1、December 2010 Translation by DIN-Sprachendienst.English price group 7No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).IC
2、S 25.220.20!$ld b) the standard has been editorially revised. Previous editions DIN EN 12373-16: 2001-10 DIN EN ISO 2085:2010-12 3 National Annex NA (informative) Correspondence between the previous standards series DIN EN 12373 “Aluminium and aluminium alloys Anodizing” and the corresponding new IS
3、O and DIN EN ISO Standards Table NA.1 Correspondence previous now DIN EN 12373 DIN EN ISO Anodizing of aluminium and its alloys Part 1 7599 General specifications for anodic oxidation coatings on aluminium The title has been slightly changed Part 2 2106 Determination of mass per unit area (surface d
4、ensity) of anodic oxidation coatings Gravimetric method Part 3 2128 Determination of thickness of anodic oxidation coatings Non-destructive measurement by split-beam microscope Part 4 2143 Estimation of loss of absorptive power of anodic oxidation coatings after sealing Dye spot test with prior acid
5、 treatment Part 5 2931 Assessment of quality of sealed anodic oxidation coatings by measurement of admittance Part 6 Part 7 3210 Assessment of quality of sealed anodic oxidation coatings by measurement of the loss of mass after immersion in phosphoric acid/chromic acid solution The title has been ch
6、anged: with/without prior acid treatment Part 8 Determination of the comparative fastness to ultra-violet light and heat of coloured anodic oxidation coatings Part 9 Part 10 8251 Measurement of abrasion resistance of anodic oxidation coatings The title has been changed Part 11 7668 Measurement of sp
7、ecular reflectance and specular gloss of anodic oxidation coating at angles of 20 degrees, 45 degrees, 60 degrees or 85 degrees Part 12 6719 Measurement of reflectance characteristics of aluminium surfaces using integrating-sphere instruments Part 13 7759 Measurement of reflectance characteristics o
8、f aluminium surface using a goniophotometer or an abridged goniophotometer The German title has been slightly changed Part 14 10215 Visual determination of image clarity of anodic oxidation coatings Chart scale method Part 15 3211 Assessment of resistance of anodic oxidation coatings to cracking by
9、deformation Part 16 2085 Check for continuity of thin anodic oxidation coatings Copper sulphate test Part 17 2376 Determination of electric breakdown potential Part 18 8993 Rating system for the evaluation of pitting corrosion Chart method Part 19 8994 Rating system for the evaluation of pitting cor
10、rosion Grid method 6581DIN EN ISO 2085:2010-12 4 This page is intentionally blank EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN ISO 2085 August 2010 ICS 25.220.20 Supersedes EN 12373-16:2001English Version Anodizing of aluminium and its alloys - Check for continuity of thin anodic oxidation c
11、oatings - Copper sulfate test (ISO 2085:2010) Anodisation de laluminium et de ses alliages - Contrle de la continuit des couches anodiques minces - Essai au sulfate de cuivre (ISO 2085:2010) Anodisieren von Aluminium und Aluminiumlegierungen - Prfung der Kontinuitt dnner anodisch erzeugter Oxidschic
12、hten - Kupfersulfatversuch (ISO 2085:2010) This European Standard was approved by CEN on 28 July 2010. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration.
13、Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation
14、 under the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Ger
15、many, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUN
16、G Management Centre: Avenue Marnix 17, B-1000 Brussels 2010 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN ISO 2085:2010: EContents DIN EN ISO 2085:2010-12 EN ISO 2085:2010 (E) 2 Page Foreword3 1 Scope 4 2 Principle4 3 Reagents.4
17、4 Procedure .4 5 Expression of results 5 6 Test report 5 Foreword This document (EN ISO 2085:2010) has been prepared by Technical Committee ISO/TC 79 Light metals and their alloys” in collaboration with Technical Committee CEN/TC 132 “Aluminium and aluminium alloys” the secretariat of which is held
18、by AFNOR. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by February 2011, and conflicting national standards shall be withdrawn at the latest by February 2011. Attention is drawn to the possibility
19、 that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 12373-16:2001. According to the CEN/CENELEC Internal Regulations, the national standards organi
20、zations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Port
21、ugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. Endorsement notice The text of ISO 2085:2010 has been approved by CEN as a EN ISO 2085:2010 without any modification. “DIN EN ISO 2085:2010-12 EN ISO 2085:2010 (E) 3 1 Scope This International Standard specifies a
22、method for checking the continuity of thin anodic oxidation coatings on aluminium and its alloys by a copper sulfate contact test. The use of this method is limited to anodic oxidation coatings of thickness less than 5 m, or coatings that have been deformed. NOTE The method described enables a rapid
23、 check to be made for the continuity of a thin coating of aluminium oxidation on aluminium and its alloys. In cases of doubt regarding a visible fault on the surface of a coating, the use of this method makes it possible to verify whether the fault corresponds to a local gap in the coating which exp
24、oses bare metal. 2 Principle Drops of copper sulfate reagent are placed on surface areas of about 100 mm2, chosen at will on the test pieces, avoiding the anodizing contact areas. If the area includes points where the metal is either bare or poorly covered, chemical deposition of copper takes place
25、on the aluminium, accompanied by a release of gas. The drops of applied reagent can be examined immediately upon application, either with the naked eye or with a magnifying glass, for the release of gas from points where the metal is bare, which is almost instantaneous. After the test, black and/or
26、dark reddish spots can be seen where the coating is not continuous. 3 Reagents 3.1 Copper sulfate solution, prepared as follows: copper(II) sulfate pentahydrate, (CuSO45H2O): 20 g; hydrochloric acid (20= 1,18 g/ml): 20 ml; distilled water or deionized water: make up to 1 000 ml. 4 Procedure Carry ou
27、t the test at room temperature. Remove all grease from the test piece. Mark out a test area of approximately 100 mm2on a horizontal part of the test piece, using a wax crayon or a rapidly drying lacquer to delineate the test area, leaving the test area itself unmasked. Cover the test area with the r
28、eagent (3.1), using approximately four drops. Leave the reagent in contact with the surface for 5 min, noting any release of gas, then rinse the area with clean water. Examine the surface and count the number of black and/or dark reddish spots per 100 mm2. DIN EN ISO 2085:2010-12 EN ISO 2085:2010 (E
29、) 4 NOTE For a more quantitative measurement, the average diameter of the black and/or dark reddish spots can also be estimated. 5 Expression of results Record the number of black and/or dark reddish spots per 100 mm2for each area examined and, if appropriate, their average diameter. 6 Test report T
30、he test report shall include at least the following information: a) a reference to this International Standard (ISO 2085:2010); b) the type and identification of the product tested; c) the results of the test (see Clause 5); d) anything unusual noticed during the determination; e) the date of the test. DIN EN ISO 2085:2010-12 EN ISO 2085:2010 (E) 5