1、BS EN10028-4:2009ICS 77.140.30; 77.140.50NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBRITISH STANDARDFlat products madeof steels for pressurepurposesPart 4: Nickel alloy steels withspecified low temperature propertiesLicensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 15
2、/10/2009 07:57, Uncontrolled Copy, (c) BSIThis British Standardwas published under theauthority of the StandardsPolicy and StrategyCommittee on 31 July2009. BSI 2009ISBN 978 0 580 64187 9Amendments/corrigenda issued since publicationDate CommentsBS EN 10028-4:2009National forewordThis British Standa
3、rd is the UK implementation of EN 10028-4:2009. Itsupersedes BS EN 10028-4:2003 which is withdrawn.The UK participation in its preparation was entrusted to TechnicalCommittee ISE/73/2, Steel plates and bars for pressure purposes.A list of organizations represented on this committee can be obtained o
4、nrequest to its secretary.This publication does not purport to include all the necessary provisionsof a contract. Users are responsible for its correct application.Compliance with a British Standard cannot confer immunityfrom legal obligations.Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 1
5、5/10/2009 07:57, Uncontrolled Copy, (c) BSIBS EN 10028-4:2009EUROPEAN STANDARDNORME EUROPENNEEUROPISCHE NORMEN 10028-4June 2009ICS 77.140.30; 77.140.50 Supersedes EN 10028-4:2003 English VersionFlat products made of steels for pressure purposes - Part 4:Nickel alloy steels with specified low tempera
6、ture propertiesProduits plats en aciers pour appareils pression - Partie4: Aciers allis au nickel avec caractristiques spcifies basse tempratureFlacherzeugnisse aus Druckbehltersthlen - Teil 4:Nickellegierte kaltzhe SthleThis European Standard was approved by CEN on 14 May 2009.CEN members are bound
7、 to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such nationalstandards may be obtained on application to the CEN M
8、anagement Centre or to any CEN member.This European Standard exists in three official versions (English, French, German). A version in any other language made by translationunder the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as
9、 theofficial versions.CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland,France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,Romania, Slovaki
10、a, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATIONCOMIT EUROPEN DE NORMALISATIONEUROPISCHES KOMITEE FR NORMUNGManagement Centre: Avenue Marnix 17, B-1000 Brussels 2009 CEN All rights of exploitation in any form and by any means reservedworldwide for CEN
11、 national Members.Ref. No. EN 10028-4:2009: ELicensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 15/10/2009 07:57, Uncontrolled Copy, (c) BSIBS EN 10028-4:2009EN 10028-4:2009 (E) 2 Contents Page Foreword 3 1 Scope 4 2 Normative references 4 3 Terms and definitions . 4 4 Dimensions and tolerances
12、on dimensions . 4 5 Calculation of mass . 4 6 Classification and designation . 4 6.1 Classification 4 6.2 Designation 4 7 Information to be supplied by the purchaser . 4 7.1 Mandatory information 4 7.2 Options . 5 7.3 Example for ordering . 5 8 Requirements . 5 8.1 Steelmaking process . 5 8.2 Delive
13、ry condition 5 8.3 Chemical composition 5 8.4 Mechanical properties . 6 8.5 Surface condition. 9 8.6 Internal soundness 9 9 Inspection . 9 9.1 Types of inspection and inspection documents 9 9.2 Tests to be carried out 9 9.3 Retests 9 10 Sampling . 9 11 Test methods 9 12 Marking . 9 Annex A (informat
14、ive) Guidelines for heat treatment 10 Annex ZA (informative) Relationship between this European Standard and the Essential Requirements of EU Directive 97/23/EC . 11 Bibliography 12 Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 15/10/2009 07:57, Uncontrolled Copy, (c) BSIBS EN 10028-4:2009E
15、N 10028-4:2009 (E) 3 Foreword This document (EN 10028-4:2009) has been prepared by Technical Committee ECISS/TC 22 “Steels for pressure purposes - Qualities”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by publication of an
16、 identical text or by endorsement, at the latest by December 2009, and conflicting national standards shall be withdrawn at the latest by December 2009. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not
17、be held responsible for identifying any or all such patent rights. This document supersedes EN 10028-4:2003. This European Standard consists of the following parts, under the general title Flat products made of steels for pressure purposes: Part 1: General requirements Part 2: Non-alloy and alloy st
18、eels with specified elevated temperature properties Part 3: Weldable fine grain steels, normalized Part 4: Nickel alloy steels with specified low temperature properties Part 5: Weldable fine grain steels, thermomechanically rolled Part 6: Weldable fine grain steels, quenched and tempered Part 7: Sta
19、inless steels NOTE The clauses marked by two points () contain information relating to agreements that may be made at the time of enquiry and order. This document has been prepared under a mandate given to CEN by the European Commission and the European Free Trade Association, and supports essential
20、 requirements of EU Directive 97/23/EC. For relationship with EU Directive 97/23/EC, see informative Annex ZA, which is an integral part of this document. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this Eu
21、ropean Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the Unit
22、ed Kingdom. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 15/10/2009 07:57, Uncontrolled Copy, (c) BSIBS EN 10028-4:2009EN 10028-4:2009 (E) 4 1 Scope This European Standard specifies requirements for flat products for pressure equipment made of nickel alloy steels as specified in Table 1. T
23、he requirements and definitions of EN 10028-1:2007 + A1:2009 also apply. NOTE Once this European Standard is published in the EU Official Journal (OJEU) under Directive 97/23/EC, presumption of conformity to the Essential Safety Requirements (ESRs) of Directive 97/23/EC is limited to technical data
24、of materials in this European Standard (Part 1 and this Part 4 of the series) and does not presume adequacy of the material to a specific item of equipment. Consequently, the assessment of the technical data stated in this material standard against the design requirements of this specific item of eq
25、uipment to verify that the ESRs of Directive 97/23/EC are satisfied, needs to be done. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of
26、 the referenced document (including any amendments) applies. EN 10028-1:2007 + A1:2009, Flat products made of steels for pressure purposes Part 1: General requirements EN 10204:2004, Metallic products Types of inspection documents 3 Terms and definitions For the purposes of this document, the terms
27、and definitions given in EN 10028-1:2007 + A1:2009 apply. 4 Dimensions and tolerances on dimensions See EN 10028-1:2007 + A1:2009. 5 Calculation of mass See EN 10028-1:2007 + A1:2009, 6 Classification and designation 6.1 Classification In accordance with EN 10020, all steel grades covered by this do
28、cument are alloy special steels. 6.2 Designation See EN 10028-1:2007 + A1:2009. 7 Information to be supplied by the purchaser 7.1 Mandatory information See EN 10028-1:2007 + A1:2009. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 15/10/2009 07:57, Uncontrolled Copy, (c) BSIBS EN 10028-4:2009
29、EN 10028-4:2009 (E) 5 7.2 Options A number of options are specified in this European Standard and listed below. Additionally the relevant options of EN 10028-1:2007 + A1:2009 apply. If the purchaser does not indicate a wish to implement any of these options at the time of enquiry and order, the prod
30、ucts shall be supplied in accordance with the basic specification (see also EN 10028-1:2007 + A1:2009). 1) delivery condition other than that specified in Table 3 (see 8.2.2); 2) delivery of products in the untreated condition (see 8.2.3); 3) specification of a minimum impact energy of 40 J (see NOT
31、E to 8.4 and Table 4); 4) mid thickness test pieces for the impact test (see Clause 10); 5) verification of impact energy for longitudinal test pieces (see Clause 11). 7.3 Example for ordering 10 plates with nominal dimensions, thickness = 50 mm, width = 2 000 mm, length = 10 000 mm, made of a steel
32、 grade with the name 15NiMn6 and the number 1.6228 as specified in EN 10028-4, to be delivered with inspection document 3.1 as specified in EN 10204. 10 plates 50 x 2000 x 10 000 EN 10028-4 15NiMn6 Inspection document 3.1 or 10 plates 50 x 2000 x 10 000 EN 10028-4 1.6228 Inspection document 3.1. 8 R
33、equirements 8.1 Steelmaking process See EN 10028-1:2007 + A1:2009. 8.2 Delivery condition 8.2.1 The delivery condition shall be noted in the inspection document. 8.2.2 yy Unless otherwise agreed at the time of enquiry and order, the products covered by this document shall be supplied in the usual de
34、livery conditions specified in Table 3. 8.2.3 yy If so agreed at the time of enquiry and order, the products may be supplied in the untreated condition. In these cases, the specified tests shall be carried out on test pieces in the usual delivery condition as given in Table 3. NOTE Testing in a simu
35、lated heat treated condition does not discharge the processor from the obligation of providing proof of the specified properties in the finished product. 8.3 Chemical composition 8.3.1 The requirements of Table 1 shall apply for the chemical composition according to the cast analysis. 8.3.2 The prod
36、uct analysis shall not deviate from the specified values for the cast analysis as specified in Table 1 by more than the values given in Table 2. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 15/10/2009 07:57, Uncontrolled Copy, (c) BSIBS EN 10028-4:2009EN 10028-4:2009 (E) 6 Table 1 Chemical
37、 composition (cast analysis) a Steel grade % by mass Steel name Steel number C Si Mn P S AltotalMo Nb Ni V max. max. max. max. min. max. max. max. 11MnNi5-3 1.6212 0,14 0,50 0,70 to 1,50 0,025 0,010 0,020 0,05 0,30 bto 0,80 0,05 13MnNi6-3 1.6217 0,16 0,50 0,85 to 1,70 0,025 0,010 0,020 0,05 0,30 bto
38、 0,85 0,05 15NiMn6 1.6228 0,18 0,35 0,80 to 1,50 0,025 0,010 1,30 to 1,70 0,05 12Ni14 1.5637 0,15 0,35 0,30 to 0,80 0,020 0,005 3,25 to 3,75 0,05 X12Ni5 1.5680 0,15 0,35 0,30 to 0,80 0,020 0,005 4,75 to 5,25 0,05 X8Ni9 1.5662 0,10 0,35 0,30 to 0,80 0,020 0,005 0,10 8,5 to 10,0 0,05 X7Ni9 1.5663 0,10
39、 0,35 0,30 to 0,80 0,015 0,005 0,10 8,5 to 10,0 0,01 aElements not listed in this Table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All appropriate measures shall be taken to prevent the addition from scrap or other materials us
40、ed in steelmaking of these elements which may adversely affect the mechanical properties and usability. The content of Cr + Cu + Mo shall not exceed 0,50 %. bFor product thicknesses 40 mm, a minimum nickel content of 0,15 % is permitted. Table 2 Permissible product analysis tolerances on the limitin
41、g values given in Table 1 for the cast analysis Element Specified value in the cast analysis according to Table 1 % by mass Permissible deviationaof the product analysis % by mass C 0,18 + 0,02 Si 0,50 + 0,05 Mn 1,00 0,05 1,00 to 1,70 0,10 P 0,015 + 0,003 0,015 to 0,025 + 0,005 S 0,010 + 0,003 Al 0,
42、020 - 0,005 Mo 0,10 + 0,03 Nb 0,05 + 0,01 Ni 0,85 0,05 0,85 to 3,75 0,07 3,75 to 10,0 0,10 V 0,05 + 0,01 aIf several product analyses are carried out on one cast, and the contents of an individual element determined lie outside the permission range of the chemical composition specified for the cast
43、analysis, then it is only allowed to exceed the permissible maximum value or fall short of the permissible minimum value, but not both for one cast. 8.4 Mechanical properties The values given in Tables 3 and 4 (see also EN 10028-1:2007 + A1:2009 and clause 10) shall apply. NOTE Optionally, for steel
44、 grades 11MnNi5-3, 13MnNi6-3, 15NiMn6, 12Ni14 and X12Ni5, a minimum impact energy value of 40 J may be specified for temperatures where lower minimum values are specified (see Table 4, footnote d). Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 15/10/2009 07:57, Uncontrolled Copy, (c) BSIBS
45、EN 10028-4:2009EN 10028-4:2009 (E) 7 Table 3 Mechanical properties at room temperature Steel grade Usual delivery conditiona,b (Heat treatment symbol) Product thickness t mm Yield strength ReH MPa min. Tensile strength RmMPa Elongation after fracture A % min. Steel name Steel number 11MnNi5-3 1.6212
46、 +N (+NT) 30 285 420 to 530 24 30 t 50 275 50 t 80 265 13MnNi6-3 1.6217 +N (+NT) 30 355 490 to 610 22 30 t 50 345 50 t 80 335 15NiMn6 1.6228 +N or +NT or +QT 30 355 490 to 640 22 30 t 50 345 50 t 80 335 12Ni14 1.5637 +N or +NT or +QT 30 355 490 to 640 22 30 t 50 345 50 t 80 335 X12Ni5 1.5680 +N or +
47、NT or +QT 30 390 530 to 710 20 30 t 50 380 X8Ni9 +NT640a 1.5662 +NT640 a+N plus +NT 30 490 640 to 840 18 30 t 50 480 X8Ni9 +QT640a 1.5662 +QT640a+QT 30 490 30 t 50 480 X8Ni9 +QT680 a1.5662 +QT680 a+QTc 30 585 680 to 820 18 30 t 50 575 X7Ni9 1.5663 +QTc 30 585 680 to 820 18 30 t 50 575 a+N: normalize
48、d; +NT: normalized and tempered; +QT: quenched and tempered; +NT640/+QT640/+QT680: Heat treatment variant with minimum tensile strength of 640 MPa or 680 MPa. bFor temperatures and cooling conditions, see Table A.1. cFor product thickness 15 mm, delivery conditions +N plus +NT are also applicable. L
49、icensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 15/10/2009 07:57, Uncontrolled Copy, (c) BSIBS EN 10028-4:2009EN 10028-4:2009 (E) 8 Table 4 Minimum impact energy values Steel grade Heat treatment conditiona,b Product thickness mm Direction Minimum impact energy KV in J at a temperature in C of Steel name Steel number 20 0 -20 -40 -50 -60 -80 -100 -120 -150 -170 -196 11MnNi5-3 1.6212 +N (+NT) 80