1、raising standards worldwideNO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBSI Standards PublicationBS EN ISO 4136:2012Destructive tests on welds inmetallic materials Transversetensile test (ISO 4136:2012)BS EN ISO 4136:2012 BRITISH STANDARDNational forewordThis British Standar
2、d is the UK implementation of EN ISO 4136:2012.It supersedes BS EN ISO 4136:2011 which is withdrawn.The UK participation in its preparation was entrusted to TechnicalCommittee WEE/46, Non-destructive testing.A list of organizations represented on this committee can beobtained on request to its secre
3、tary.This publication does not purport to include all the necessaryprovisions of a contract. Users are responsible for its correctapplication. The British Standards Institution 2012. Published by BSI StandardsLimited 2012ISBN 978 0 580 79570 1ICS 25.160.40Compliance with a British Standard cannot co
4、nfer immunity fromlegal obligations.This British Standard was published under the authority of theStandards Policy and Strategy Committee on 30 November 2012.Amendments issued since publicationDate Text affectedEUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN ISO 4136 November 2012 ICS 25.160.40
5、 Supersedes EN ISO 4136:2011English Version Destructive tests on welds in metallic materials - Transverse tensile test (ISO 4136:2012) Essais destructifs des soudures sur matriaux mtalliques -Essai de traction transversale (ISO 4136:2012) Zerstrende Prfung von Schweiverbindungen an metallischen Werk
6、stoffen - Querzugversuch (ISO 4136:2012) This European Standard was approved by CEN on 31 October 2012. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration.
7、 Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by tr
8、anslation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Fin
9、land, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZAT
10、ION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2012 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN ISO 4136:2012: EBS EN ISO 4136:2012EN ISO 4136:2012 (E) 3 F
11、oreword This document (EN ISO 4136:2012) has been prepared by Technical Committee ISO/TC 44 “Welding and allied processes” in collaboration with Technical Committee CEN/TC 121 “Welding” the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard,
12、either by publication of an identical text or by endorsement, at the latest by May 2013, and conflicting national standards shall be withdrawn at the latest by May 2013. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or C
13、ENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN ISO 4136:2011. According to the CEN/CENELEC Internal Regulations, the national standards organisations of the following countries are bound to implement this European Standard: Austria, Be
14、lgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Swit
15、zerland, Turkey and the United Kingdom. Endorsement notice The text of ISO 4136:2012 has been approved by CEN as a EN ISO 4136:2012 without any modification. BS EN ISO 4136:2012ISO 4136:2012(E) ISO 2012 All rights reserved iiiContents PageForeword iv1 Scope . 12 Normative references 13 Principle 14
16、Symbols and abbreviated terms . 15 Preparation of test specimens 25.1 Location . 25.2 Marking . 25.3 Heat treatment and/or ageing . 25.4 Extraction 35.5 Machining 36 Test procedure 77 Test results 77.1 General . 77.2 Location of fracture . 77.3 Examination of fracture surfaces 78 Test report . 7Anne
17、x A (informative) Example of a test report . 9BS EN ISO 4136:2012ISO 4136:2012(E)ForewordISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
18、ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates
19、 closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.The main task of technical committees is to prepare International Standards. D
20、raft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote.Attention is drawn to the possibility that some of the elements of this doc
21、ument may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights.ISO 4136 was prepared by Technical Committee ISO/TC 44, Welding and allied processes, Subcommittee SC 5, Testing and inspection of welds.This third edition cancels and replaces
22、the second edition (ISO 4136:2001), which has been technically revised.iv ISO 2012 All rights reservedBS EN ISO 4136:2012INTERNATIONAL STANDARD ISO 4136:2012(E)Destructive tests on welds in metallic materials Transverse tensile test1 ScopeThis International Standard specifies the sizes of test speci
23、men and the procedure for carrying out transverse tensile tests in order to determine the tensile strength and the location of fracture of a welded butt joint.This International Standard applies to metallic materials in all forms of product with joints made by any fusion welding process.Unless other
24、wise specified for specific points in this International Standard, the general principles of ISO 6892-1 and ISO 6892-2 apply.2 Normative referencesThe following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For unda
25、ted references, the latest edition of the referenced document (including any amendments) applies.ISO 4063:2009, Welding and allied processes Nomenclature of processes and reference numbersISO 6892-1, Metallic materials Tensile testing at ambient temperature Part 1: Method of test at room temperature
26、ISO 6892-2, Metallic materials Tensile testing at ambient temperature Part 2: Method of test at elevated temperature3 PrincipleAn increasing tensile load is continuously applied until rupture occurs in a test specimen taken transversely from a welded joint.Unless otherwise specified, the test shall
27、be carried out at ambient temperature (23 5) C.4 Symbols and abbreviated termsThe symbols and abbreviated terms to be used for the transverse tensile tests are specified in Table 1 and represented in Figures 1 to 3. ISO 2012 All rights reserved 1BS EN ISO 4136:2012ISO 4136:2012(E)Table 1 Symbols and
28、 abbreviated termsSymbol Term Unitb Width of the parallel length mmb1Width of shoulder mmd Diameter of the plug mmD Outside diameter of the pipe ammLcParallel length mmLoOriginal gauge length mmLsMaximum width of the weld after machining mmLtTotal length of the test specimen mmr Radius of shoulder m
29、mt Thickness of the welded joint mmtsThickness of the test specimen mmaThe term “pipe”, alone or in combination, is used to mean “pipe”, “tube” or “hollow section (without rectangular cross section)”.5 Preparation of test specimens5.1 LocationThe test specimen shall be taken transversely from the we
30、lded joint in such a way that, after machining, the weld axis remains in the middle of the parallel length of the test specimen. For small diameter pipes, the test may be carried out on whole pipe (see Figure 3). If not specified by the application standards or agreed upon between the contracting pa
31、rties, “small diameters” means D 8 mm. If thermal cutting or other cutting methods which could affect the cut surfaces are used to cut the test specimen from the welded plate or from the test piece, the cuts shall be made at a distance 8 mm from the surfaces of the final parallel length of the test
32、specimen. Thermal cutting shall not be used parallel to the original surface of the welded plate or of the test piece.5.4.3 Other metallic materialsShearing and thermal cutting are excluded, and only machining (e.g. sawing or milling) shall be used.5.5 Machining5.5.1 GeneralThe tolerances specified
33、in ISO 6892-1 and ISO 6892-2 shall apply.5.5.2 LocationIn general, the thickness of the test specimen, ts, shall be equal to the thickness of the parent metal near the welded joint see Figure 1 a). When a relevant application standard requires testing of the full thickness 30 mm, several test specim
34、ens may be taken to cover the full thickness of the joint see Figure 1 b). In such cases, the location of the test specimen in the welded joint thickness shall be identified.a) Full section testb) Multi specimen testNOTE The test pieces may overlap.Figure 1 Examples of the location of test specimens
35、 in joints5.5.3 Dimensions5.5.3.1 Plates and pipesThe thickness of the test specimen shall be constant along the parallel length, Lc; the shape and dimensions shall conform to those given in Table 2 with reference to the symbols shown in Figure 2. ISO 2012 All rights reserved 3BS EN ISO 4136:2012ISO
36、 4136:2012(E)For the test specimen machined from pipe, flattening of the gripped ends may be necessary; however, this flattening and the possible resulting variation in thickness shall not affect the parallel length, Lc.Table 2 Dimensions for plates and pipesDimensions in millimetresDenomination Sym
37、bol DimensionsTotal length of the test specimen Ltto suit particular testing machineWidth of shoulder b1b + 12Width of the parallel lengthplates b12 for ts 225 for ts 2pipes b6 for D 5012 for 50 168,3Parallel length a bLc Ls+ 60Radius at shoulder r 25aFor pressure welding and beam welding (process g
38、roups 2, 4, and 5 in accordance with ISO 4063:2009), Ls= 0.bFor some other metallic materials (e.g. aluminium, copper and their alloys) Lc Ls+ 100 may be necessary.a) Test specimen for plates4 ISO 2012 All rights reservedBS EN ISO 4136:2012ISO 4136:2012(E)b) Test specimen for pipesFigure 2 Test spec
39、imens for plates and pipes5.5.3.2 Full section pipesThe dimensions for full section pipe test specimens are shown in Figure 3. ISO 2012 All rights reserved 5BS EN ISO 4136:2012ISO 4136:2012(E)Figure 3 Tensile test specimen for full section pipe5.5.3.3 Solid sectionsDimensions of test specimen from s
40、olid sections shall be agreed between the contracting parties. Where machined cylindrical test specimens are required, the dimensions shall be as in ISO 6892-1 and ISO 6892-2, except that the parallel length, Lc, shall be not less than Ls+ 60 mm, as shown in Figure 4.For aluminium, copper and their
41、alloys, refer to footnote bto Table 2.6 ISO 2012 All rights reservedBS EN ISO 4136:2012ISO 4136:2012(E)Figure 4 Cylindrical test specimen for solid section5.5.4 Surface preparationThe final stages of preparation shall be performed by machining or grinding, suitable precautions being taken to avoid s
42、uperficial strain hardening or excessive heating of the material. The surfaces shall be free from scratches or notches transverse to the test specimen direction in the parallel length, Lc, except for undercut which shall not be removed unless required by the relevant application standard.The surface
43、s of the test specimen shall be machined in such a way that, unless specified otherwise in the relevant application standard, all excess weld metal is removed. Unless specified otherwise the penetration bead shall be left intact inside full section pipes.6 Test procedureThe test specimen shall be lo
44、aded gradually and continuously in accordance with ISO 6892-1 and ISO 6892-2.7 Test results7.1 GeneralThe test results shall be determined in accordance with ISO 6892-1 and ISO 6892-2.7.2 Location of fractureThe location of the fracture shall be noted and reported.If necessary, the side of the test
45、specimen may be macroetched to assist location of the weld.7.3 Examination of fracture surfacesAfter rupture of the test specimen, the fracture surfaces shall be examined and the existence of any imperfections that may have adversely affected the test shall be recorded, including their type, size an
46、d quantity. If fish eyes are present, they shall be recorded and only their central regions shall be considered as imperfections.8 Test reportThe test report shall include the following information in addition to that given in ISO 6892-1 and ISO 6892-2. reference to this International Standard i.e.,
47、 ISO 4136; ISO 2012 All rights reserved 7BS EN ISO 4136:2012ISO 4136:2012(E) type and location of test specimen, sketch if required (see Figure 1); test temperature if outside the ambient temperature; location of fracture; type and dimensions of imperfections observed.An example of a typical test re
48、port is given in Annex A.8 ISO 2012 All rights reservedBS EN ISO 4136:2012ISO 4136:2012(E)Annex A (informative) Example of a test reportNo. According to pWPS According to test result “tensile test”test result “ ” Manufacturer: Purpose of the examination: Form of product: Parent metal: Filler metal:
49、Test temperature: Table A.1 Transverse tensile test in accordance with ISO 4136Test specimen No./positionDimension/ diameter mmMaximum load FmNUltimate tensile strength RmN/mm2Location of fractureRemark e.g. fracture appearanceExaminer or test body: Certified by:(name, date and signature) (name, date and signature) ISO 2012 All rights reserved 9This page deliberately left blankThis page deliberately left blankBSI is the independent national body responsible for preparing British Standards