1、July 2009DEUTSCHE NORM English price group 8No part of this standard may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 91.100.30!$XEm“1533474www.
2、din.deDDIN EN 12390-5Testing hardened concrete Part 5: Flexural strength of test specimensEnglish version of DIN EN 12390-5:2009-07Prfung von Festbeton Teil 5: Biegezugfestigkeit von ProbekrpernEnglische Fassung DIN EN 12390-5:2009-07SupersedesDIN EN 12390-5:2001-02 andDIN EN 12390-5 Corrigendum1:20
3、06-05www.beuth.deDocument comprises pages12DIN EN 12390-5:2009-07 National foreword This standard has been prepared by Technical Committee CEN/TC 104 “Concrete and related products” (Secretariat: DIN, Germany). The responsible German body involved in its preparation was the Normenausschuss Bauwesen
4、(Building and Civil Engineering Standards Committee), Technical Committee NA 005-07-05 AA Prfverfahren fr Beton. Amendments This standard differs from DIN EN 12390-5:2001-02 and DIN EN 12390-5 Corrigendum 1:2006-05 as follows: a) The standard has been editorially revised. b) The selected loading rat
5、e is to be applied after the initial load (not exceeding 20 % of the anticipated failure load). Previous editions DIN EN 12390-5: 2001-02 DIN EN 12390-5 Corrigendum 1: 2006-05 2 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 12390-5 February 2009 ICS 91.100.30 Supersedes EN 12390-5:2000 Englis
6、h Version Testing hardened concrete Part 5: Flexural strength of test specimens Essai pour bton durci Partie 5: Rsistance la flexion sur prouvettes Prfung von Festbeton Teil 5: Biegezugfestigkeit von Probekrpern This European Standard was approved by CEN on 27 December 2008. CEN members are bound to
7、 comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN Ma
8、nagement Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translationunder the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as
9、 the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France,Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania,Slova
10、kia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2009 CEN All rights of exploitation in any form and by any means reserved worldwide
11、for CEN national Members. Ref. No. EN 12390-5:2009: EEN 12390-5:2009 (E) Contents Page Foreword3 1 Scope 4 2 Normative references 4 3 Principle4 4 Apparatus .4 5 Test specimens5 6 Procedures .5 7 Expression of results 6 8 Test report 6 9 Precision.7 Annex A (normative) Loading by a centre-point load
12、9 2 DIN EN 12390-5:2009-07 EN 12390-5:2009 (E) Foreword This document (EN 12390-5:2009) has been prepared by Technical Committee CEN/TC 104 “Concrete and related products”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by pub
13、lication of an identical text or by endorsement, at the latest by August 2009, and conflicting national standards shall be withdrawn at the latest by August 2009. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC
14、shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 12390-5:2000. It is recognized good practice to include measurement of density prior to the determination of flexural strength, as a check on compaction of the concrete. The two-point method of l
15、oading has been taken as the reference method, but the use of centre-point loading has been included as a normative annex. An inter-comparison of the two-point and the centre-point methods has been made as part of a test programme, part-funded by the EC under the Measurement and Testing Programme, c
16、ontract MAT I-CT-94-CO43. The centre-point method gave results which were consistently 13 % higher than those from the two-point method. This standard is one of a series concerned with testing concrete. The series EN 12390 includes the following parts: EN 12390 Testing hardened concrete Part 1: Shap
17、e, dimensions and other requirements for specimens and moulds; Part 2: Making and curing specimens for strength tests; Part 3: Compressive strength of test specimens; Part 4: Compressive strength - Specification for testing machines; Part 5: Flexural strength of test specimens; Part 6: Tensile split
18、ting strength of test specimens; Part 7: Density of hardened concrete; Part 8: Depth of penetration of water under pressure. The following amendments have been made to the 2000-10 edition of this standard: editorial revision selected loading rate to be applied after the initial (not exceeding approx
19、 20% of the anticipated failure load) According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Gree
20、ce, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. 3 DIN EN 12390-5:2009-07 EN 12390-5:2009 (E) 1 Scope This European Standard specifies a method for the de
21、termination of the flexural strength of specimens of hardened concrete. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced
22、 document (including any amendments) applies. EN 12350-1, Testing fresh concrete Part 1: Sampling EN 12390-1:2000, Testing hardened concrete Part 1: Shape, dimensions and other requirements for test specimens and moulds EN 12390-2, Testing hardened concrete Part 2: Making and curing specimens for st
23、rength tests EN 12390-4, Testing hardened concrete Part 4: Compressive strength Specification for testing machines 3 Principle Prismatic specimens are subject to a bending moment by the application of load through upper and lower rollers. The maximum load sustained is recorded and the flexural stren
24、gth is calculated. 4 Apparatus 4.1 Testing machine The test shall be carried out using a testing machine conforming to EN 12390-4. 4.2 Force application The device for applying loads (see Figure 1) shall consist of: 1) two supporting rollers; 2) two upper rollers carried by an articulated cross memb
25、er, which divides the load applied by the machine equally between the two rollers. All rollers shall be manufactured from steel and shall have a circular cross-section with a diameter of 20 mm to 40 mm. They shall be at least 10 mm longer than the width of the test specimen. Three rollers, including
26、 the two upper ones, shall be capable of rotating freely around their axis and of being inclined in a plane normal to the longitudinal axis of the test specimen. The distance, I, between the outer rollers (i.e. the span) shall be equal to 3d, where d is the width of the specimen. The distance betwee
27、n the inner rollers shall be equal to d. The inner rollers shall be equally spaced between the outer rollers as shown in Figure 1. All rollers shall be adjusted to the positions illustrated in Figure 1 to an accuracy of 2,0 mm. 4 DIN EN 12390-5:2009-07 EN 12390-5:2009 (E) 5 Test specimens 5.1 Genera
28、l The test specimens shall be prisms conforming to EN 12390-1. Specimens cast in moulds shall conform to EN 12350-1 and EN 12390-2. The direction of casting shall be identified on the specimen. Sawn specimens which meet the requirements of EN 12390-1 may also be tested. The specimens shall be examin
29、ed and any abnormalities observed shall be reported. 5.2 Adjustment of test specimens Where the dimensions or shapes of test specimens do not conform to 4.4 of EN 12390-1:2000 because they exceed the respective tolerances, they shall be rejected or adjusted as follows: 1) uneven surfaces shall be le
30、velled by grinding; 2) the deviation of angles shall be corrected by cutting and/or grinding. 6 Procedures 6.1 Preparation and positioning of specimens Wipe clean all testing machine bearing surfaces and remove any loose grit or other extraneous material from the surfaces of the specimen that will b
31、e in contact with the rollers. For specimens stored in water, wipe excess moisture from the surface of the specimen before placing in the testing machine. Place the test specimen in the machine, correctly centred and with the longitudinal axis of the specimen at right angles to the longitudinal axis
32、 of the upper and lower rollers. Ensure that the reference direction of loading is perpendicular to the direction of casting of the specimen. NOTE The test result may be affected by the direction of loading with respect to the direction of casting. 6.2 Loading Do not apply the load until all loading
33、 and supporting rollers are resting evenly against the test specimen. Select a constant rate of stress within the range 0,04 MPa/s (N/mm.s) to 0,06 MPa/s (N/mm.s). After the application of the initial load, which does not exceed approximately 20% of the failure load, apply the load to the specimen w
34、ithout shock and increase continuously, at the selected constant rate 1 0 %, until no greater load can be sustained. The required loading rate is given by the formula: IddsR221= (1) where: R is the required loading rate, in N/s; 5 DIN EN 12390-5:2009-07 EN 12390-5:2009 (E) s is the stress rate, in M
35、Pa/s (N/mm.s); d1and d2are the lateral dimensions of the specimen, in mm; I is the spacing of the lower rollers, in mm. When using manually controlled testing machines, correct, by appropriate adjustment of the controls, any tendency for the selected rate of loading to decrease, as specimen failure
36、is approached. Record the maximum load indicated. Report a fracture if it is outside the loading rollers. (see Figure 1). 7 Expression of results The flexural strength is given by the equation: cf 212F Ifdd=(2) where fcfis the flexural strength, in MPa (N/mm); F is the maximum load, in N; I is the d
37、istance between the supporting rollers, in mm; d1and d2are the lateral dimensions of the specimen, in mm (see Figure 1). Express the flexural strength to the nearest 0,1 MPa (N/mm). 8 Test report The report shall include: a) identification of the test specimen; b) designated or measured dimensions o
38、f the specimen; c) details of adjustment by grinding (if appropriate); d) type of apparatus: two point/centre point; e) surface moisture condition of specimen at time of test (saturated/moist); f) date of test; g) maximum load at failure, in kN; h) flexural strength of specimen, to nearest 0,1 MPa (
39、N/mm); i) location of fracture (if outside upper rollers); j) appearance of the concrete (if unusual); 6 DIN EN 12390-5:2009-07 EN 12390-5:2009 (E) k) any deviation from the standard test method; l) a declaration from the person technically responsible for the test that it was carried out in accorda
40、nce with this document, except as detailed in item k). The report may include: m) condition of specimen on receipt for storage; n) age of specimen at time of test (if known); o) appearance of the concrete (if unusual). 9 Precision There is currently no precision data for this test, or the alternativ
41、e test set out in Annex A. Key 1 Loading roller (capable of rotation and of being inclined) 2 Supporting roller 3 Supporting roller (capable of rotation and of being inclined) Figure 1 Arrangement of loading of test specimen (two-point loading) 7 DIN EN 12390-5:2009-07 EN 12390-5:2009 (E) Key 1 Load
42、ing roller (capable of rotation and of being inclined) 2 Supporting roller 3 Supporting roller (capable of rotation and of being inclined) Figure 2 Arrangement of loading of test specimen (centre-point loading) 8 DIN EN 12390-5:2009-07 EN 12390-5:2009 (E) Annex A (normative) Loading by a centre-poin
43、t load A.1 General In the case where a centre-point load is used, the method of test shall be changed in accordance with this Annex. NOTE This method gives higher values for the flexural strength than the two-point method. An inter-comparison undertaken in the EC Measurement and Testing Programme, u
44、nder contract MAT 1-CT-94-0043, indicates that the centre-point loading method gives results consistently 13 % higher than the two-point loading method. A.2 Force application The loading arrangements shall consist of one load-applying roller at mid-span as indicated in Figure 2. The load-applying ro
45、ller shall be free to rotate. A.3 Loading application The load shall be applied in accordance with 6.2, except that the loading rate shall be determined in accordance with the formula: IsddR=32221(A.1) where: R is the required loading rate, in MPa (N/mm) s is the stress rate, in MPa/s (N/mm.s); d1an
46、d d2are the lateral dimensions of the specimen, in mm. (see Figure 2) I is the spacing of the lower rollers, in mm. 9 DIN EN 12390-5:2009-07 EN 12390-5:2009 (E) 10 A.4 Expression of results The flexural strength is given by the equation: cf 21232F Ifdd=(A.2) where fcfis the flexural strength, in MPa
47、 (N/mm); F is the maximum load, in N; I is the distance between the supporting rollers, in mm; d1and d2are the lateral dimensions of the cross-section, in mm. Express the flexural strength to the nearest 0,1 MPa (N/mm). A.5 Test report In the test report clearly indicate that the centre-point loading method was used. DIN EN 12390-5:2009-07