1、BRITISH STANDARD AEROSPACE SERIES BS2HC 209:1989 Specification for Low carbon, precipitation hardening nickel- chromium-aluminium- molybdenum-niobium alloy castings (Nickel base Cr11.5, Al6.0, Mo4.0, Nb2.0) UDC 629.7:669.245267128293 14:669.245.018.298BS2HC209:1989 This BritishStandard, having been
2、prepared under the directionof the Aerospace Standards Policy Committee ACE/-, was published under theauthority of the Board ofBSIand comes into effect on 31October1989 BSI 01-2000 First published October1979 First revision October1989 The following BSI references relate to the work on this standard
3、: Committee referenceACE/48 Draft for comment88/70332DC ISBN 0 580 17572 3 Committees responsible for this BritishStandard The preparation of this BritishStandard was entrusted by the Aerospace Standards Policy Committee(ACE/-) to Technical CommitteeACE/48, upon which the following bodies were repre
4、sented: British Industrial Fasteners Federation British Steel Industry Ministry of Defence Seamless Steel Tube Association Society of British Aerospace Companies Limited Amendments issued since publication Amd. No. Date of issue CommentsBS2HC209:1989 BSI 01-2000 i Contents Page Committees responsibl
5、e Inside front cover Foreword ii 1 Scope 1 2 References 1 3 Material requirements 1 Table 1 Material requirements 2BS2HC209:1989 ii BSI 01-2000 Foreword This revision supersedes BSHC209:1979, which is withdrawn, and includes trace elements in the chemical composition and is presented in a tabular fo
6、rmat. The basic specification for the material remains unchanged. A British Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity
7、 from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, pagesi andii, pages1 and 2 and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the insi
8、de front cover.BS2HC209:1989 BSI 01-2000 1 1 Scope This BritishStandard specifies the chemical composition, mechanical properties and inspection and test requirements for a heat resisting nickel alloy (Nickel base, Cr11.5, Al6.0, Mo4.0, Nb2.0) in the form of castings and remelting stock. 2 Reference
9、s This standard makes reference to the following BritishStandards: BSHC100, Inspection and testing procedure for iron, nickel, copper, cobalt and refractory metal base alloy castings. BSEN2500, Aerospace series Guidelines for the preparation and use of standards for metallic materials 1) . 3 Materia
10、l requirements The requirements for the material in the delivery and use of conditions are given inTable 1, the format and nomenclature of which complies with the requirements defined in BSEN2500. 1) In preparation.BS2HC209:1989 2 BSI 01-2000 Table 1 Material requirements 1 Chemical composition % or
11、 (parts per million) Element C Si Mn S Ag Al As B Bi Cd Co Cr Cu Fe Ga In Min. 0.03 5.5 0.005 11.0 Max. 0.07 0.50 0.25 0.015 (5) 6.2 (30) 0.015 (0.5) (0.2) 1.0 12.0 0.50 0.50 (30) (0.2) Element Mg Mo Nb + Ta Pb Sb Se Sn Te Ti Tl V W Zn Zr Ni Min. 3.8 1.5 0.4 0.05 Base Max. (50) 4.5 2.2 (5) (3) (5) (
12、30) (2) 1.0 (0.2) 0.1 0.2 (10) 0.15 2 1 2 3 3 Method of melting Vacuum melted and cast 4 Form Remelt stock Castings 5 Acceptance standard BS HC100, sections1 and2 BS HC100, sections1 and3 6 Delivery condition and heat treatment As cast, seenote1. 7 Use condition and heat treatment As cast, seenote1.
13、 8 Test piece heat treatment sampling Cast None BS HC100, sections1 and2 Separate or integral None. Seenote1 Seenote2 12 Tensile Temperature C Ambient 13 Proof stress R p 0.2 MPa W 685 14 Strength R m MPa W 755 15 Elongation A % W 6 21 Stress rupture Temperature C 980 22 Time t h W 45 25 Rupture str
14、ess B R MPa 150 27 NOTES 1. If required by the order, castings shall be treated under vacuum or protective atmosphere for2hours at1 170 10 C, and cooled to room temperature followed by precipitation treatment at870 10 C for2 hours. 2. If required, the properties to be obtained on test pieces machine
15、d from designated areas of castings shall be agreed between the manufacturer and the purchaser.blankBS2HC 209:1989 BSI 389 Chiswick High Road London W4 4AL BSIBritishStandardsInstitution BSI is the independent national body responsible for preparing BritishStandards. It presents the UK view on stand
16、ards in Europe and at the international level. It is incorporated by Royal Charter. Revisions BritishStandards are updated by amendment or revision. Users of BritishStandards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality of
17、 our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this BritishStandard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel:02089969000. Fax:02089967400. BSI offers
18、 members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel:02089969001. Fax:02089967001.
19、 In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as BritishStandards, unless otherwise requested. Information on standards BSI provides a wide range of information on national, European and international standards
20、 through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel:02089967111. Fax:02089967048. Subscribing members of BSI are kept up to date with
21、standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel:02089967002. Fax:02089967001. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK, of
22、the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any means electronic, photocopying, recording or otherwise without prior wri
23、tten permission from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. If permission is granted, the terms may include royalty payments or a licensing agreement. Details and advice can be obtained from the Copyright Manager. Tel:02089967070.