1、October 2014Translation by DIN-Sprachendienst.English price group 8No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS
2、25.220.60!%;s“2248004www.din.deDDIN EN 13523-4Coil coated metals Test methods Part 4: Pencil hardness;English version EN 13523-4:2014,English translation of DIN EN 13523-4:2014-10Bandbeschichtete Metalle Prfverfahren Teil 4: Bleistifthrte;Englische Fassung EN 13523-4:2014,Englische bersetzung von DI
3、N EN 13523-4:2014-10Tles prlaques Mthodes dessai Partie 4: Duret crayon;Version anglaise EN 13523-4:2014,Traduction anglaise de DIN EN 13523-4:2014-10SupersedesDIN EN 13523-4:2001-12www.beuth.deIn case of doubt, the German-language original shall be considered authoritative.Document comprises 11 pag
4、es09.14 DIN EN 13523-4:2014-10 2 A comma is used as the decimal marker. National foreword This document (EN 13523-4:2014) has been prepared by Technical Committee CEN/TC 139 “Paints and varnishes”, Working Group WG 9 “Testing of coil coated metals” (Secretariat: DIN, Germany). The responsible German
5、 body involved in its preparation was the DIN-Normenausschuss Beschichtungsstoffe und Beschichtungen (DIN Standards Committee Coatings and Coating Materials), Working Committee NA 002-00-07 AA Allgemeine Prfverfahren fr Beschichtungsstoffe und Beschichtungen. Amendments This standard differs from DI
6、N EN 13523-4:2001-12 as follows: a) the definition of pencil hardness has been revised; b) in the description of the test result, the term “remove the coating” was corrected to read “scratch the coating”; c) an information concerning the conditioning of the specimen has been added; d) for the applic
7、ability of the pencil hardness test, reference to EN ISO 15184 has been added. Previous editions DIN EN 13523-4: 2001-12 EN 13523-4July 2014 ICS 25.220.60 Supersedes EN 13523-4:2001English Version Coil coated metals - Test methods - Part 4: Pencil hardness Tles prlaques - Mthodes dessai - Partie 4:
8、Duret crayon Bandbeschichtete Metalle - Prfverfahren - Teil 4: Bleistifthrte This European Standard was approved by CEN on 14 June 2014. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national
9、 standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version
10、 in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czec
11、h Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey andUnited Kingdom. CEN
12、-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2014 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 13523-4:2014 EEUROPEAN COMMITTEE FOR STANDARDIZATIONCOMIT EUROPEN DE NORMALISATIONEUROPISCHES KOMITEE FR NORMUNGEURO
13、PEAN STANDARDNORME EUROPENNEEUROPISCHE NORMEN 13523-4:2014 (E) 2 Contents Page Foreword 3 1 Scope 5 2 Normative references 5 3 Terms and definitions .5 4 Principle 5 5 Apparatus and materials .5 6 Sampling .6 7 Test panels .6 8 Procedure .6 9 Expression of results 7 10 Precision .7 11 Test report 8
14、Bibliography 9 DIN EN 13523-4:2014-10EN 13523-4:2014 (E) 3 Foreword This document (EN 13523-4:2014) has been prepared by Technical Committee CEN/TC 139 “Paints and varnishes”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by
15、publication of an identical text or by endorsement, at the latest by January 2015 and conflicting national standards shall be withdrawn at the latest by January 2015. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENE
16、LEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 13523-4:2001. The main technical changes are: a) the definition of pencil hardness was amended; b) the term “remove the coating” was corrected to “scratch the coating” in the description of t
17、he result of the test; c) a remark on preconditioning was added; d) concerning the applicability of the pencil hardness test, a reference to EN ISO 15184 was added. EN 13523, Coil coated metals Test methods, consists of the following parts: Part 0: General introduction Part 1: Film thickness Part 2:
18、 Gloss Part 3: Colour difference Instrumental comparison Part 4: Pencil hardness Part 5: Resistance to rapid deformation (impact test) Part 6: Adhesion after indentation (cupping test) Part 7: Resistance to cracking on bending (T-bend test) Part 8: Resistance to salt spray (fog) Part 9: Resistance t
19、o water immersion Part 10: Resistance to fluorescent UV radiation and water condensation Part 11: Resistance to solvents (rubbing test) Part 12: Resistance to scratching DIN EN 13523-4:2014-10EN 13523-4:2014 (E) 4 Part 13: Resistance to accelerated ageing by the use of heat Part 14: Chalking (Helmen
20、 method) Part 15: Metamerism Part 16: Resistance to abrasion Part 17: Adhesion of strippable films Part 18: Resistance to staining Part 19: Panel design and method of atmospheric exposure testing Part 20: Foam adhesion Part 21: Evaluation of outdoor exposed panels Part 22: Colour difference Visual c
21、omparison Part 23: Resistance to humid atmospheres containing sulfur dioxide Part 24: Resistance to blocking and pressure marking Part 25: Resistance to humidity Part 26: Resistance to condensation of water Part 27: Resistance to humid poultice (Cataplasm test) Part 29: Resistance to environmental s
22、oiling (Dirt pick-up and striping) According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav
23、 Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. DIN EN 13523-4:2014-10EN 13523-4:2014 (E) 5 1 Scope
24、This part of EN 13523 describes the procedure to assess the relative hardness of an organic coating on a metallic substrate, by means of pencils of known hardness. Smooth surfaces will give more accurate results but the method is also applicable for textured surfaces. The more pronounced the texture
25、, the greater the unreliability of results. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of
26、the referenced document (including any amendments) applies. EN 13523-0:2014, Coil coated metals Test methods Part 0: General introduction EN 23270, Paints and varnishes and their raw materials - Temperatures and humidities for conditioning and testing (ISO 3270) 3 Terms and definitions For the purpo
27、ses of this document, the terms and definitions given in EN 13523-0:2014 and the following apply. 3.1 pencil hardness resistance of the coating surface to scratching when a pencil with a specified dimension, shape and hardness of the lead is pushed across the surface 4 Principle The coating is inten
28、tionally damaged by pencils of increasing hardness. The hardest lead which does not scratch the coating for a minimum of 3 mm length determines the degree of hardness. 5 Apparatus and materials Ordinary laboratory apparatus, together with the following: 5.1 Set of CretacolorTMor Faber Castell drawin
29、g pencils1)or their equivalents in the following range: 6B, 5B, 4B, 3B, 2B, B, HB, F, H, 2H, 3H, 4H, 5H, 6H (softer) (harder) 1) Cretacolor is the trade name of a product supplied by Brevillier b) a reference to this part of EN 13523 (EN 13523-4); c) identification of the pencils used; d) whether a
30、mechanical device has been used; e) the results of the test, as indicated in Clause 9; f) any deviation from the test method specified; g) any unusual features (anomalies) observed during the test; h) the date of the test. DIN EN 13523-4:2014-10EN 13523-4:2014 (E) 9 Bibliography EN 1396, Aluminium a
31、nd aluminium alloys - Coil coated sheet and strip for general applications - Specifications EN 10169, Continuously organic coated (coil coated) steel flat products Technical delivery conditions EN ISO 15184:2012, Paints and varnishes - Determination of film hardness by pencil test (ISO 15184:2012) DIN EN 13523-4:2014-10