1、raising standards worldwideNO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBSI Standards PublicationHeat-shrinkable moulded shapesPart 3: Specification requirements for shape dimensions, material requirements and compatibility performanceSheet 101: Heat-shrinkable moulded shape
2、s, polyolefin, semi-rigid, limited fire hazard, material requirements and system performanceBS EN 62329-3-101:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 13/06/2011 07:28, Uncontrolled Copy, (c) BSINational forewordThis British Standard is the UK implementation of EN 62329-3-101:2010.
3、 It isidentical to IEC 62329-3-101:2010.The UK participation in its preparation was entrusted to Technical CommitteeGEL/15, Solid electrical insulating materials.A list of organizations represented on this committee can be obtained onrequest to its secretary.This publication does not purport to incl
4、ude all the necessary provisions of acontract. Users are responsible for its correct application. BSI 2011 ISBN 978 0 580 58368 1 ICS 29.035.01Compliance with a British Standard cannot confer immunity from legal obligations.This British Standard was published under the authority of the Standards Pol
5、icy and Strategy Committee on 28 February 2011.Amendments issued since publicationAmd. No. Date Text affectedBRITISH STANDARDBS EN 62329-3-101:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 13/06/2011 07:28, Uncontrolled Copy, (c) BSIEUROPEAN STANDARD EN 62329-3-101 NORME EUROPENNE EUROP
6、ISCHE NORM September 2010 CENELEC European Committee for Electrotechnical Standardization Comit Europen de Normalisation Electrotechnique Europisches Komitee fr Elektrotechnische Normung Management Centre: Avenue Marnix 17, B - 1000 Brussels 2010 CENELEC - All rights of exploitation in any form and
7、by any means reserved worldwide for CENELEC members. Ref. No. EN 62329-3-101:2010 E ICS 29.035.01 English version Heat-shrinkable moulded shapes - Part 3: Specification requirements for shape dimensions, material requirements and compatibility performance - Sheet 101: Heat-shrinkable moulded shapes,
8、 polyolefin, semi-rigid, limited fire hazard, material requirements and system performance (IEC 62329-3-101:2010) Profils thermortractables - Partie 3: Exigences relatives aux dimensions des profils, exigences de matriaux et performances de compatibilit - Feuille 101: Profils thermortractables, exig
9、ences relatives aux matriaux semi-rigides en polyolfine, risque de feu limit et performances du systme (CEI 62329-3-101:2010) Wrmeschrumpfende Formteile - Teil 3: Anforderungen fr Formteilmae, Materialeigenschaften und Kompatibilittsverhalten - Blatt 101: Wrmeschrumpfende Formteile aus Polyolefin, h
10、albsteif, flammwidrig, Materialanforderungen und Systemeigenschaften (IEC 62329-3-101:2010) This European Standard was approved by CENELEC on 2010-09-01. CENELEC members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the
11、 status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Central Secretariat or to any CENELEC member. This European Standard exists in three official versions (English, French, Ger
12、man). A version in any other language made by translation under the responsibility of a CENELEC member into its own language and notified to the Central Secretariat has the same status as the official versions. CENELEC members are the national electrotechnical committees of Austria, Belgium, Bulgari
13、a, Croatia, Cyprus, the Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, the Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. BS EN 62329-3
14、-101:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 13/06/2011 07:28, Uncontrolled Copy, (c) BSIEN 62329-3-101:2010 Foreword The text of document 15/569/FDIS, future edition 1 of IEC 62329-3-101, prepared by IEC TC 15, Solid electrical insulating materials, was submitted to the IEC-CENEL
15、EC parallel vote and was approved by CENELEC as EN 62329-3-101 on 2010-09-01. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and CENELEC shall not be held responsible for identifying any or all such patent rights. The followi
16、ng dates were fixed: latest date by which the EN has to be implemented at national level by publication of an identical national standard or by endorsement (dop) 2011-06-01 latest date by which the national standards conflicting with the EN have to be withdrawn (dow) 2013-09-01 Annex ZA has been add
17、ed by CENELEC. _ Endorsement notice The text of the International Standard IEC 62329-3-101:2010 was approved by CENELEC as a European Standard without any modification. In the official version, for Bibliography, the following note has to be added for the standard indicated: IEC 60684-3-216 NOTE Harm
18、onized as EN 60684-3-216. _ BS EN 62329-3-101:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 13/06/2011 07:28, Uncontrolled Copy, (c) BSIEN 62329-3-101:2010 Annex ZA (normative) Normative references to international publications with their corresponding European publications The followin
19、g referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. NOTE When an international publication has been modified by c
20、ommon modifications, indicated by (mod), the relevant EN/HD applies. Publication Year Title EN/HD Year IEC 60695-11-10 - Fire hazard testing - Part 11-10: Test flames - 50 W horizontal and vertical flame test methods EN 60695-11-10 - IEC 60757 1983 Code for designation of colours HD 457 S1 1985 IEC
21、62329-1 - Heat shrinkable moulded shapes - Part 1: Definitions and general requirements EN 62329-1 - IEC 62329-2 2006 Heat shrinkable moulded shapes - Part 2: Methods of test EN 62329-2 2006 IEC 62329-3-100 2010 Heat-shrinkable moulded shapes - Part 3: Specification requirements for shape dimensions
22、, material requirements and compatibility performance - Sheet 100: Heat-shrinkable moulded shape dimensions EN 62329-3-100 2010 ISO 1817 2005 Rubber, vulcanized - Determination of the effect of liquids - - BS EN 62329-3-101:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 13/06/2011 07:28,
23、 Uncontrolled Copy, (c) BSI62329-3-101 IEC:2010 CONTENTS INTRODUCTION.5 1 Scope.6 2 Normative references6 3 Designation 7 4 Conditions of test for the moulded shapes.7 5 Requirements .7 6 Moulded shapes material conformance .7 7 Moulded shapes compatibility .7 Annex A (informative) Adhesive compatib
24、ility guide for sheet 101 moulded shapes . 11 Bibliography 12 Table 1 Property requirements .8 Table 2 Resistance to selected fluids10 BS EN 62329-3-101:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 13/06/2011 07:28, Uncontrolled Copy, (c) BSI62329-3-101 IEC:2010 5 INTRODUCTION This Int
25、ernational Standard is one of a series that deals with heat-shrinkable moulded shapes for electrical purposes. The series consists of three parts: Part 1: Definitions and general requirements (IEC 62329-1) Part 2: Methods of test (IEC 62329-2) Part 3: Specification requirements for moulded shape dim
26、ensions, material requirements and compatibility performance (IEC 62329-3) This standard gives one of the sheets comprising Part 3 as follows: Sheet 101: Heat-shrinkable moulded shapes, polyolefin, semi-rigid, limited fire hazard, material requirements and system performance NOTE See IEC 62329-3-100
27、 for moulded shape dimensions. BS EN 62329-3-101:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 13/06/2011 07:28, Uncontrolled Copy, (c) BSI 6 62329-3-101 IEC:2010 HEAT-SHRINKABLE MOULDED SHAPES Part 3: Specification requirements for shape dimensions, material requirements and compatibil
28、ity performance Sheet 101: Heat-shrinkable moulded shapes, polyolefin, semi-rigid, limited fire hazard, material requirements and system performance 1 Scope This sheet of IEC 62329-3 gives the requirements for heat-shrinkable moulded shapes, polyolefin, semi-rigid, limited fire hazard, material requ
29、irements and system performance. Experience of product performance indicates that this moulded shape material is suitable for inclusion in systems for operation in the following temperature range: 30 C to + 105 C. The moulded shapes may be supplied with a pre-coated adhesive. Refer to the manufactur
30、ers/suppliers for options. A guide to adhesive compatibility is given in Annex A. These moulded shapes are normally supplied in the styles and dimensions given in IEC 62329-3-100. The colour is normally black. Styles and dimensions other than those specifically listed in IEC 62329-3-100 may be avail
31、able as custom items. These items shall be considered to comply with this standard if they comply with the property requirements listed in Table 1 with the exception of dimensions. Materials that conform to this specification meet established levels of performance. However, the selection of a materi
32、al by a user for a specific application should be based on the actual requirements necessary for adequate performance in that application and not based on this specification alone. 2 Normative references The following referenced documents are indispensable for the application of this document. For d
33、ated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies IEC 60695-11-10, Fire hazard testing Part 11-10: Test flames 50 W horizontal and vertical flame test methods IEC 62329-1, Heat-shrinkable moulded
34、shapes Part 1: Definitions and general requirements IEC 62329-2:2006, Heat-shrinkable moulded shapes Part 2: Methods of test IEC 62329-3-100:2010, Heat-shrinkable moulded shapes Part 3: Specification requirements for shape dimensions, material requirements and compatibility performance Sheet 100: He
35、at-shrinkable moulded shape dimensions IEC 60757:1983, Code for designation of colours ISO 1817: 2005, Rubber, vulcanized - Determination of the effect of liquids BS EN 62329-3-101:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 13/06/2011 07:28, Uncontrolled Copy, (c) BSI62329-3-101 IEC:
36、2010 7 3 Designation The moulded shapes shall be designated as shown by the following example: Description IEC publication number IEC Part number IEC Sheet number IEC Style/size code Colour Adhesive code (see NOTE) a Drain holes b Moulded shapes IEC 62329 3 101 B/01 BK W1 D a Insert UN if uncoated.
37、b Insert N if no drain holes. NOTE For compatible adhesives and codes, see Annex A. Any abbreviation for colour shall comply with IEC 60757. Where no abbreviation is given, the colour shall be written in full. 4 Conditions of test for the moulded shapes The moulded shapes shall be shrunk in a forced
38、 air circulation oven for (10 1 ) min at the temperature specified in Table 1. 5 Requirements In addition to the general requirements given in IEC 62329-1, the heat-shrinkable moulded shapes shall comply with the dimensional requirements given in IEC 62329-3-100 and Table 1. 6 Moulded shapes materia
39、l conformance Conformance with the requirements of this specification shall be based on the results form test sheets, ( 2 0,15 ) mm thick, unless otherwise specified1, which shall be prepared from the same cross-linked heat-shrinkable material that is used to manufacture the heat-shrinkable moulded
40、shapes. 7 Moulded shapes compatibility Conformance with the compatibility requirements of this specification shall be based on the results from the assembly configuration as shown in Figure 3 of IEC 62329-2. _ 1A suitable size has been found to be 150 mm 150 mm. BS EN 62329-3-101:2010Licensed Copy:
41、Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 13/06/2011 07:28, Uncontrolled Copy, (c) BSI 8 62329-3-101 IEC:2010 Table 1 Property requirements Property IEC 62329-2 clause or subclause Units Max. or Min. Requirements Remarks Heat shock Tensile strength Elongation at break 7 10 10 MPa % Min. Min. 5 100 Hea
42、t at 175C 3 K Bending at low temperature 8 No cracks shall be visible Condition at -30 C 2 K. Mandrel diameter shall be 20 mm 10+mm. Dimensional stability on storage 9 The dimensions shall be as specified in Tables 1 to 22 IEC 62329-3-100 Recovery conditions as Clause 4 for dimensions Tensile streng
43、th Elongation at break 10 10 MPa % Min. Min. 7 200 Use a jaw separation rate of 100 mm/min. Secant modulus at 2 % elongation 11 MPa 50 to 130 Electric strength 12 MV/m Min. 8 Volume resistivity after damp heat 13 m Min. 1010 Flammability 16 s Max. 30 Test in accordance with method A of IEC 60695-11-
44、10 Copper corrosion 18 % Max. None above the allowable 8 Heat for (16 0,5 ) h at 150 C 3K Resistance to selected fluids Tensile strength Elongation at break 20 10 10 MPa % Min. Min. 4 100 Use the fluids and test temperatures specified in Table 2. Heat ageing Tensile strength Elongation at break 23 1
45、0 10 MPa % Min. Min. 5 100 Heat at 150 C 3K Water absorption 24 % Max. 0,5 Mould growth Tensile strength Elongation at break 30 10 10 MPa % Min. Min. 7 200 Method B 56 days exposure Long term heat ageing Elongation at break 21 10 % Min. 100 Heat for (3000 5) h at 105 C 3 K Oxygen index 17.1 Min. 29
46、Temperature index 17.2 C Min. 250 Smoke index 26 Max. 20 Toxicity index 27 Max. 5 Halogen content 28 28.1 28.2 % % Max. Max. 0,2 0,1 Expressed as chlorine Acid gas generation Conductivity 29 29.2 pH pH S/mm Min. Max. Max. 3,5 10,5 10,0 BS EN 62329-3-101:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHIN
47、A STANDARDS, 13/06/2011 07:28, Uncontrolled Copy, (c) BSI62329-3-101 IEC:2010 9 Property IEC 62329-2 clause or subclause Units Max. or Min. Requirements Remarks Compatibility Adhesive type 31 W1aTest at C 3K Dynamic shear At room temperature 31.1 N Min. 300 23 At elevated temperature 31.1.7 N Min. 3
48、0 105 Static load 31.2 kg Min. 10 23 At elevated temperature 31.1 N 0,5 105 Dynamic shear Min. 300 23 Fluid type Standard or symbol (24 0,5) h immersion at C 2K Kerosene fuel F34 23 Grease G 354 23 Oil 0-156 23 Fluid resistance 31.3 N Min. 150 Water 23 Thermal ageing 31.4 N Min. 300 Heat for (168 1
49、) h at 100 C 3 K Peel adhesion 31.5 N/25mm Min. 60 Altitude immersion 31.6 Min. 109 aThese system performance requirements are based on using W1 adhesive (see Annex A). When using other adhesives the performance may be different. Refer to the supplier/manufacturer. BS EN 62329-3-101:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 13/06/2011 07:28, Uncontrolled Copy, (c) B