith inter
33、ior dimensions of 102 6 3 mm (4.00 6 0.13 in.) wideby 380 6 3 mm (15.00 6 0.13 in.) deep by 318 6 3mm(12.506 0.13 in.) high at the opposite end of the chamber fromthe radiant energy source.6.2 The radiant heat energy source shall be a panel ofporous material mounted in a cast iron or steel frame wit
34、h aradiation surface of 305 by 457 mm (12 by 18 in.). It shall becapable of operating at temperatures up to 816C (1500F).The panel fuel system shall consist of a venturi-type aspiratorFIG. 4 Flooring Radiant Panel Tester Schematic Side ElevationE 648 06a4for mixing gas3and air at approximately atmos
35、pheric pressure,a clean, dry air supply capable of providing 28.3 NTP m3/h(1000 standard ft3/h) at 76 mm (3.0 in.) of water, and suitableinstrumentation for monitoring and controlling the flow of fuelto the panel.6.2.1 The radiant heat energy panel is mounted in thechamber at a nominal angle of 30 6
36、 5 to the horizontalspecimen plane. The radiant panel shall be adjusted to obtainthe flux profile within the limits specified in 10.6. Thehorizontal distance from the 0 mark on the specimen fixture tothe bottom edge (projected) of the radiating surface of thepanel is 89 6 3 mm (3.5 6 0.13 in.). The
37、panel-to-specimenvertical distance is 140 6 3 mm (5.5 6 0.13 in.) (see Fig. 4).6.2.2 The radiation pyrometer for standardizing the thermaloutput of the panel shall be suitable for viewing a circular area254 mm (10 in.) in diameter at a range of about 1.37 m (54 in.).It shall be calibrated over the 4
38、90 to 510C (914 to 950F)operating blackbody temperature range in accordance with theprocedure described in Annex A1.6.2.3 A high impedance or potentiometric voltmeter with asuitable millivolt range shall be used to monitor the output ofthe radiation pyrometer described in 6.2.2.6.3 The specimen hold
39、er (see Fig. 5) shall be constructedfrom heat-resistant stainless steel (AISI Type 300 (UNA-NO8330) or equivalent) having a thickness of 1.98 mm (0.078in.) and an overall dimension of 1140 by 320 mm (45 by 12343Gas used in this test shall be commercial grade propane having a heating valueof approxim
40、ately 83.1 MJ/m3(2500 Btu/ft3), commercial grade methane having aminimum purity of 96 %, or natural gas.FIG. 5 Flooring Radiant Panel Tester Schematic Low Flux End, ElevationE 648 06a5in.) with a specimen opening of 200 by 1000 mm (7.9 by 39.4in.). Six slots shall be cut in the flange on either side
41、 of theholder to reduce warping. The holder shall be fastened to theplatform with two stud bolts at each end.6.4 The pilot burner, used to ignite the specimen, is anominal 6 mm (14 in.) inside diameter, 10 mm (38 in.) outsidediameter stainless steel tube line burner having 19 evenlyspaced 0.7 mm (0.
42、028 in.) diameter (#70 drill) holes drilledradially along the centerline, and 16 evenly spaced 0.7 mm(0.028 in.) diameter (#70 drill) holes drilled radially 60 belowthe centerline (see Fig. 6). In operation, the gas flow is adjustedto 0.085 to 0.100 m3/h (3.0 to 3.5 SCFH) (air scale) flow rate.The p
43、ilot burner is positioned no more than 5 from thehorizontal so the flame generated will impinge on the specimenat the 0 distance burned point (see Fig. 4 and Fig. 5). When theburner is not being applied to the specimen, move it away fromthe ignition position so it is at least 50 mm (2 in.) away from
44、the specimen.6.4.1 With the gas flow properly adjusted and the pilotburner in the test position, the pilot flame shall extend fromapproximately 63.5 mm (2.5 in.) at either end to approximately127 mm (5 in.) at the center.6.4.2 The holes in the pilot burner shall be kept clean.Asoftwire brush has bee
45、n found suitable to remove the surfacecontaminants. Nickel-chromium or stainless steel wire with anoutside diameter of 0.5 mm (0.020 in.) is suitable for openingthe holes.6.5 A 3.2-mm (18-in.) stainless steel sheathed groundedjunction Chromel-Alumel thermocouple shall be located in theflooring radia
46、nt panel test chamber (see Fig. 4 and Fig. 5). Thechamber thermocouple is located in the longitudinal centralvertical plane of the chamber 25 mm (1 in.) down from the topand 102 mm (4 in.) back from inside the exhaust stack.6.5.1 The thermocouple shall be kept clean to ensureaccuracy of readout.6.5.
47、2 An indicating potentiometer with a range from 100 to500C (212 to 932F) shall be used to determine the chambertemperature prior to a test.6.6 An exhaust duct with a capacity of 28.3 to 85 NTPm3/min (1000 to 3000 standard ft3/min) decoupled from thechamber stack by at least 76 mm (3 in.) on all side
48、s and withan effective area of the canopy slightly larger than plane area ofthe chamber with the specimen platform in the out position isused to remove combustion products from the chamber. Withthe panel turned on and the dummy specimen in place, the airflow rate through the stack shall be 76.2 6 15
49、.2 m/min (250 650 ft/min) when measured with a hot wire anemometer about30 s after insertion of the probe into the center of the stackopening at a distance of 152 mm (6 in.) down from the top ofthe stack opening.6.7 The dummy specimen that is used in the flux profiledetermination shall be made of 19-mm (34-in.) inorganic 0.74g/cm3(46 lb/ft3) nominal density calcium silicate board (seeFig. 7). It is 250 mm (10 in.) wide by 1070 mm (42 in.) longwith 27-mm (1116-in.) diameter holes centered on and alongthe centerline at the 100, 200, 300, .