1、 DETAIL SPECIFICATION SHEET FILLER TUBE, FUEL TANK MILITARY VEHICLES Inactive for new design after 22 January 1999. This specification is approved for use by all Departments and Agencies of the Department of Defense. The requirements for acquiring the product described herein shall consist of this s
2、pecification sheet. FIGURE 1. Filler tube. ASMC N/A FSC 2910 INCH-POUND MS90908C 09 May 2011 SUPERSEDING MS90908B (AT) 10 December 1982 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHSMS90908C 2 Inches mm Inches mm Inches mm Inches mm .049 1.2446 . 375 8.
3、255 .905 22.987 3.00 76.2 .059 1.4986 . 4375 11.1125 1.00 25.4 3.440 87.376 .0625 1.5875 .625 15.875 1.940 49.275 3.500 88.9 .125 3.175 .670 17.018 2.00 50.8 6.1875 157.1625 NOTES: 1. Dimensions are in inches. Tolerances are 1/64 on fractions, .010 on decimals, 1 on angles. 2. Metric equivalents are
4、 given for information only. 3. All dimensions are “reference” dimensions. 4. For design feature purposes, this standard takes precedence over acquisition documents referenced herein. 5. In the event of a conflict between the text of this specification sheet and the references cited herein, the text
5、 of this specification sheet shall take precedence. 6. This document is not intended to limit construction to features other than as shown herein by dimensions, notations or referenced documents. FIGURE 1. Filler tube Continued. REQUIREMENTS: Filler tube shall be specified on figure 1. Strainer mate
6、rial shall be cloth, wire, industrial, square mesh, plain square weave, copper-zinc alloy or phosphor bronze, 60 X 60 mesh specified in ASTM-E2016. Materials of other parts shall be steel, low-carbon 0.15% maximum, grade 1008 to 1012 HR or CR with temper 4 or temper 5 in accordance with QQ-S-698. Op
7、tional material: ASTM-A1011/A1011M, Grade CS Type B, ASTM-A1008/A1008M, Grade CS Type B, or ASTM-A513 Grades 1008 or 1010. Welding rod shall be Type I in accordance with SAE-AMS6457. Resistance spot welding shall be in accordance with AWS-D8.7 and AWS-D8.9. Arc welding shall be Type I in accordance
8、with AWS-D1.1/D1.1M. Solder shall be composition 40 or 50 in accordance with J-STD 004, J-STD 005, and J-STD 006 or composition 40 or 50 in accordance with ASTM-B32. Surface shall be free from burrs and sharp edges. Protective coating prior to installation of strainer: Assembly shall be protected wi
9、th zinc coating in accordance with ASTM-A153/A153M or zinc coating (electrodeposited) in accordance with ASTM-B633, Fe/Zn 5, Type VI. Marking shall consist of the Part Identification Number (PIN) and manufacturers identification in accordance with MIL-STD-130. Chain clip shall be in accordance with
10、RR-C-271, Type II, Class 6, classified as an attachment, Type II is a connecting link, use of one link for the chain clip. Provided by IHSNot for Resale-,-,-MS90908C 3 Part or Identifying Number (PIN). Example of a PIN: MS90908-1 (base number) Changes from previous issue. Marginal notations are not
11、used in this revision to identify changes with respect to the previous issue due to the extent of the changes. Referenced documents. This document references the following: MIL-STD-130 ASTM-B633 MS35644 ASTM-E2016 QQ-S-698 AWS-D1.1/D1.1M RR-C-271 AWS-D8.7 ASTM-A153/A153M AWS-D8.9 ASTM-A513 J-STD-004
12、 ASTM-A1008/A1008M J-STD-005 ASTM-A1011/A1011M J-STD-006 ASTM-B32 SAE-AMS6457 CONCLUDING MATERIAL Custodians: Preparing activity: Army AT DLA CC Navy SH Air Force 99 (Project 2910-2010-002) DLA CC Review activities: Army CR4 Navy MC, SA, YD Air Force 71 NOTE: The activities listed above were interested in this document as of the date of this document. Since organizations and responsibilities can change, you should verify the currency of the information above using the ASSIST Online database at https:/assist.daps.dla.mil. Provided by IHSNot for Resale-,-,-