1、Designation: F412 15F412 16Standard Terminology Relating toPlastic Piping Systems1This standard is issued under the fixed designation F412; the number immediately following the designation indicates the year of originaladoption or, in the case of revision, the year of last revision.Anumber in parent
2、heses indicates the year of last reapproval.Asuperscriptepsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope1.1 This terminology is a compilation of definitions of technical terms
3、 used in the plastic piping industry. Terms that aregenerally understood or adequately defined in other readily available sources are not included.1.2 When a term is used in an ASTM document for which Committee F17 is responsible it is included only when judged, afterreview, by Subcommittee F17.91 t
4、o be a generally usable term.1.3 Definitions that are identical to those published by other ASTM committees or other standards organizations are identifiedwith the committee number (for example, D20) or with the abbreviation of the name of the organization (for example, IUPACInternational Union of P
5、ure and Applied Chemistry).1.4 A definition is a single sentence with additional information included in notes.1.5 Definitions are followed by the committee responsible for the standard(s) (for example, F17.26) and standard numbers(s)in which they are used (for example, F714).2. Referenced Documents
6、2.1 ASTM Standards:2C114 Test Methods for Chemical Analysis of Hydraulic CementD256 Test Methods for Determining the Izod Pendulum Impact Resistance of PlasticsD638 Test Method for Tensile Properties of PlasticsD648 Test Method for Deflection Temperature of Plastics Under Flexural Load in the Edgewi
7、se PositionD747 Test Method for Apparent Bending Modulus of Plastics by Means of a Cantilever BeamD790 Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating MaterialsD882 Test Method for Tensile Properties of Thin Plastic SheetingD883 Terminology Rela
8、ting to PlasticsD907 Terminology of AdhesivesD1003 Test Method for Haze and Luminous Transmittance of Transparent PlasticsD1079 Terminology Relating to Roofing and WaterproofingD1238 Test Method for Melt Flow Rates of Thermoplastics by Extrusion PlastometerD1488 Test Method for Amylaceous Matter in
9、AdhesivesD1505 Test Method for Density of Plastics by the Density-Gradient TechniqueD1527 Specification for Acrylonitrile-Butadiene-Styrene (ABS) Plastic Pipe, Schedules 40 and 80 (Withdrawn 2013)3D1785 Specification for Poly(Vinyl Chloride) (PVC) Plastic Pipe, Schedules 40, 80, and 120D2104 Specifi
10、cation for Polyethylene (PE) Plastic Pipe, Schedule 40 (Withdrawn 2010)3D2239 Specification for Polyethylene (PE) Plastic Pipe (SIDR-PR) Based on Controlled Inside DiameterD2241 Specification for Poly(Vinyl Chloride) (PVC) Pressure-Rated Pipe (SDR Series)D2282 Specification for Acrylonitrile-Butadie
11、ne-Styrene (ABS) Plastic Pipe (Withdrawn 2006)31 This terminology is under the jurisdiction of ASTM Committee F17 on Plastic Piping Systems and is the direct responsibility of Subcommittee F17.91 on Editorial andTerminology.Current edition approved June 1, 2015Aug. 1, 2016. Published July 2015August
12、 2016. Originally approved in 1975. Last previous edition approved in 20132015 asF412 13.F412 15. DOI: 10.1520/F0412-15.10.1520/F0412-16.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume in
13、formation, refer to the standards Document Summary page on the ASTM website.3 The last approved version of this historical standard is referenced on www.astm.org.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been
14、 made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.
15、Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1D2444 Test Method for Determination of the Impact Resistance of Thermoplastic Pipe and Fittings by Means of a Tup (FallingWeight)D2447 Specification for Polyethylene (PE) Plastic Pipe, S
16、chedules 40 and 80, Based on Outside Diameter (Withdrawn 2010)3D2513 Specification for Polyethylene (PE) Gas Pressure Pipe, Tubing, and FittingsD2661 Specification for Acrylonitrile-Butadiene-Styrene (ABS) Schedule 40 Plastic Drain, Waste, and Vent Pipe and FittingsD2666 Specification for Polybutyle
17、ne (PB) Plastic Tubing (Withdrawn 2003)3D2680 Specification for Acrylonitrile-Butadiene-Styrene (ABS) and Poly(Vinyl Chloride) (PVC) Composite Sewer PipingD2683 Specification for Socket-Type Polyethylene Fittings for Outside Diameter-Controlled Polyethylene Pipe and TubingD2737 Specification for Pol
18、yethylene (PE) Plastic TubingD2751 Specification for Acrylonitrile-Butadiene-Styrene (ABS) Sewer Pipe and Fittings (Withdrawn 2014)3D2837 Test Method for Obtaining Hydrostatic Design Basis for Thermoplastic Pipe Materials or Pressure Design Basis forThermoplastic Pipe ProductsD2846/D2846M Specificat
19、ion for Chlorinated Poly(Vinyl Chloride) (CPVC) Plastic Hot- and Cold-Water Distribution SystemsD3035 Specification for Polyethylene (PE) Plastic Pipe (DR-PR) Based on Controlled Outside DiameterD3139 Specification for Joints for Plastic Pressure Pipes Using Flexible Elastomeric SealsD3261 Specifica
20、tion for Butt Heat Fusion Polyethylene (PE) Plastic Fittings for Polyethylene (PE) Plastic Pipe and TubingD3309 Specification for Polybutylene (PB) Plastic Hot- and Cold-Water Distribution SystemsD3350 Specification for Polyethylene Plastics Pipe and Fittings MaterialsF402 Practice for Safe Handling
21、 of Solvent Cements, Primers, and Cleaners Used for Joining Thermoplastic Pipe and FittingsF405 Specification for Corrugated Polyethylene (PE) Pipe and Fittings (Withdrawn 2015)3F441/F441M Specification for Chlorinated Poly(Vinyl Chloride) (CPVC) Plastic Pipe, Schedules 40 and 80F442/F442M Specifica
22、tion for Chlorinated Poly(Vinyl Chloride) (CPVC) Plastic Pipe (SDRPR)F449 Practice for Subsurface Installation of Corrugated Polyethylene Pipe for Agricultural Drainage or Water Table ControlF628 Specification for Acrylonitrile-Butadiene-Styrene (ABS) Schedule 40 Plastic Drain, Waste, and Vent Pipe
23、With a CellularCoreF645 Guide for Selection, Design, and Installation of Thermoplastic Water- Pressure Piping SystemsF714 Specification for Polyethylene (PE) Plastic Pipe (DR-PR) Based on Outside DiameterF771 Specification for Polyethylene (PE) Thermoplastic High-Pressure Irrigation Pipeline Systems
24、 (Withdrawn 2013)3F876 Specification for Crosslinked Polyethylene (PEX) TubingF877 Specification for Crosslinked Polyethylene (PEX) Hot- and Cold-Water Distribution SystemsF891 Specification for Coextruded Poly(Vinyl Chloride) (PVC) Plastic Pipe With a Cellular CoreF948 Test Method for Time-to-Failu
25、re of Plastic Piping Systems and Components Under Constant Internal Pressure With FlowF1025 Guide for Selection and Use of Full-Encirclement-Type Band Clamps for Reinforcement or Repair of Punctures or Holesin Polyethylene Gas Pressure PipeF1281 Specification for Crosslinked Polyethylene/Aluminum/Cr
26、osslinked Polyethylene (PEX-AL-PEX) Pressure PipeF1335 Specification for Pressure-Rated Composite Pipe and Fittings for Elevated Temperature Service (Withdrawn 2011)3F1473 Test Method for Notch Tensile Test to Measure the Resistance to Slow Crack Growth of Polyethylene Pipes and ResinsF1488 Specific
27、ation for Coextruded Composite PipeF1499 Specification for Coextruded Composite Drain, Waste, and Vent Pipe (DWV)F1668 Guide for Construction Procedures for Buried Plastic PipeF1733 Specification for Butt Heat Fusion Polyamide(PA) Plastic Fitting for Polyamide(PA) Plastic Pipe and TubingF1760 Specif
28、ication for Coextruded Poly(Vinyl Chloride) (PVC) Non-Pressure Plastic Pipe Having Reprocessed-RecycledContentF1924 Specification for Plastic Mechanical Fittings for Use on Outside Diameter Controlled Polyethylene Gas Distribution Pipeand TubingF1948 Specification for Metallic Mechanical Fittings fo
29、r Use on Outside Diameter Controlled Thermoplastic Gas DistributionPipe and TubingF1970 Specification for Special Engineered Fittings, Appurtenances or Valves for use in Poly (Vinyl Chloride) (PVC) orChlorinated Poly (Vinyl Chloride) (CPVC) SystemsF1973 Specification for Factory Assembled Anodeless
30、Risers and Transition Fittings in Polyethylene (PE) and Polyamide 11(PA11) and Polyamide 12 (PA12) Fuel Gas Distribution SystemsF1986 Specification for Multilayer PipeType 2, Compression Fittings, and Compression Joints for Hot and Cold Drinking-WaterSystemsF1987 Specification for Multilayer Pipe Ty
31、pe 2, Compression Fittings, and Compression Joints for Hydronic Heating SystemsF2145 Specification for Polyamide 11 (PA 11) and Polyamide 12 (PA12) Mechanical Fittings for Use on Outside DiameterControlled Polyamide 11 and Polyamide 12 Pipe and TubingF2158 Specification for Residential Central-Vacuu
32、m Tube and FittingsF2160 Specification for Solid Wall High Density Polyethylene (HDPE) Conduit Based on Controlled Outside Diameter (OD)F412 162F2176 Specification for Mechanical Couplings Used on Polyethylene Conduit, Duct and InnerductF2788/F2788M Specification for Metric and Inch-sized Crosslinke
33、d Polyethylene (PEX) PipeF2818 Specification for Specification for Crosslinked Polyethylene (PEX) Material Gas Pressure Pipe and TubingF2829/F2829M Specification for Metric- and Inch-Sized Crosslinked Polyethylene (PEX) Pipe SystemsF2905/F2905M Specification for Black Crosslinked Polyethylene (PEX)
34、Line Pipe, Fittings and Joints For Oil and GasProducing ApplicationsF2929 Specification for Crosslinked Polyethylene (PEX) Tubing of 0.070 in. Wall and Fittings for Radiant Heating Systems upto 75 psigF2968/F2968M Specification for Black Crosslinked Polyethylene (PEX) Pipe, Fittings and Joints For G
35、as DistributionApplications2.2 ISO Standards:4ISO 3 Preferred NumbersISO 497 Preferred NumbersISO R 161 Pipes of Plastics Materials for the Transport of Fluids (Outside Diameters and Nominal Pressures) Part I, MetricSeriesISO TR 9080 Thermolplastics Pipes for the Transport of Fluids-Methods of Extra
36、polation of Hydrostatic Stress Rupture Datato Determine the Long-Term Hydrostatic Strength of Thermoplastic Pipe Materials2.3 ANSI Standard:4Z17.1 ANSI Preferred Numbers2.4 PPI Standard:5PPI TR-43. Terminologyacceptance testingtesting performed on a product to determine whether or not an individual
37、lot of the product conforms withspecified requirements. F17DISCUSSIONThe number of requirements are usually fewer than for qualification testing (see definition).acetal plastics, nhighly crystalline linear thermoplastic homopolymers or copolymers characterized by repeating oxymethyleneunits. F17acry
38、lonitrile-butadiene-styrene (ABS) pipe and fitting plastics plastics containing polymers or blends of polymers, or both,in which the minimum butadiene content is 6%, the minimum acrylonitrile content is 15 %, the minimum styrene or substitutedstyrene content, or both, is 15 %, and the maximum conten
39、t of all other monomers is not more than 5 %; plus lubricants,stabilizers, and colorants. F17.61 D1527, D2282 17.62 D2680, D2751adhesivea substance capable of holding materials together by surface attachment. F17adhesive bonded jointsee joint, adhesive bonded.adhesive, solventsee solvent cement.adia
40、batic extrusiona method of extrusion in which, after the extrusion apparatus has been heated sufficiently by conventionalmeans to plastify the material, the extrusion process can be continued with the sole source of heat being the conversion of thedrive energy, through viscous resistance of the plas
41、tic mass in the extruder. D20 D883aging, n(1) the effect on materials of exposure to an environment for an interval of time.(1) the effect on materials of exposure to an environment for an interval of time.(2) the process of exposing materials to an environment for an interval of time.(2) the proces
42、s of exposing materials to an environment for an interval of time. D20 D883alloy, nin plastics, two or more immiscible polymers united, usually by another component, to form a plastic resin havingenhanced performance properties. D20 D883allowable stressThe maximum force per unit area that may be saf
43、ely applied to a pipe.DISCUSSION4 Available from American National Standards Institute (ANSI), 25 W. 43rd St., 4th Floor, New York, NY 10036, http:/www.ansi.org.5 Available from Plastics Pipe Institute (PPI), 105 Decker Court, Suite 825, Irving, TX 75062, http:/www.plasticpipe.org.F412 163In Guide F
44、645, the allowable stress is determined by multiplying the hydrostatic design stress (HDS) at 73F by the temperature correction factor.F17.61 F645antioxidant, ncompounding ingredient used to retard deterioration caused by oxidation. F17apparent densitythe weight per unit volume of a material includi
45、ng voids inherent in the material as tested. F17DISCUSSIONThe term bulk density is commonly used for material such as molding powder.approving authoritythe individual official, board, department, or agency established and authorized by a state, county, city, orother political subdivision, created by
46、 law to administer and enforce specified requirements.artificial weatheringexposure to laboratory conditions, which may be cyclic, involving temperature, relative humidity, radiantenergy, or any other conditions or pollutants found in the atmosphere in various geographical areas; or both. F17DISCUSS
47、IONThe interlaboratory exposure conditions are usually intensified beyond those encountered in actual outdoor exposure in an attempt to achieve anaccelerated effect.backfillall material used to fill the trench from bedding to finished surface. F17.65 F449, F1668backfill, finalmaterial used to fill t
48、he trench from initial backfill to finished surface. F17backfill, initialmaterial used to fill the trench from top of bedding to a designated height over the pipe. F17backfill, pipe zonesee pipe zone backfill.backfill, unconsolidatednoncompacted material in place in trench. F17bead-up cycle, npart o
49、f the fusion procedure that insures complete contact between the heater surfaces and the pipe ends byapplying pressure such as fusion joining pressure to force the pipe ends against the heater surfaces.DISCUSSIONThe bead-up cycle begins at initial contact of the pipe ends against the heater and ends when an indication of melt (slight melt bead) is observed aroundthe pipe circumference.beam loadingthe application of a load to a pipe between two points of support, usually expressed in newtons (or pounds-force)and t