1、BS EN 1465:2009ICS 83.180NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBRITISH STANDARDAdhesives Determination oftensile lap-shearstrength of bondedassembliesThis British Standardwas published under theauthority of the StandardsPolicy and StrategyCommittee on 31 March2009 BSI
2、 2009ISBN 978 0 580 62631 9Amendments/corrigenda issued since publicationDate CommentsBS EN 1465:2009National forewordThis British Standard is the UK implementation of EN 1465:2009. Itsupersedes BS EN 1465:1995 which is withdrawn.The UK participation in its preparation was entrusted to TechnicalComm
3、ittee PRI/52, Adhesives.A list of organizations represented on this committee can be obtained onrequest to its secretary.This publication does not purport to include all the necessary provisionsof a contract. Users are responsible for its correct application.Compliance with a British Standard cannot
4、 confer immunityfrom legal obligations.BS EN 1465:2009EUROPEAN STANDARDNORME EUROPENNEEUROPISCHE NORMEN 1465February 2009ICS 83.180 Supersedes EN 1465:1994 English VersionAdhesives - Determination of tensile lap-shear strength ofbonded assembliesAdhsifs - Dtermination de la rsistance au cisaillement
5、en traction dassemblages colls recouvrement simpleKlebstoffe - Bestimmung der Zugscherfestigkeit vonberlappungsklebungenThis European Standard was approved by CEN on 27 December 2008.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving t
6、his EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such nationalstandards may be obtained on application to the CEN Management Centre or to any CEN member.This European Standard exists in three official versions (
7、English, French, German). A version in any other language made by translationunder the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as theofficial versions.CEN members are the national standards bodies of Austria, Belgium, Bulgari
8、a, Cyprus, Czech Republic, Denmark, Estonia, Finland,France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATIO
9、NCOMIT EUROPEN DE NORMALISATIONEUROPISCHES KOMITEE FR NORMUNGManagement Centre: Avenue Marnix 17, B-1000 Brussels 2009 CEN All rights of exploitation in any form and by any means reservedworldwide for CEN national Members.Ref. No. EN 1465:2009: EBS EN 1465:2009EN 1465:2009 (E) 2 Contents Page Forewo
10、rd 3Introduction .41 Scope 52 Normative references 53 Principle 54 Apparatus .55 Specimens 66 Conditioning and testing atmosphere .67 Procedure .68 Expression of results 79 Test report 7Bibliography 9BS EN 1465:2009EN 1465:2009 (E) 3 Foreword This document (EN 1465:2009) has been prepared by Technic
11、al Committee CEN/TC 193 “Adhesives”, the secretariat of which is held by AENOR. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by August 2009, and conflicting national standards shall be withdrawn a
12、t the latest by August 2009. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 1465:1994. According to the C
13、EN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania,
14、 Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. BS EN 1465:2009EN 1465:2009 (E) 4 Introduction Safety statement Persons using this document should be familiar with the normal laboratory practice, if applicable
15、. This document does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user to establish appropriate safety and health practices and to ensure compliance with any regulatory conditions. ENVIRONMENTAL STATEMENT It is understood that so
16、me of the material permitted in this standard may have negative environmental impact. As technological advantages lead to acceptable alternatives for these materials, they will be eliminated from this standard to the extent possible. At the end of the test, the user of the standard shall take care t
17、o carry out an appropriate disposal of the wastes, according to local regulation. BS EN 1465:2009EN 1465:2009 (E) 5 1 Scope This European Standard specifies a method for determining the tensile lap-shear strength of bonded assemblies when tested on a standard specimen and under specified conditions
18、of preparation and testing. NOTE 1 This test procedure is not applicable for calculations needed for bond design in structural joints. NOTE 2 This test Test methods for the determination of tensile lap-shear strength of bonded assemblies with wood adhesives are also specified in EN 205 and EN 302-1
19、2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 13887, Structural Adhes
20、ives - Guidelines for surface preparation of metals and plastics prior to adhesive bonding EN ISO 291, Plastics - Standard atmospheres for conditioning and testing (ISO 291:2005) EN ISO 527-1, Plastics - Determination of tensile properties - Part 1: General principles (ISO 527-1:1993 including Corr
21、1:1994) EN ISO 10365, Adhesives - Designation of main failure patterns (ISO 10365:1992) 3 Principle Adhesive lap-shear bond strength is determined by stressing in shear of a single overlap joint (see Figure 1) between rigid adherends by applying to the adherends a tensile force which is parallel to
22、the bond area and to the major axis of the specimen. The reported result is the observed force or stress at rupture. 4 Apparatus 4.1 Testing machine It shall comply with a test machine, class 1 and the response time of the machine shall be short enough not to affect the accuracy with which the force
23、 applied at the time of rupture can be measured. NOTE The recorded force shall not differ from the true applied force by more than 1%. The machine shall be capable of applying a tensile force that increases at a steady rate. Where equipment does not allow for constant rate of load application, a rat
24、e of jaw separation shall be used which approximates the rate of loading (see EN ISO 527-1). It shall be provided with a suitable pair of self-aligning grips to hold the specimen. The grips and attachments shall be so constructed that they will move into alignment with the test specimen as soon as t
25、he load is applied, so that the long axis of the test specimen will coincide with the direction of the applied force through the centre line of the grip assembly to avoid bending moment. Grips that operate by bolting through the adherends shall be avoided since such grips give rise to undesirable st
26、ress concentration. 4.2 Jig for accurately locating adherends during bonding. BS EN 1465:2009EN 1465:2009 (E) 6 5 Specimens 5.1 Unless otherwise specified, test specimens shall conform to the form, dimensions, and alignment as shown in Figure 1. The recommended length (L) of overlap is (12,5 0,25) m
27、m. NOTE 1 The choice of dimensions other than those shown in the Figure 1 may result in difficulties in the interpretation of results. NOTE 2 This overlap is intended for aluminium alloys and materials of similar or higher moduli of elasticity (E) and tensile yield strength. EXAMPLE For AA 2024-T3 o
28、r AECMA AL-P 13 PL (T3) : E = 68 000 MPa Tensile yield strength at 0,2 % offset = 290 MPa. 5.2 The test joints may be prepared either individually or from slotted or unslotted panels (see Figure 1). Each method is equally suitable either for development or for comparative tests. 5.3 The adherend sur
29、face shall be properly treated to obtain an optimum bond. Surface treatments shall be in accordance with manufacturers instructions or EN 13887 unless otherwise specified. The adhesive shall be applied and cured according to the recommendations of the manufacturer of the adhesive. In the absence of
30、such recommendations, the procedure shall be such as to achieve an optimum bond with minimum variations. In any case, the use of a jig to ensure the correct overlap and accurate alignment of the adherends is recommended. Special care shall be taken in preparing individual specimens to ensure proper
31、alignment and that bond thicknesses are as uniform and constant as possible. The thickness should orient itself to the intended use. A typical thickness is 0,2 mm. Thicknesses can be controlled by inserting a calibrated wire spacer or small glass spheres in the bond area. If a wire spacer is used, t
32、he wire shall lie parallel to the direction of application ot the load as this minimizes the effect of the wire on the joint. The surfaces shall be prepared according to EN 13887 unless otherwise specified. For all adherends the method used for surface preparation shall be reported. 5.4 The number o
33、f test specimens will depend on the precision required, but reliance should not be placed on fewer than 5 observations. 6 Conditioning and testing atmosphere The test specimens shall be conditioned and tested in one of the standard laboratory atmospheres specified in EN ISO 291. 7 Procedure Locate t
34、he test specimen symmetrically in the grips, with each grip (50 1) mm from the nearest edge of the overlap. A shim may be used in the grips so that the applied force will be in the plane of the adhesive bond. Operate the machine so that the stress or strain on the test joint increases at a constant
35、(i.e. steady) rate. This rate shall be such that the average joint will be broken in a period of (65 20) s. Record the highest force during rupture as the breaking force of that specimen. Results from test specimens that rupture in the adherend shall be discarded except for routine testing and noted
36、 in the test report. BS EN 1465:2009EN 1465:2009 (E) 7 8 Expression of results Express the results of the tests as the arithmetic mean and coefficient of variation of the breaking force in newtons or the breaking stress in megapascals of the valid test specimens. The tensile lap-shear strenght, in m
37、egapascals, is calculated by dividing the breaking force, in newtons, by the shear area, in square milimeters. NOTE It is suggested that the following criteria for repeatability and reproductibility should normally be observed for test results obtained using this European Standard: a) the repeatibil
38、ity (see ISO 3534-1) (i.e. the difference between any two breaking forces obtaines with one sample of adhesive by the same operator in a given test room or laboratory) should be less than 2,5 times the standard deviation. b) the reproductibility (see ISO 3534-1) (i.e. the difference between the mean
39、 breaking forces obtained with one sample of adhesive on the same system in different test rooms or laboratories) should be less than 20 % of the arithmetic mean of the individual mean values. It is stressed that these criteria are offered for guidance; failure to meet one or other of the requiremen
40、ts does not of itself imply failure to comply with this European Standard. 9 Test report The test report shall include, at least, the following: a) reference to this European Standard (EN 1465); b) identification of the adhesive tested, including type, source, manufacturers code number, batch or lot
41、 number, form, etc.; c) identification of adherends, including material thickness, width and surface preparation; d) description of bonding process, including method of application of adhesive, drying or precuring conditions (where applicable), and curing or setting time, temperature and pressure; e
42、) average thickness (as precisely as praticable) of the adhesive layer after formation of the bond, as well as the method used for controling the bond thickness; f) complete description of the test specimen, including dimensions and construction of the test specimen, with nominal overlap of the join
43、t, whether individual or of panel construction, whether slotted or unslotted panels, conditions used for cutting individual test specimens, number of test panels represented, and number of individual test specimens; g) conditioning procedure and applied parameters prior to testing, and test atmosphe
44、re; h) the rate of loading or rate of jaw separation; i) the individual breaking force or stress test results, the arithmetic mean and the coefficient of variation of the mean, together with information about the spread of results; j) type of failure according to EN ISO 10365; k) result from test sp
45、ecimens that rupture in the adherends; l) any operating deviations or difficulties that may have affected the results. BS EN 1465:2009EN 1465:2009 (E) 8 Dimensions in millimetres Key 1 discard 4 area in test grips 2 typically (90 1) 5 shear area 3 adhesive line Figure 1 Forms and dimensions of test
46、panels BS EN 1465:2009EN 1465:2009 (E) 9 Bibliography 1 ISO 3534-1, Statistics - Vocabulary and symbols - Part 1: General statistical terms and terms used in probability BS EN1465:2009BSI GroupHeadquarters 389Chiswick High Road,London, W4 4AL, UKTel +44 (0)20 8996 9001Fax +44 (0)20 8996 - British S
47、tandards InstitutionBSI is the independent national body responsible for preparing BritishStandards. It presents the UK view on standards in Europe and at theinternational level. It is incorporated by Royal Charter.RevisionsBritish Standards are updated by amendment or revision. Users of BritishStan
48、dards should make sure that they possess the latest amendments oreditions.It is the constant aim of BSI to improve the quality of our products and services.We would be grateful if anyone finding an inaccuracy or ambiguity while usingthis British Standard would inform the Secretary of the technical c
49、ommitteeresponsible, the identity of which can be found on the inside front cover. Tel:+44 (0)20 8996 9000. Fax: +44 (0)20 8996 7400.BSI offers members an individual updating service called PLUS which ensuresthat subscribers automatically receive the latest editions of standards.Buying standardsOrders for all BSI, international and foreign standards publications should beaddressed to Customer Services. Tel: +44 (0)20 8996 9001. Fax: +44 (0)20 89967001 Email: