1、raising standards worldwideNO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBSI Standards PublicationBS EN 13074-2:2011BS 2000-542:2011Bitumen and bituminous binders Recovery of binder from bituminous emulsion or cut-back or fluxed bituminous bindersPart 2: Stabilisation after r
2、ecovery by evaporationLicensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 03/06/2011 08:12, Uncontrolled Copy, (c) BSIBS EN 13074-2:2011 BRITISH STANDARDNational forewordThis British Standard is the UK implementation of EN 13074-2:2011.It supersedes BS EN 14895:2006 which is withdrawn.The UK part
3、icipation in its preparation was entrusted to TechnicalCommittee PTI/13, Petroleum Testing and Terminology.A list of organizations represented on this committee can beobtained on request to its secretary.Energy Institute, under the brand of IP, publishes and sells all Parts of BS 2000, and all BS EN
4、 petroleum test methods that would be Part of BS 2000, both in its annual publication “Standard methods for analysis and testing of petroleum and related products and British Standard 2000 Parts” and individually.Further information is available from: Energy Institute, 61 New Cavendish Street, Londo
5、n W1G 7AR. Tel: 020 7467 7100. Fax: 020 7255 1472.This publication does not purport to include all the necessaryprovisions of a contract. Users are responsible for its correctapplication. BSI 2011 ISBN 978 0 580 64492 4 ICS 75.140; 91.100.50 Compliance with a British Standard cannot confer immunity
6、fromlegal obligations.This British Standard was published under the authority of theStandards Policy and Strategy Committee on 31 March 2011. Amendments issued since publicationDate Text affectedLicensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 03/06/2011 08:12, Uncontrolled Copy, (c) BSIBS EN
7、13074-2:2011EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 13074-2 February 2011 ICS 91.100.50 Supersedes EN 14895:2006English Version Bitumen and bituminous binders - Recovery of binder from bituminous emulsion or cut-back or fluxed bituminous binders - Part 2: Stabilisation after recovery by
8、 evaporation Bitumes et liants bitumineux - Rcupration du liant dune mulsion de bitume ou dun bitume fluidifi ou flux - Partie 2: Stabilisation aprs rcupration par vaporation Bitumen und bitumenhaltige Bindemittel - Rckgewinnung des Bindemittels aus Bitumenemulsion oder verschnittenen oder gefluxten
9、 Bitumen - Teil 2: Stabilisierung nach Rckgewinnung durch Verdunstung This European Standard was approved by CEN on 8 January 2011. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national stan
10、dard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in a
11、ny other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Rep
12、ublic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN D
13、E NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2011 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 13074-2:2011: ELicensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 03/06/20
14、11 08:12, Uncontrolled Copy, (c) BSIBS EN 13074-2:2011EN 13074-2:2011 (E) 2 Contents Page Foreword 31 Scope 42 Normative references 43 Terms and definitions .44 Principle 45 Apparatus .46 Procedure .57 Test report 6Bibliography 7Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 03/06/2011 08:12
15、, Uncontrolled Copy, (c) BSIBS EN 13074-2:2011EN 13074-2:2011 (E) 3 Foreword This document (EN 13074-2:2011) has been prepared by Technical Committee CEN/TC 336 “Bituminous binders”, the secretariat of which is held by AFNOR. This European Standard shall be given the status of a national standard, e
16、ither by publication of an identical text or by endorsement, at the latest by August 2011, and conflicting national standards shall be withdrawn at the latest by August 2011. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and
17、/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 14895:2006. This European Standard EN 13074 consists of the following parts: EN 13074 -1, Bitumen and bituminous binders Recovery of binder from bituminous emulsion or cut-back or flu
18、xed bituminous binders Part 1: Recovery by evaporation EN 13074 -2, Bitumen and bituminous binders Recovery of binder from bituminous emulsion or cut-back or fluxed bituminous binders Part 2: Stabilisation after recovery by evaporation EN 13074-2 has been created as the result of the merging of EN 1
19、3074:2002 and EN 14895:2006 under a single EN 13074 reference (two different parts), since both standards describe similar procedures which are generally performed consecutively. The two different parts have been made as consistent as possible and the procedures for removing, storing and preparing t
20、he binder sample for further testing have been clarified and specified more accurately. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech
21、 Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA ST
22、ANDARDS, 03/06/2011 08:12, Uncontrolled Copy, (c) BSIBS EN 13074-2:2011EN 13074-2:2011 (E) 4 1 Scope This European Standard specifies a method for the stabilisation at 85 C for 24 h of a binder after recovery from a bituminous emulsion or from a cut-back or fluxed bitumen for further testing. It app
23、lies to all types of bituminous emulsions, modified with polymers or non-modified, and as well as to all types of cut-back and fluxed bitumens, both modified with polymers and non-modified. The recovery test method is specified in EN 13074-1. WARNING The use of this document may involve hazardous ma
24、terials, operations and equipment. This document does not purport to address all of the safety problems associated with its use. The hazards associated with the use of this method have been assessed using cut-back bitumen containing 10 % kerosene and 90 % 160/220 penetration grade bitumen and were f
25、ound low enough to be acceptable. However it is the responsibility of the user of this document to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. 2 Normative references The following referenced documents are indispensable for
26、 the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 12594, Bitumen and bituminous binders Preparation of test samples EN 13074-1, Bitumen and bituminous b
27、inders Recovery of binder from bituminous emulsion or cut-back or fluxed bituminous binders Part 1: Recovery by evaporation 3 Terms and definitions For the purposes of this document, the following terms and definitions apply. 3.1 recovered binder material remaining after the treatment of a bituminou
28、s emulsion or a cut-back or fluxed bitumen under the conditions specified in EN 13074-1 3.2 stabilised binder binder free from most of the volatile part of its flux oils, obtained from recovered binder by heating at 85 C for 24 h under the conditions specified according to this method 4 Principle A
29、thin layer of recovered binder from a bituminous emulsion or a cut-back or fluxed bituminous product is stabilised for 24 h at 85 C in a ventilated oven. 5 Apparatus Usual laboratory apparatus and glassware, together with the following: 5.1 Flat plates, of known surface area, equipped with an edge o
30、f maximum internal height 35 mm and a minimum surface area of 0.04 m. The internal base of the plate shall have no deformation greater in depth Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 03/06/2011 08:12, Uncontrolled Copy, (c) BSIBS EN 13074-2:2011EN 13074-2:2011 (E) 5 than 1 mm. The nu
31、mber of plates to be used shall be appropriate to give a sufficient amount of binder for further testing. The plates may be manufactured from a suitable non-stick material, such as a silicone material, or may be coated with a non-stick coating such as such as silicone coating; or the plates may be l
32、ined with a suitable non stick paper or fabric. When using non-stick paper or fabric, any crinkle of the paper or fabric shall be avoided, in particular by giving the paper the exact dimensions of the bottom of the plates. 5.2 Ventilated oven, at least 80 l internal volume, capable of maintaining a
33、temperature of (85 2) C around the sample and in which the level of the shelves has been checked. It is acceptable to use the same oven for both the recovery step (EN 13074-1) and the stabilisation step provided that this oven is capable of maintaining around the sample the specified temperatures. I
34、n case the same oven is to be used for both steps, the sample may be left in the oven during the period of temperature adjustment (from 50 C as specified in EN 13074-1 up to 85 C), provided this period does not exceed 1 h. 6 Procedure 6.1 Stabilisation of the binder Stabilisation of the recovered bi
35、nder shall take place immediately after the recovery procedure (EN 13074-1). Put the plate with the recovered binder in the oven (5.2) and leave it for (24 1) h at (85 2) C. If there are several plates, introduce them simultaneously. The binders should not be grouped when their volatile parts might
36、be of different natures. Arrange the plates in such a way that air circulation is not hindered. Air circulation has to be effective on each side of each plate. At the end of the specified period, remove the plate(s) from the oven. 6.2 Removal and storage of the stabilised binder Collect without any
37、delay the stabilised binder from the plate(s) using an appropriate tool but without applying any extra heat to the sample. To facilitate the removal of binders from the non-stick material, it may be necessary to cool the plates in a refrigerator or freezer. The stabilised binder from all the plates
38、of the same sample shall be placed in a same sample container. If the stabilised binder is required for further testing at a later date, it shall be stored for as short a time as possible, but no longer than 28 days, in a sealed container and stored at a temperature lower than 28 C. NOTE When storin
39、g the stabilised binder, a period as short as possible should be favoured (if possible less than one week). Specific storage conditions (use of inert gas, e.g. nitrogen) are recommended, especially in cases where storage time exceeds 1 week. 6.3 Homogenisation of the stabilised binder and preparatio
40、n of the sample for further testing Before performing further testing on the stabilised binder, the binder from each plate shall be homogenized by mixing. If the sample of recovered binder comes from more than one plate, the binder from the whole plates shall be blended. Heating of the stabilised bi
41、nder shall be strictly in accordance with EN 12594. When possible, the preparations for further testing shall be carried out immediately after homogenising the stabilised binder to avoid reheating. When moulding samples for further testing and in order to prevent any further ageing, the stabilised b
42、inder shall be heated at a temperature between expected softening point + 80 C and expected softening point + 100 C for the minimum time necessary. Moulds for further testing shall be preheated according to the recommendations mentioned in the appropriate standards. Licensed Copy: Wang Bin, ISO/EXCH
43、ANGE CHINA STANDARDS, 03/06/2011 08:12, Uncontrolled Copy, (c) BSIBS EN 13074-2:2011EN 13074-2:2011 (E) 6 7 Test report The test report shall contain at least the following information: a) type and complete identification (including the date and place of sampling) of the material under the recovery
44、test (EN 13074-1) followed by the stabilisation test; b) reference to this European Standard; c) conditions of use of the stabilised binder (see 6.2 and 6.3); d) any deviation, by agreement or otherwise, from the procedure described; e) date of the test. Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA S
45、TANDARDS, 03/06/2011 08:12, Uncontrolled Copy, (c) BSIBS EN 13074-2:2011 EN 13074-2:2011 (E) 7 Bibliography EN 58, Bitumen and bituminous binders Sampling bituminous binders Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 03/06/2011 08:12, Uncontrolled Copy, (c) BSIEnergy Institute Buying Par
46、ts of BS 2000Orders for BS 2000 publications should be addressed to either:Energy Institute Library and Information Service61 New Cavendish Street London W1G 7ARTel: +44 (0)20 7467 7100 Fax: +44 (0)20 7255 1472 www.energyinst.org.ukOrder standards securely via: www.energyinstpubs.org.ukor:British St
47、andards Institution Customer Services389 Chiswick High Road London W4 4ALTel: +44 (0)20 8996 9001 Fax: +44 (0)20 8996 7001 Order hard copy standards securely via: exists in all BS 2000 publications. No part of this publication may be reproduced in any form without the prior permission in writing of
48、 BSI and the Energy Institute. Enquiries about copyright should be made to the Secretary of PTI/13 at the Energy Institute.PTI/13BS 2000 SeriesLicensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 03/06/2011 08:12, Uncontrolled Copy, (c) BSIThis page deliberately left blankLicensed Copy: Wang Bin,
49、ISO/EXCHANGE CHINA STANDARDS, 03/06/2011 08:12, Uncontrolled Copy, (c) BSIBSI is the independent national body responsible for preparing British Standardsand other standards-related publications, information and services. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter.British Standards Institution (BSI)raising standards worldwideBSI Group Headquarters389 Chiswick H