1、February 2017 English price group 15No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 77.150.10!%an“2627592www.din.de
2、DIN EN 754-2Aluminium and aluminium alloys Cold drawn rod/bar and tube Part 2: Mechanical properties;English version EN 7542:2016,English translation of DIN EN 754-2:2017-02Aluminium und Aluminiumlegierungen Gezogene Stangen und Rohre Teil 2: Mechanische Eigenschaften;Englische Fassung EN 7542:2016,
3、Englische bersetzung von DIN EN 754-2:2017-02Aluminium et alliages daluminium Barres et tubes tirs Partie 2: Caractristiques mcaniques;Version anglaise EN 7542:2016,Traduction anglaise de DIN EN 754-2:2017-02SupersedesDIN EN 7542:201312www.beuth.deDocument comprises 41 pagesDTranslation by DIN-Sprac
4、hendienst.In case of doubt, the German-language original shall be considered authoritative.02.17 DIN EN 754-2:2017-02 2 A comma is used as the decimal marker. National foreword This document (EN 754-2:2016) has been prepared by Technical Committee CEN/TC 132 “Aluminium and aluminium alloys” (Secreta
5、riat: AFNOR, France), Working Group WG 5 “Extruded and drawn products” (Secretariat: SN, Norway). The responsible German body involved in its preparation was DIN-Normenausschuss Nichteisenmetalle (DIN Standards Committee Nonferrous Metals), Working Committee NA 066-01-04 AA Strangpresserzeugnisse. A
6、mendments This standard differs from DIN EN 754-2:2013-12 as follows: a) in Subclause 3.4, Table 5 has been amended. The second footnote has been changed to (previously ): b c“bS = width across flats for square and hexagonal bar, thickness for rectangular bar”; b) in Subclause 3.4, Table 34, “drawn
7、rod/bar”, in temper “T6”, a reference to has been added. cPrevious editions DIN 1746: 1938-09, 1947-11, 1951-11, 1959-06 DIN 1747: 1938-09, 1948-03, 1951-12, 1959-06, 1960-07 DIN 1746-1: 1963-06, 1968-12, 1976-12, 1987-01 DIN 1747-1: 1963-06, 1968-12, 1972-01, 1983-02 DIN EN 754-2: 1997-08, 2008-06,
8、 2013-12 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 754-2 November 2016 ICS 77.150.10 Supersedes EN 754-2:2013English Version Aluminium and aluminium alloys - Cold drawn rod/bar and tube - Part 2: Mechanical properties Aluminium et alliages daluminium - Barres et tubes tirs - Partie 2: Car
9、actristiques mcaniques Aluminium und Aluminiumlegierungen - Gezogene Stangen und Rohre - Teil 2: Mechanische EigenschaftenThis European Standard was approved by CEN on 15 August 2016. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving
10、this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three officia
11、l versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Au
12、stria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Swe
13、den, Switzerland, Turkey andUnited Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2016 CEN All rights of exploitation in any form and by any means reserved worldwide for CE
14、N national Members. Ref. No. EN 754-2:2016 EEN 754-2:2016 (E) 2 Contents Page European foreword . 3 1 Scope 4 2 Normative references 4 3 Mechanical property limits . 4 3.1 General 4 3.2 Elongation 4 3.3 Reference list of the tables of mechanical properties of the relevant aluminium and aluminium all
15、oys . 5 3.4 Detailed tables of mechanical properties. 6 Annex A (informative) List of tempers used in Tables 1 to 37 37 Bibliography . 39 DIN EN 754-2:2017-02 EN 754-2:2016 (E) 3 European foreword This document (EN 754-2:2016) has been prepared by Technical Committee CEN/TC 132 “Aluminium and alumin
16、ium alloys”, the secretariat of which is held by AFNOR. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by May 2017, and conflicting national standards shall be withdrawn at the latest by May 2017. A
17、ttention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 754-2:2013. CEN/TC 132 affirms its policy that if a patente
18、e refuses to grant licenses on standardized products under reasonable and not discriminatory conditions, this product will be removed from the corresponding document. EN 754 comprises the following parts under the general title “Aluminium and aluminium alloys Cold drawn rod/bar and tube“: Part 1: Te
19、chnical conditions for inspection and delivery Part 2: Mechanical properties Part 3: Round bars, tolerances on dimensions and form Part 4: Square bars, tolerances on dimensions and form Part 5: Rectangular bars, tolerances on dimensions and form Part 6: Hexagonal bars, tolerances on dimensions and f
20、orm Part 7: Seamless tubes, tolerances on dimensions and form Part 8: Porthole tubes, tolerances on dimensions and form According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium,
21、Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland
22、, Turkey and the United Kingdom. DIN EN 754-2:2017-02 EN 754-2:2016 (E) 4 1 Scope This European Standard specifies the mechanical property limits resulting from tensile testing applicable to aluminium and aluminium alloy cold drawn rod/bar and tube. Technical conditions for inspection and delivery,
23、including product and testing requirements, are specified in EN 754-1. Temper designations are defined in EN 515. The chemical composition limits for these materials are given in EN 573-3. 2 Normative references The following documents, in whole or in part, are normatively referenced in this documen
24、t and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 754-1:2016, Aluminium and aluminium alloys Cold drawn rod/bar and tube Part 1: Technical con
25、ditions for inspection and delivery EN ISO 6892-1, Metallic materials Tensile testing Part 1: Method of test at room temperature (ISO 6892-1) 3 Mechanical property limits 3.1 General The mechanical properties shall be in conformity with those specified in Table 1 to Table 37 or those agreed upon bet
26、ween supplier and purchaser and stated in the order document. For all alloys the condition F (as fabricated) can be used, but without guaranteed mechanical properties. Table 1 to Table 37 contain limits of mechanical property values obtained by tensile testing according to EN ISO 6892-1 after sampli
27、ng and test piece preparation according to EN 754-1. NOTE The mechanical properties refer to test pieces taken in the longitudinal direction. Mechanical properties of test pieces taken in other directions can differ from those for the longitudinal direction quoted in this standard. Brinell hardness
28、values given in Table 1 to Table 37 expressed as HBW values are for information only. 3.2 Elongation If not otherwise agreed, the A value shall be used. The A value for elongation is the % elongation measured over a gauge length of 05,65 S (where S0is the initial cross-sectional area of the test-pie
29、ce), and expressed in percent. For certain products the supplier may choose (if not otherwise specified in the order documents) to use the elongation based on A50mm.Consequently, values for the A50mmare included in the following tables. The A50mmvalue is the elongation measured over a gauge length o
30、f 50 mm and expressed in percent. Test pieces and their location in the specimen are given in EN 754-1. DIN EN 754-2:2017-02 EN 754-2:2016 (E) 5 3.3 Reference list of the tables of mechanical properties of the relevant aluminium and aluminium alloys Page Table 1 : Aluminium EN AW-1050A Al 99,5 6 Tab
31、le 2 : Aluminium EN AW-1200 AI 99,0 7 Table 3 : Alloy EN AW-2007 Al Cu4PbMgMn 8 Table 4 : Alloy EN AW-2011 AI Cu6BiPb 9 Table 5 : Alloy EN AW-2011A AI Cu6BiPb(A) 10 Table 6 : Alloy EN AW-2014 AI Cu4SiMg 11 Table 7 : Alloy EN AW-2014A AI Cu4SiMg(A) 12 Table 8 : Alloy EN AW-2017A AI Cu4MgSi(A) 13 Tabl
32、e 9 : Alloy EN AW-2024 AI Cu4Mg1 14 Table 10 : Alloy EN AW-2030 AI Cu4PbMg 15 Table 11 : Alloy EN AW-3003 AI Mn1Cu 16 Table 12 : Alloy EN AW-3103 AI Mn1 17 Table 13 : Alloy EN AW-5005 AI Mg1(B) 18 Table 14 : Alloy EN AW-5005A AI Mg1(C) 18 Table 15 : Alloy EN AW-5019 AI Mg5 19 Table 16 : Alloy EN AW-
33、5049 Al Mg2Mn0,8 20 Table 17 : Alloy EN AW-5251 AI Mg2Mn0,3 21 Table 18 : Alloy EN AW-5052 AI Mg2,5 22 Table 19 : Alloy EN AW-5154A AI Mg3,5(A) 23 Table 20 : Alloy EN AW-5754 AI Mg3 24 Table 21 : Alloy EN AW-5083 AI Mg4,5Mn0,7 25 Table 22 : Alloy EN AW-5086 AI Mg4 26 Table 23 : Alloy EN AW-6012 AI M
34、gSiPb 27 Table 24 : Alloy EN AW-6026 AI MgSiBi 27 Table 25 : Alloy EN AW-6060 AI MgSi 28 Table 26 : Alloy EN AW-6061 AI Mg1SiCu 29 Table 27 : Alloy EN AW-6262 AI Mg1SiPb 30 Table 28 : Alloy EN AW-6262A AI Mg1SiSn 30 Table 29 : Alloy EN AW-6063 AI Mg0,7Si 31 Table 30 : Alloy EN AW-6063A AI Mg0,7Si(A)
35、 32 Table 31 : Alloy EN AW-6064A AI Mg1SiBi 33 Table 32 : Alloy EN AW-6065 AI Mg1Bi1Si 33 Table 33 : Alloy EN AW-6082 AI Si1MgMn 34 DIN EN 754-2:2017-02 EN 754-2:2016 (E) 6 Table 34 : Alloy EN AW-7020 AI Zn4,5Mg1 34 Table 35 : Alloy EN AW-7022 AI Zn5Mg3Cu 35 Table 36 : Alloy EN AW-7049A AI Zn8MgCu 3
36、5 Table 37 : Alloy EN AW-7075 AI Zn5,5MgCu 36 3.4 Detailed tables of mechanical properties Table 1 Aluminium EN AW-1050A Al 99,5 Drawn rod/bar Temper Dimensions mm RmMPa Rp0,2MPa A % min. A50mm% min. HBW Typical value D aS bmin. max. min. max. O, H111 80 60 60 95 - - 25 22 20 H14 40 10 100 135 70 -
37、6 5 30 H16 15 5 120 160 105 - 4 3 35 H18 10 3 145 - 125 - 3 3 43 Drawn tube Temper Wall thickness t mm RmMPa Rp0,2MPa A % min. A50mm% min. HBW Typical value min. max. min. max. O, H111 20 60 95 - - 25 22 20 H14 10 100 135 70 - 6 5 30 H16 5 120 160 105 - 4 3 35 H18 3 145 - 125 - 3 3 43 aD = Diameter
38、for round bar. bS = Width across flats for square and hexagonal bar, thickness for rectangular bar. DIN EN 754-2:2017-02 EN 754-2:2016 (E) 7 Table 2 Aluminium EN AW-1200 Al 99,0 Drawn rod/bar Temper Dimensions mm RmMPa Rp0,2MPa A % min. A50mm% min. HBW Typical value D aS bmin. max. min. max. O, H111
39、 80 60 70 105 - - 20 16 23 H14 40 10 110 145 80 - 5 4 37 H16 15 5 135 170 115 - 3 3 45 H18 10 3 150 - 130 - 3 3 50 Drawn tube Temper Wall thickness t mm RmMPa Rp0,2MPa A % min. A50mm% min. HBW Typical value min. max. min. max. O, H111 20 70 105 - - 20 16 23 H14 10 110 145 80 - 5 4 37 H16 5 135 170 1
40、15 - 3 3 45 H18 3 150 - 130 - 3 3 50 aD = Diameter for round bar. bS = Width across flats for square and hexagonal bar, thickness for rectangular bar. DIN EN 754-2:2017-02 EN 754-2:2016 (E) 8 Table 3 Alloy EN AW-2007 Al Cu4PbMgMn Drawn rod/bar Temper Dimensions mm RmMPa Rp0,2MPa A % min. A50mm% min.
41、 HBW Typical value D aS bmin. max. min. max. T3 c 30 30 D 80 30 30 S 80 370 340 - 240 220 - 7 6 5 - 95 95 T351 c 80 80 370 - 240 - 5 3 95 Drawn tube Temper Wall thickness t mm RmMPa Rp0,2MPa A % min. A50mm% min. HBW Typical value min. max. min. max. T3 c 20 370 - 250 - 7 5 95 T3510 T3511 c 20 370 -
42、240 - 5 3 95 aD = Diameter for round bar. bS = Width across flats for square and hexagonal bar, thickness for rectangular bar. cProperties may be obtained by press quenching. DIN EN 754-2:2017-02 EN 754-2:2016 (E) 9 Table 4 Alloy EN AW-2011 Al Cu6BiPb Drawn rod/bar Temper Dimensions mm RmMPa Rp0,2MP
43、a A % min. A50mm% min. HBW Typical value D aS bmin. max. min. max. T3 40 40 D 50 50 D 80 40 40 S 50 50 S 80 320 300 280 - - - 270 250 210 - - - 10 10 10 8 - - 90 90 90 T8 80 80 370 - 270 - 8 6 115 Drawn tube Temper Wall thickness t mm RmMPa Rp0,2MPa A % min. A50mm% min. HBW Typical value min. max. m
44、in. max. T3 c 5 5 t 20 310 290 - - 260 240 - - 10 8 8 6 90 90 T8 20 370 - 275 - 8 6 115 aD = Diameter for round bar. bS = Width across flats for square and hexagonal bar, thickness for rectangular bar. cProperties may be obtained by press quenching. DIN EN 754-2:2017-02 EN 754-2:2016 (E) 10 Table 5
45、Alloy EN AW-2011A Al Cu6BiPb(A) Drawn rod/bar Temper Dimensions mm RmMPa Rp0,2MPa A % min. A50mm% min. HBW Typical value D aS bmin. max. min. max. T3 40 40 D 50 50 D 80 40 40 S 50 50 S 80 320 300 280 - - - 270 250 210 - - - 10 10 10 8 - - 90 90 90 T8 80 80 370 - 270 - 8 6 115 Drawn tube Temper Wall
46、thickness t mm RmMPa Rp0,2MPa A % min. A50mm% min. HBW Typical value min. max. min. max. T3 c 5 5 t 20 310 290 - - 260 240 - - 10 8 8 6 90 90 T8 20 370 - 275 - 8 6 115 aD = Diameter for round bar. bS = Width across flats for square and hexagonal bar, thickness for rectangular bar. cProperties may be
47、 obtained by press quenching. DIN EN 754-2:2017-02 EN 754-2:2016 (E) 11 Table 6 Alloy EN AW-2014 Al Cu4SiMg Drawn rod/bar Temper Dimensions mm RmMPa Rp0,2MPa A % min. A50mm% min. HBW Typical value D aS bmin. max. min. max. O, H111 80 80 - 240 - 125 12 10 45 T3 80 80 380 - 290 - 8 6 110 T351 80 80 38
48、0 - 290 - 6 4 110 T4 80 80 380 - 220 - 12 10 110 T451 80 80 380 - 220 - 10 8 110 T6 80 80 450 - 380 - 8 6 140 T651 80 80 450 - 380 - 6 4 140 Drawn tube Temper Wall thickness t mm RmMPa Rp0,2MPa A % min. A50mm% min. HBW Typical value min. max. min. max. O, H111 20 - 240 - 125 12 10 45 T3 20 380 - 290 - 8 6 110 T3510, T3511 20 380 - 290 - 6 4 110 T4 20 380 - 240 - 12 10 110 T4510, T4511 20 380 - 240 - 10 8 110 T6 20 450 - 380 - 8 6 140 T6510, T6511 20 450 - 380 - 6 4 140 aD = Diameter for round bar. bS = Width acr