1、Designation: F442/F442M 12F442/F442M 13 An American National StandardStandard Specification forChlorinated Poly(Vinyl Chloride) (CPVC) Plastic Pipe(SDRPR)1This standard is issued under the fixed designation F442/F442M; the number immediately following the designation indicates the yearof original ad
2、option or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1
3、. Scope*1.1 This specification covers chlorinated poly(vinyl chloride) (CPVC) pipe made in standard thermoplastic pipe dimensionratios and pressure rated for water (see Appendix). Included are criteria for classifying CPVC plastic pipe materials and CPVCplastic pipe, and requirements and test method
4、s for materials, workmanship, dimensions, sustained pressure, burst pressure,flattening, and extrusion quality. Methods of marking are also given.NOTE 1The CPVC pipe covered by this specification was covered previously in Specification D2241.NOTE 2The sustained and burst pressure test requirements a
5、nd the pressure ratings in the Appendix are calculated from stress values obtained fromtests made on pipe 2 in. (50 mm) and smaller. However, tests on larger pipe have shown these stress values to be valid.1.2 The products covered by this specification are intended for use with the distribution of p
6、ressurized liquids only, which arechemically compatible with the piping materials. Due to inherent hazards associated with testing components and systems withcompressed air or other compressed gases some manufacturers do not allow pneumatic testing of their products. Consult withspecific product/com
7、ponent manufacturers for their specific testing procedures prior to pneumatic testing.NOTE 3Pressurized (compressed) air or other compressed gases contain large amounts of stored energy which present serious saftey hazards shoulda system fail for any reason.1.3 The text of this specification referen
8、ces notes, footnotes, and appendixes which provide explanatory material. These notesand footnotes (excluding those in tables and figures) shall not be considered as requirements of the specification.1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standar
9、d. The values stated in eachsystem may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from thetwo systems may result in non-conformance with the standard.Within the text, the SI units are shown in brackets.1.5 The following safety hazards
10、caveat pertains only to the test methods portion, Section 8, of this specification:This standarddoes not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of thisstandard to establish appropriate safety and health practices and deter
11、mine the applicability of regulatory limitations prior touse.A specific precautionary statement is given in Note 67.2. Referenced Documents2.1 ASTM Standards:2D618 Practice for Conditioning Plastics for TestingD1598 Test Method for Time-to-Failure of Plastic Pipe Under Constant Internal PressureD159
12、9 Test Method for Resistance to Short-Time Hydraulic Pressure of Plastic Pipe, Tubing, and FittingsD1600 Terminology for Abbreviated Terms Relating to PlasticsD1784 Specification for Rigid Poly(Vinyl Chloride) (PVC) Compounds and Chlorinated Poly(Vinyl Chloride) (CPVC)CompoundsD2122 Test Method for
13、Determining Dimensions of Thermoplastic Pipe and FittingsD2241 Specification for Poly(Vinyl Chloride) (PVC) Pressure-Rated Pipe (SDR Series)1 This specification is under the jurisdiction of ASTM Committee F17 on Plastic Piping Systems and is the direct responsibility of Subcommittee F17.25 on Vinyl
14、BasedPipe.Current edition approved May 1, 2012June 1, 2013. Published August 2012June 2012. Originally approved in 1974. Last previous edition approved in 20092012 asF442 09. 12. DOI: 10.1520/F0442_F0442M-12.10.1520/F0442_F0442M-13.2 For referencedASTM standards, visit theASTM website, www.astm.org,
15、 or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes
16、have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official
17、document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1D2837 Test Method for Obtaining Hydrostatic Design Basis for Thermoplastic Pipe Materials or Pressure Design Bas
18、is forThermoplastic Pipe ProductsF412 Terminology Relating to Plastic Piping Systems2.2 Federal Standard:Fed. Std. No. 123 Marking for Shipment (Civil Agencies)32.3 Military Standard:MIL-STD-129 Marking for Shipment and Storage32.4 NSF Standards:Standard No. 14 for Plastic Piping Components and Rela
19、ted Materials4Standard No. 61 for Drinking Water Systems ComponentsHealth Effects43. Terminology3.1 DefinitionsDefinitions are in accordance with Terminology F412, and abbreviations are in accordance with TerminologyD1600, unless otherwise specified. The abbreviation for chlorinated poly(vinyl chlor
20、ide) plastic is CPVC.3.2 Definitions of Terms Specific to This Standard:3.2.1 hydrostatic design stress the estimated maximum tensile stress the material is capable of withstanding continuously witha high degree of certainty that failure of the pipe will not occur. This stress is circumferential whe
21、n internal hydrostatic waterpressure is applied.3.2.2 pressure rating (PR)the estimated maximum water pressure the pipe is capable of withstanding continuously with ahigh degree of certainty that failure of the pipe will not occur.3.2.3 relation between standard dimension ratio, hydrostatic design s
22、tress, and pressure ratingthe following expression,commonly known as the ISO equation,5 is used in this specification to relate standard dimension ratio, hydrostatic design stress,and pressure rating:2S/P 5 R 21or2S/P 5 D o /t! 21where:S = hydrostatic design stress, psi MPa,P = pressure rating, psi
23、kPa,D o = average outside diameter, in. mmt = minimum wall thickness, in. mm, andR = standard thermoplastic pipe dimension ratio (Do /t for CPVC pipe), also known as SDR.3.2.4 standard thermoplastic pipe dimension ratio (SDR)the standard thermoplastic pipe dimension ratio (SDR) is the ratioof pipe d
24、iameter to wall thickness. For CPVC pipe it is calculated by dividing the average outside diameter of the pipe inmillimetres or in inches by the minimum wall thickness in millimetres or in inches. If the wall thickness calculated by this formulais less than 0.060 in. 1.52 mm, it shall be arbitrarily
25、 increased to 0.060 in. 1.52 mm. The SDR values shall be rounded to thenearest 0.5.3.2.5 standard thermoplastic pipe materials designation codethe pipe materials designation code shall consist of theabbreviation CPVC for the type of plastic, followed by theASTM type and grade inArabic numerals and t
26、he design stress at 73F23C in units of 100 psi 690 kPa with any decimal figures dropped, followed by the design stress at 180F 82C in units of100 psi 0.7 MPa with any decimal figures dropped. When the design stress code contains less than two figures, a cipher shallbe used before the number. Thus a
27、complete material code shall consist of four letters and foursix figures for CPVC plastic pipematerials (see Section 5 and, Note 5 and X1.2.1).4. Classification4.1 GeneralThis specification covers CPVC pipe made from one CPVC plastic pipe material in six standard dimension ratiosand water pressure r
28、atings for nonthreaded pipe.4.2 Standard Thermoplastic Pipe Dimension Ratios (SDR)This specification covers CPVC pipe in six standard dimensionratios, namely, 11, 13.5, 17, 21, 26, and 32.5, which are uniform for all nominal pipe sizes for each material and pressure rating.These are referred to as S
29、DR11, SDR13.5, SDR21, SDR17, SDR26, and SDR32.5, respectively. The pressure rating is uniformfor all nominal pipe sizes for a given CPVC pipe material and SDR (see Table X1.1).4.3 Hydrostatic Design StressesThis specification covers CPVC pipe made from CPVC plastic as defined by hydrostaticdesign st
30、resses developed on the basis of long-term tests (see Appendix).NOTE 4This standard specification does not include requirements for pipe and fittings intended to be used to vent combustion gases.3 Available from Standardization Documents Order Desk, DODSSP, Bldg. 4, Section D, 700 Robbins Ave., Phil
31、adelphia, PA 19111-5098, http:/www.dodssp.daps.mil.4 Available from NSF International, P.O. Box 130140, 789 N. Dixboro Rd., Ann Arbor, MI 48113-0140, http:/www.nsf.org.5 See ISO R161-1960: Pipes of Plastics Materials for the Transport of Fluids (Outside Diameters and Nominal Pressures) Part 1, Metri
32、c Series.F442/F442M 1325. Materials5.1 GeneralChlorinated poly(vinyl chloride) plastics used to make pipe meeting the requirements of this specification arecategorized by means of two criteria, namely, (1) short-term strength tests, and (2) long-term hydrostatic strength tests at both 73and 180 F 23
33、 and 82 C.5.2 Basic MaterialsMaterials: This specification covers CPVC pipe made from compounds meeting the requirements of Class23447 as defined in Specification D1784. The materials shall have an established HDS (Hydrostatic Design Stress) equal to orgreater than 2000 psi 13.80 MPa at 73 F 23 C an
34、d 500 psi 3.45 MPa) at 180 F 82 C when evaluated in accordance withTest Method D2837.5.2.1 Basic Materials Short-term TestsThis specification covers pipe made from CPVC plastics having certain physicalproperties as described in Specification D1784.5.2.1.1 CompoundThe CPVC compounds used for this pip
35、e shall equal or exceed the classification 23447 described inSpecification D1784.5.2.2 Basic Materials Long-term TestThis specification convers pipe made from CPVC plastics having certain HydrostaticDesign Bases (HDB) and Hydrostatic Design Stresses (HDS) described in Test Method D2837.5.2.2.1 Compo
36、undThe CPVC compounds used for this pipe shall have a Hydrostatic Design Basis at 73F 23C of 4000 psi28 MPa, and a Hydrostatic Design Basis at 180F 82C of either 1000 psi 7.0 MPa or 1250 psi 8.6 MPa when evaluatedin accordance with Test Method D2837.5.2.3 Standard thermoplastic pipe materials design
37、ationThe pipe materials designation shall consist of the materialdesignation code CPVC 4120-05 or CPVC 4120-06 for the type of plastic.NOTE 5As per Terminology F412 (see, “code, thermoplastic pipe materials designation”) the pipe materials designation code CPVC 4120 is asfollows: CPVC is the abbrevi
38、ation for chlorinated poly(vinyl chloride) as per Terminology D1600, 41 represents Cell Classification 23447 perSpecification D1784, and 20 represents a HDS of 2000 psi 14 MPa for water at 73F (23C) per Test Method D2837. In addition, the -05 or -06 suffixrepresents a HDS of 500 psi 3.4 MPa or 625 p
39、si 4.3 MPa respectively for water at 180F 82C per Test Method D2837.5.3 Rework MaterialThe manufacturers shall use only their own clean rework pipe material and the pipe produced shall meetall the requirements of this specification.6. Requirements6.1 Dimension and Tolerances:6.1.1 Outside DiametersT
40、he outside diameters and tolerances shall be as shown in Table 1 when measured in accordance withTest Method D2122. The tolerances on out-of-roundness shall apply only to pipe prior to shipment.6.1.2 Wall ThicknessThe wall thicknesses and tolerances shall be as shown in Table 2 when measured in acco
41、rdance with TestMethod D2122.TABLE 1 Outside Diameters and Tolerances for CPVC Plastic PipeNominal Pipe SizeAverage OutsideDiameter,in. mmTolerances, in. mmFor AverageMaximum Out-of-Roundness(maximum minus minimum diameter)SDR32.5SDR26SDR21SDR17SDR13.5SDR1114 8 0.540 13.7 0.004 0.10 0.030 (0.76) 0.0
42、16 (0.41)38 10 0.675 17.1 0.004 0.10 0.030 (0.76) 0.016 (0.41)12 15 0.840 21.3 0.004 0.10 0.030 (0.76) 0.016 (0.41)34 20 1.050 26.7 0.004 0.10 0.030 (0.76) 0.020 (0.51)1 25 1.315 33.4 0.005 0.13 0.030 (0.76) 0.020 (0.51)114 32 1.660 42.2 0.005 0.13 0.030 (0.76) 0.024 (0.61)112 40 1.900 48.2 0.006 0.
43、15 0.060 (1.52) 0.024 (0.61)2 50 2.375 60.3 0.006 0.15 0.060 (1.52) 0.024 (0.61)212 65 2.875 73.0 0.007 0.18 0.060 (1.52) 0.030 (0.76)3 80 3.500 88.9 0.007 0.18 0.060 (1.52) 0.023 (0.58)312 90 4.000 101.6 0.008 0.20 0.100 (2.54) 0.030 (0.76)4 100 4.500 114.3 0.008 0.20 0.100 (2.54) 0.023 (0.58)5 125
44、 5.563 141.3 0.010 0.25 0.100 (2.54) 0.060 (1.52)6 150 6.625 168.3 0.011 0.28 0.100 (2.54) 0.070 (1.78)8 200 8.625 219.1 0.015 0.38 0.150 (3.81) 0.090 (2.29)10 250 10.750 273.1 0.015 0.38 0.150 (3.81) 0.100 (2.54)12 300 12.750 323.9 0.015 0.38 0.150 (3.81) 0.120 (3.05)F442/F442M 133TABLE 2 Wall Thic
45、knesses and Tolerances for CPVC Plastic PipeNominalPipeSize,Wall ThicknessA,B in. mmSDR32.5 SDS26 SDR21 SDR17 SDR13.5 SDR11Min Tolerance Min Tolerance Min Tolerance Min Tolerance Min Tolerance Min Tolerance14 8 . . . . . . . . . . . . . . . . . . . . . 0.060 1.52 +0.020 0.51 0.060 1.52 +0.020 0.5138
46、 10 . . . . . . . . . . . . . . . . . . . . . . . . 0.060 1.52 +0.020 0.51 0.061 1.55 +0.020 0.5112 15 . . . . . . . . . . . . . . . . . . . . . . . . 0.062 1.57 +0.020 0.51 0.076 1.93 +0.020 0.5134 20 . . . . . . . . . . . . 0.060 1.52 +0.020 0.51 0.062 1.57 +0.020 0.51 0.078 1.98 +0.020 0.51 0.095
47、 2.41 +0.020 0.511 25 . . . . . . 0.060 1.52 +0.020 0.51 0.063 1.60 +0.020 0.51 0.077 1.96 +0.020 0.51 0.097 2.46 +0.020 0.51 0.119 3.02 +0.020 0.51114 32 . . . . . . 0.064 1.63 +0.020 0.51 0.079 2.01 +0.020 0.51 0.098 2.49 +0.020 0.51 0.123 3.12 +0.020 0.51 0.151 3.84 +0.020 0.51112 40 . . . . . .
48、0.073 1.85 +0.020 0.51 0.090 2.29 +0.020 0.51 0.112 2.84 +0.020 0.51 0.141 3.58 +0.020 0.51 0.173 4.39 +0.021 0.532 50 . . . . . . 0.091 2.31 +0.020 0.51 0.113 2.87 +0.020 0.51 0.140 3.56 +0.020 0.51 0.176 4.47 +0.021 0.53 0.216 5.49 +0.026 0.66212 65 . . . . . . 0.110 2.79 +0.020 0.51 0.137 3.48 +0.020 0.51 0.169 4.29 +0.020 0.51 0.213 5.41 +0.026 0.66 0.261 6.63 +0.031 0.793 80 0.108 2.74 +0.020 0.51 0.135 3.43 +0.020 0.51 0.167 4.24 +0.020 0.51 0.206 5.23 +0.025 0.