1、raising standards worldwideNO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBSI Standards PublicationFlexible insulating sleevingPart 3: Specifications for individual types of sleeving Sheet 281: Heat-shrinkable, polyolefin sleeving, semiconductiveBS EN 60684-3-281:2010Licensed
2、Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:36, Uncontrolled Copy, (c) BSINational forewordThis British Standard is the UK implementation of EN 60684-3-281:2010. It isidentical to IEC 60684-3-281:2010.The UK participation in its preparation was entrusted by Technical CommitteeGEL/15,
3、 Solid electrical insulating materials, to Subcommittee GEL/15/5,Flexible insulating sleeving for electrical purposes.A list of organizations represented on this committee can be obtained onrequest to its secretary.This publication does not purport to include all the necessary provisions of acontrac
4、t. Users are responsible for its correct application. BSI 2011ISBN 978 0 580 65790 0ICS 29.035.20Compliance with a British Standard cannot confer immunity fromlegal obligations.This British Standard was published under the authority of the StandardsPolicy and Strategy Committee on 28 February 2011.A
5、mendments issued since publicationAmd. No. Date Text affectedBRITISH STANDARDBS EN 60684-3-281:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:36, Uncontrolled Copy, (c) BSIEUROPEAN STANDARD EN 60684-3-281 NORME EUROPENNE EUROPISCHE NORM September 2010 CENELEC European Commi
6、ttee for Electrotechnical Standardization Comit Europen de Normalisation Electrotechnique Europisches Komitee fr Elektrotechnische Normung Management Centre: Avenue Marnix 17, B - 1000 Brussels 2010 CENELEC - All rights of exploitation in any form and by any means reserved worldwide for CENELEC memb
7、ers. Ref. No. EN 60684-3-281:2010 E ICS 29.035.20 English version Flexible insulating sleeving - Part 3: Specifications for individual types of sleeving - Sheet 281: Heat-shrinkable, polyolefin sleeving, semiconductive (IEC 60684-3-281:2010) Gaines isolantes souples - Partie 3: Spcifications pour ty
8、pes particuliers de gaines - Feuille 281: Gaines thermortractables en polyolfine, semiconductrices (CEI 60684-3-281:2010) Isolierschluche - Teil 3: Anforderungen fr einzelne Schlauchtypen - Blatt 281: Halbleitende Polyolefin-Wrmeschrumpfschluche (IEC 60684-3-281:2010) This European Standard was appr
9、oved by CENELEC on 2010-09-01. CENELEC members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such nati
10、onal standards may be obtained on application to the Central Secretariat or to any CENELEC member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CENELEC member into its own languag
11、e and notified to the Central Secretariat has the same status as the official versions. CENELEC members are the national electrotechnical committees of Austria, Belgium, Bulgaria, Croatia, Cyprus, the Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Ital
12、y, Latvia, Lithuania, Luxembourg, Malta, the Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. BS EN 60684-3-281:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:36, Uncontrolled Copy, (c) BSIEN 60684-3-281:
13、2010 Foreword The text of document 15/563/FDIS, future edition 1 of IEC 60684-3-281, prepared by IEC TC 15, Solid electrical insulating materials, was submitted to the IEC-CENELEC parallel vote and was approved by CENELEC as EN 60684-3-281 on 2010-09-01. Attention is drawn to the possibility that so
14、me of the elements of this document may be the subject of patent rights. CEN and CENELEC shall not be held responsible for identifying any or all such patent rights. The following dates were fixed: latest date by which the EN has to be implemented at national level by publication of an identical nat
15、ional standard or by endorsement (dop) 2011-06-01 latest date by which the national standards conflicting with the EN have to be withdrawn (dow) 2013-09-01 Annex ZA has been added by CENELEC. _ Endorsement notice The text of the International Standard IEC 60684-3-281:2010 was approved by CENELEC as
16、a European Standard without any modification. _ BS EN 60684-3-281:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:36, Uncontrolled Copy, (c) BSIEN 60684-3-281:2010 Annex ZA (normative) Normative references to international publications with their corresponding European publi
17、cations The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. NOTE When an international publication ha
18、s been modified by common modifications, indicated by (mod), the relevant EN/HD applies. Publication Year Title EN/HD Year - - Test requirements on accessories for use on power cables of rated voltage from 3,6/6(7,2) kV up to 20,8/36(42) kV - Part 1: Cables with extruded insulation HD 629.1 S2 2006
19、IEC 60296 2003 Fluids for electrotechnical applications - Unused mineral insulating oils for transformers and switchgear EN 60296 + corr. September 2004 2004 IEC 60502 Series Power cables with extruded insulation and their accessories for rated voltages from 1 kV (Um = 1,2 kV) up to 30 kV (Um = 36 k
20、V) - - IEC 60684-1 2003 Flexible insulating sleeving - Part 1: Definitions and general requirements EN 60684-1 2003 IEC 60684-2 + A1 + A2 1997 2003 2005 Flexible insulating sleeving - Part 2: Methods of test EN 60684-2 + A1 + A2 1997 2003 2005 IEC 60757 1983 Code for designation of colours HD 457 S1
21、 1985 BS EN 60684-3-281:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:36, Uncontrolled Copy, (c) BSI60684-3-281 IEC:2010 CONTENTS INTRODUCTION.5 1 Scope.6 2 Normative references .6 3 Designation 7 4 Conditions of test .7 5 Requirements .7 6 Sleeving conformance 7 Annex A (
22、informative) Guidance to the available sizes and wall thicknesses 10 Table 1 Property requirements .8 Table 2 Resistance to selected fluids .9 Table A.1 Type A, thin wall 10 Table A.2 Type B, medium wall10 BS EN 60684-3-281:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:36,
23、 Uncontrolled Copy, (c) BSI60684-3-281 IEC:2010 5 INTRODUCTION This International Standard is one of a series which deals with flexible insulating sleeving for electrical purposes. The series consists of three parts: Part 1: Definitions and general requirements (IEC 60684-1) Part 2: Methods of test
24、(IEC 60684-2) Part 3: Specifications for individual types of sleeving (IEC 60684-3) This standard comprises one of the sheets of Part 3 as follows: Sheet 281: Heat-shrinkable, polyolefin sleeving, semiconductive BS EN 60684-3-281:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011
25、08:36, Uncontrolled Copy, (c) BSI 6 60684-3-281 IEC:2010 FLEXIBLE INSULATING SLEEVING Part 3: Specifications for individual types of sleeving Sheet 281: Heat-shrinkable, polyolefin sleeving, semiconductive 1 Scope This part of IEC 60684 gives the requirements for two types of heat-shrinkable, polyol
26、efin sleeving, semiconductive, with a nominal shrink ratio of 3:1. This sleeving has been found suitable up to temperatures of 100 C. Type A: Thin wall Internal diameter up to 195,0 mm typically Type B: Medium wall Internal diameter up to 120,0 mm typically These sleevings are normally supplied in t
27、he colour black. Since these types of sleevings cover a significantly large range of sizes and wall thicknesses, Tables A.1 and A.2 in this standard provides guidance to the range of sizes available. The actual size shall be agreed between the user and the supplier. Materials which conform to this s
28、pecification meet established levels of performance. However, the selection of a material by a user for a specific application should be based on the actual requirements necessary for adequate performance in that application and not based on this specification alone. This sleeving is designed to be
29、used in MV cable accessories and as such electrical performance must be proven as part of the assembly. Examples of this are described in HD 629 and IEC 60502 series. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated reference
30、s, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. IEC 60296:2003, Fluids for electrotechnical applications Unused mineral insulating oils for transformers and switchgear IEC 60502 (all parts), Power cables wit
31、h extruded insulation and their accessories for rated voltages from 1 kV (Um = 1,2 kV) up to 30 kV (Um = 36 kV) IEC 60684-1:2003, Flexible insulating sleeving Part 1: Definitions and general requirements IEC 60684-2:1997, Flexible insulating sleeving Part 2: Methods of test Amendment 1 (2003) Amendm
32、ent 2 (2005) IEC 60757:1983, Code for designation of colours BS EN 60684-3-281:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:36, Uncontrolled Copy, (c) BSI60684-3-281 IEC:2010 7 HD 629, Test requirements on accessories for use on power cables of rated voltages from 3,6/6(7
33、,2)kV up to 20,8/36 (42)kV Part 1: Cables with extruded insulation 3 Designation The sleeving shall be identified by the following designation: Description IEC publication number IEC part number IEC sheet number Type Size (expanded and recovered internal diameter in millimetres) Colour Sleeving IEC
34、60684 - 3 -281 - A - 50/20 Black Any colour abbreviation shall comply with IEC 60757, where applicable. Non-standard colours shall be written out in full. NOTE This information is for labelling only in accordance with IEC 60684-1. 4 Conditions of test Unless otherwise specified, the sleeving shall b
35、e shrunk in a forced air circulation oven for (10 1) min at 200 C 3 K prior to testing. 5 Requirements In addition to the general requirements given in IEC 60684-1, the sleeving shall comply with the requirements of Tables 1 and 2. 6 Sleeving conformance Conformance to the requirements of this speci
36、fication shall normally be based on the results from typical sizes: Type A, Thin wall: Recovered ID 20 mm - 30 mm Type B, Medium wall: Recovered ID 20 mm - 30 mm BS EN 60684-3-281:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:36, Uncontrolled Copy, (c) BSI 8 60684-3-281 IE
37、C:2010 Table 1 Property requirements Property IEC 60684-2 clause or subclause Units Max. or min. Requirements Remarks Dimensions Internal diameter Wall thickness Concentricity expanded recovered 3 3.1.2 3.3.2 3.3.3 mm mm % Min. Min. To be agreed between the purchaser and the supplier 60 85 Heat shoc
38、k Tensile strength Elongation at break 6 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 8 175 Heat at 150 C 5 K. Longitudinal change 9 % Max. +5 10 Bending at low temperature 14 No cracking shall be visible. Test at 40 C For strips, the mandrel shall be between 20 and 22 times the wall thickness. Full
39、section sleeving is tested unfilled and the mandrel shall be between 20 and 22 times the outer diameter. Dimensional stability on storage 16 The dimensions shall remain as agreed. See Clause 1 Scope. Tensile strength Elongation at break 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 10 200 Use a jaw se
40、paration rate of 100 mm/min. Below 6,5 mm as sleeving. At 6,5 mm and above as dumbbells Secant modulus at 2 % elongation 19.4 MPa Max. 250 Resistance to selected fluids Tensile strength Elongation at break 36 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 8 175 Use the fluids and test temperatures spec
41、ified in Table 2. Immersion (24 1) h Heat ageing Tensile strength Elongation at break 39 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 8 175 Heat at 135 C 3 K. Volume resistivity at room temperature 23 23.4.2 m Min. 103See note. Long term ageing Elongation at break 50 19.2 % Min. 100 The ageing temper
42、ature shall be 100 C 3 K. NOTE This value is set so as to define the tube as conductive. It does not indicate any guarantee of suitable performance in an accessory and further testing by the supplier will be needed to prove this. Note also that the value may change with applied voltage. BS EN 60684-
43、3-281:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:36, Uncontrolled Copy, (c) BSI60684-3-281 IEC:2010 9 Table 2 Resistance to selected fluids Test fluid No. Fluids Type Standard or symbol Immersion temperature at C 2 K 1 Insulating oil Mineral based IEC 60296 23 2 Isoprop
44、yl alcohol 23 3 Water De-ionized 85 Other fluids and/or temperatures may be specified for customers with specific needs. These additional fluids and/or temperatures shall be applicable when incorporated into agreements between the supplier and the customer. BS EN 60684-3-281:2010Licensed Copy: Wang
45、Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:36, Uncontrolled Copy, (c) BSI 10 60684-3-281 IEC:2010 Annex A (informative) Guidance on the available sizes and wall thicknesses Table A.1 Type A, thin wall Internal diameter Wall Expanded Min. mm Recovered Max. mm Recovered wall thickness mm 20,0 8,
46、0 2,0 25,0 10,0 2,0 30,0 12,0 2,0 38,0 16,0 2,0 40,0 15,0 2,0 50,0 20,0 2,0 65,0 24,0 2,0 75,0 28,0 2,0 80,0 24,0 2,0 95,0 35,0 2,0 110,0 45,0 2,0 120,0 55,0 2,0 155,0 65,0 2,0 180,0 70,0 2,0 195,0 90,0 2,5 Table A.2 Type B, medium wall Internal diameter Wall Expanded Min. mm Recovered Max. mm Recov
47、ered wall thickness mm 36,0 10,0 3,0 51,0 14,0 3,0 63,0 18,0 3,0 70,0 23,0 3,0 85,0 22,0 3,0 90,0 34,0 3,0 95,0 29,0 3,0 120,0 34,0 3,0 _ BS EN 60684-3-281:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:36, Uncontrolled Copy, (c) BSIThis page deliberately left blankLicensed
48、 Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:36, Uncontrolled Copy, (c) BSIBSI is the independent national body responsible for preparing British Standards. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter.British Stan
49、dards Institution (BSI)raising standards worldwideBSI Group Headquarters389 Chiswick High Road London W4 4AL UKTel +44 (0)20 8996 9001Fax +44 (0)20 8996 Standards are updated by amendment or revision. Users of BritishStandards should make sure that they possess the latest amendments oreditions.It is the constant aim of BSI to improve the qualit