1、August 2014 Translation by DIN-Sprachendienst.English price group 7No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS
2、25.220.60!%:;1“2232414www.din.deDDIN EN 13523-26Coil coated metals Test methods Part 26: Resistance to condensation of water;English version EN 13523-26:2014,English translation of DIN EN 13523-26:2014-08Bandbeschichtete Metalle Prfverfahren Teil 26: Bestndigkeit gegen Kondenswasser;Englische Fassun
3、g EN 13523-26:2014,Englische bersetzung von DIN EN 13523-26:2014-08Tles prlaques Mthodes dessai Partie 26: Rsistance la condensation de leau;Version anglaise EN 13523-26:2014,Traduction anglaise de DIN EN 13523-26:2014-08SupersedesDIN EN 13523-26:2006-08www.beuth.deDocument comprises 10 pagesIn case
4、 of doubt, the German-language original shall be considered authoritative.07.14DIN EN 13523-26:2014-08 2 A comma is used as the decimal marker. National foreword This document (EN 13523-26:2014) has been prepared by Technical Committee CEN/TC 139 “Paints and varnishes”, (Secretariat: DIN, Germany),
5、Working Group WG 9 “Testing of coil coated metals” (Secretariat: DIN, Germany). The responsible German body involved in its preparation was the Normenausschuss Beschichtungsstoffe und Beschichtungen (DIN Standards Committee Coatings and Coating Materials), Working Committee NA 002-00-07 AA Allgemein
6、e Prfverfahren fr Beschichtungsstoffe und Beschichtungen. Amendments This standard differs from DIN EN 13523-26:2006-08 as follows: a) the description of the water cabinet has been revised and a figure showing an example of a water cabinet has been introduced; b) exposure times for the test panels h
7、ave been extended. Previous editions DIN EN 13523-26: 2006-08 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 13523-26 June 2014 ICS 25.220.60 Supersedes EN 13523-26:2006English Version Coil coated metals - Test methods - Part 26: Resistance to condensation of water Tles prlaques - Mthodes dess
8、ai - Partie 26: Rsistance la condensation de leau Bandbeschichtete Metalle - Prfverfahren - Teil 26: Bestndigkeit gegen Kondenswasser This European Standard was approved by CEN on 7 May 2014. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for
9、 giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three
10、 official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodi
11、es of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Sp
12、ain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2014 CEN All rights of exploitation in any form and by any means reserved worldwi
13、de for CEN national Members. Ref. No. EN 13523-26:2014 EEN 13523-26:2014 (E) 2 Contents Page Foreword 3 1 Scope 5 2 Normative references 5 3 Terms and definitions . 5 4 Principle 5 5 Apparatus . 5 5.1 Cabinet 5 6 Sampling . 6 7 Test panels . 6 8 Procedure . 6 8.1 Exposure . 6 8.2 Evaluation . 7 9 Ex
14、pression of results 7 10 Precision . 7 11 Test report 7 Bibliography 8 DIN EN 13523-26:2014-08 EN 13523-26:2014 (E) 3Foreword This document (EN 13523-26:2014) has been prepared by Technical Committee CEN/TC 139 “Paints and varnishes”, the secretariat of which is held by DIN. This European Standard s
15、hall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by December 2014, and conflicting national standards shall be withdrawn at the latest by December 2014. Attention is drawn to the possibility that some of the elements of this
16、 document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 13523-26:2006. The main technical changes are: a) the description of the water cabinet was amended and a figure showing an exampl
17、e of a water cabinet was introduced; b) exposure times for the test panels are amended. EN 13523, Coil coated metals Test methods, consists of the following parts: Part 0: General introduction Part 1: Film thickness Part 2: Gloss Part 3: Colour difference Instrumental comparison Part 4: Pencil hardn
18、ess Part 5: Resistance to rapid deformation (impact test) Part 6: Adhesion after indentation (cupping test) Part 7: Resistance to cracking on bending (T-bend test) Part 8: Resistance to salt spray (fog) Part 9: Resistance to water immersion Part 10: Resistance to fluorescent UV radiation and water c
19、ondensation Part 11: Resistance to solvents (rubbing test) Part 12: Resistance to scratching Part 13: Resistance to accelerated ageing by the use of heat Part 14: Chalking (Helmen method) DIN EN 13523-26:2014-08 EN 13523-26:2014 (E) 4 Part 18: Resistance to staining Part 19: Panel design and method
20、of atmospheric exposure testing Part 20: Foam adhesion Part 21: Evaluation of outdoor exposed panels Part 22: Colour difference Visual comparison Part 23: Resistance to humid atmospheres containing sulfur dioxide Part 24: Resistance to blocking and pressure marking Part 25: Resistance to humidity Pa
21、rt 26: Resistance to condensation of water Part 27: Resistance to humid poultice (Cataplasm test) Part 29: Resistance to environmental soiling (Dirt pick-up and striping) According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following countries are bound to i
22、mplement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Roma
23、nia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. DIN EN 13523-26:2014-08 Part 15: Metamerism Part 16: Resistance to abrasion Part 17: Adhesion of strippable filmsEN 13523-26:2014 (E) 51 Scope This Part of EN 13523 specifies a procedure for evaluating the resistance
24、 to continuous condensation of an organic coating on a metallic substrate, by means of exposure in a humidity cabinet under controlled conditions. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its applicatio
25、n. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 13523-0:2014, Coil coated metals Test methods Part 0: General introduction EN 13523-2, Coil coated metals Test methods Part 2: Gloss E
26、N 13523-3, Coil coated metals Test methods Part 3: Colour difference Instrumental comparison EN ISO 4628-2, Paints and varnishes Evaluation of degradation of coatings Designation of quantity and size of defects, and of intensity of uniform changes in appearance Part 2: Assessment of degree of bliste
27、ring (ISO 4628-2) 3 Terms and definitions For the purposes of this document, the definitions given in EN 13523-0:2014 apply. 4 Principle A test panel is exposed to continuous water condensation for a pre-determined time and at a specified temperature. The test panel is evaluated for any changes such
28、 as blistering or corrosion, e.g. red rust, white rust. Optionally, changes in colour and/or gloss are evaluated as well. 5 Apparatus Ordinary laboratory apparatus and glassware, together with the following: 5.1 Cabinet The apparatus consists essentially of an electrically heated water bath with tem
29、perature control and a cover designed to support the test panels which are placed at an angle of (60 5) to the horizontal, The tested face of the samples is facing down, the other face being exposed to the environment. If necessary, suitable inert blanking samples may be used to ensure the tightness
30、 of the chamber. The insulation of the cabinet shall be enough to guarantee constant temperature of the air space below the panels. An example for cabinet design is given in Figure 1. DIN EN 13523-26:2014-08 EN 13523-26:2014 (E) 6 Key 1 heated water bath 2 cover 3 test panel Figure 1 Principle desig
31、n of the humidity cabinet (cross view) 6 Sampling See EN 13523-0. 7 Test panels See EN 13523-0. The panels (usually 150 mm 100 mm) shall be flat and free from contamination. 8 Procedure 8.1 Exposure If specified, determine the gloss and colour before exposure. Position the test panels in the frame a
32、t an angle of (60 5) to the horizontal with the test surface facing down. Control the temperature of the water so that the temperature in the air space above the water is maintained at (38 2) C. Use deionised water, having a conductivity not greater than 0,5 mS/m and maintain the quantity of the wat
33、er throughout the test. Ambient temperature around the cabinet shall not exceed 23 C. Expose the test panels for 500 h, 1 000 h or 1 500 h, unless otherwise agreed. DIN EN 13523-26:2014-08 EN 13523-26:2014 (E) 78.2 Evaluation At the end of the required exposure period remove the panels from the cabi
34、net, carefully wipe off surface moisture with a soft tissue and immediately conduct the final evaluation. If required, take pictures to record any change caused by exposure. Inspect the surface for blisters in accordance with EN ISO 4628-2. If specified, evaluate the gloss difference in accordance w
35、ith EN 13523-2 and the colour difference in accordance with EN 13523-3. NOTE Edges are not evaluated, as they could be affected by the frame. 9 Expression of results The results shall be expressed as: blistering in accordance with EN ISO 4628-2; gloss difference in accordance with EN 13523-2; colour
36、 difference in accordance with EN 13523-3. 10 Precision No precision data are currently available. 11 Test report The test report shall contain at least the following information: a) all details necessary to identify the product tested; b) a reference to this part of EN 13523 (EN 13523-26); c) the d
37、uration of the exposure, in hours; d) the results of the test, as indicated in Clause 9; e) any deviation from the test method specified; f) any unusual features (anomalies) observed during the test; g) the date(s) of the test. DIN EN 13523-26:2014-08 EN 13523-26:2014 (E) 8Bibliography 1 EN 1396, Al
38、uminium and aluminium alloys Coil coated sheet and strip for general applications Specifications 2 EN 10169, Continuously organic coated (coil coated) steel flat products Technical delivery conditions 3 EN ISO 6270-1, Paints and varnishes Determination of resistance to humidity Part 1: Continuous condensation (ISO 6270-1) DIN EN 13523-26:2014-08