1、PUBLISHED DOCUMENTPD CEN ISO/TR 20880:2007Footwear Performance requirements for components for footwear OutsolesICS 61.060g49g50g3g38g50g51g60g44g49g42g3g58g44g55g43g50g56g55g3g37g54g44g3g51g40g53g48g44g54g54g44g50g49g3g40g59g38g40g51g55g3g36g54g3g51g40g53g48g44g55g55g40g39g3g37g60g3g38g50g51g60g53g
2、44g42g43g55g3g47g36g58PD CEN ISO/TR 20880:2007This Published Document was published under the authority of the Standards Policy and Strategy Committee on 30 March 2007 BSI 2007ISBN 978 0 580 50447 1National forewordThis Published Document was published by BSI. It is the UK implementation of CEN ISO/
3、TR 20880:2007.The UK participation in its preparation was entrusted to Technical Committee TCI/69, Footwear, leather and coated fabrics.A list of organizations represented on TCI/69 can be obtained on request to its secretary.This publication does not purport to include all the necessary provisions
4、of a contract. Users are responsible for its correct application. Amendments issued since publicationAmd. No. Date CommentsTECHNICAL REPORTRAPPORT TECHNIQUETECHNISCHER BERICHTCEN ISO/TR 20880February 2007ICS 61.060English VersionFootwear - Performance requirements for components forfootwear - Outsol
5、es (ISO/TR 20880:2007)Chaussures - Exigences de performance pour lescomposants des chaussures - Semelles dusure (ISO/TR20880:2007)Schuhe - Anforderungen an das Gebrauchsverhalten vonSchuhbestandteilen - Laufsohlen (ISO/TR 20880:2007)This Technical Report was approved by CEN on 21 August 2006. It has
6、 been drawn up by the Technical Committee CEN/TC 309.CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland,France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Po
7、land, Portugal,Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATIONCOMIT EUROPEN DE NORMALISATIONEUROPISCHES KOMITEE FR NORMUNGManagement Centre: rue de Stassart, 36 B-1050 Brussels 2007 CEN All rights of exploitation in any form and by an
8、y means reservedworldwide for CEN national Members.Ref. No. CEN ISO/TR 20880:2007: EForeword This document (CEN ISO/TR 20880:2007) has been prepared by Technical Committee CEN/TC 309 “Footwear“, thesecretariat of which is held by AENOR, in collaboration with Technical Committee ISO/TC 216 “Footwear“
9、.CEN ISO/TR 20880:2007Reference numberISO/TR 20880:2007(E)TECHNICAL REPORT ISO/TR20880First edition2007-02-15Footwear Performance requirements for components for footwear OutsolesChaussures Exigences de performance pour les composants des chaussures Semelles dusure CEN ISO/TR 20880:2007ii iiiContent
10、s Page Foreword iv 1 Scope . 1 2 Normative references . 1 3 Terms and definitions. 2 4 Requirements 2 4.1 General. 2 4.2 Performance requirements for outsoles components for general purpose sports footwear. 2 4.3 Performance requirements for outsoles components for school footwear . 4 4.4 Performanc
11、e requirements for outsoles components for casual footwear 6 4.5 Performance requirements for outsoles components for mens town footwear . 8 4.6 Performance requirements for outsoles components for cold weather footwear. 9 4.7 Performance requirements for outsoles components for womens town footwear
12、 10 4.8 Performance requirements for outsoles components for fashion footwear 11 4.9 Performance requirements for outsoles components for infants footwear 13 4.10 Performance requirements for outsoles components for indoor footwear 14 5 Marking and labelling . 15 CEN ISO/TR 20880:2007iv Foreword ISO
13、 (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical com
14、mittee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrot
15、echnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the mem
16、ber bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. In exceptional circumstances, when a technical committee has collected data of a different kind from that which is normally published as an International Standard (
17、“state of the art”, for example), it may decide by a simple majority vote of its participating members to publish a Technical Report. A Technical Report is entirely informative in nature and does not have to be reviewed until the data it provides are considered to be no longer valid or useful. Atten
18、tion is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO/TR 20880 was prepared by the European Committee for Standardization (CEN) Technical Committee CEN/TC 3
19、09, Footwear, in collaboration with Technical Committee ISO/TC 216, Footwear, in accordance with the Agreement on technical cooperation between ISO and CEN (Vienna Agreement). CEN ISO/TR 20880:20071Footwear Performance requirements for components for footwear Outsoles 1 Scope This Technical Report e
20、stablishes the performance requirements for outsoles components for footwear (not for the finished footwear), irrespective of the material, in order to assess the suitability for the end use. It also establishes the test methods to be used to evaluate the compliance with the requirements. This Techn
21、ical Report applies to outsoles for all kind of footwear as defined in Clause 3. This Technical Report is intended to be used as a reference between the footwear manufacturer and the supplier. It is not intended for third party certification of finished shoes destined for the consumer. 2 Normative r
22、eferences The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 31-0, Quantities and units Part 0:
23、General principles EN ISO 5404, Leather Physical and mechanical tests Determination of the water resistance of heavy leathers EN ISO 17707, Footwear Test methods for outsoles Flex resistance ISO 17709, Footwear Sampling location, preparation and duration of conditioning of samples and test pieces EN
24、 ISO 19952, Footwear Vocabulary ISO 20865, Footwear Test methods for outsoles Compression energy ISO 20869, Footwear Test methods for outsoles, insoles, lining and insocks Water soluble content ISO 20871, Footwear Test methods for outsoles Abrasion resistance ISO 20872, Footwear Test methods for out
25、soles Tear strength ISO 20873, Footwear Test methods for outsoles Dimensional stability ISO 20874, Footwear Test methods for outsoles Needle tear strength ISO 20875, Footwear Test methods for outsoles Determination of split tear strength and delamination resistance EN 1391, Adhesives for leather and
26、 footwear materials A method for evaluating the bondability of materials Minimum requirements and material classification CEN ISO/TR 20880:20072 EN 1392, Adhesives for leather and footwear materials Solvent-based and dispersion adhesives Test methods for measuring the bond strength under specified c
27、onditions EN 13287, Personal protective equipment Footwear Test method for slip resstance 3 Terms and definitions For the purposes of this document, the terms and definitions given in EN ISO 19952 apply. 4 Requirements 4.1 General This Technical Report establishes two different types of performance
28、requirement. The essential requirements shall all be taken into account. The additional ones can be additionally agreed by the component supplier and the footwear manufacturer as indicated in the subclauses 4.2 to 4.10. The results of each single analytical determination, as well as the average valu
29、es, shall be rounded off in accordance with ISO 31-0. When taken from finished footwear, the sample shall be prepared in accordance with ISO 17709. 4.2 Performance requirements for outsoles components for general purpose sports footwear 4.2.1 Essential requirements These essential requirements shall
30、 be fulfilled in all cases. See Table 1. Table 1 Test method and properties for general sports footwear Essential requirements Test method Property Requirement EN ISO 17707 Flex resistance cut growth u 4,0 mm, and no spontaneous crack ISO 20871 Abrasion resistance 0,9 g/cm3u d u 200 mm30,9 g/cm3 d u
31、 150 mg ISO 20875 Delamination resistance or split tear a0,9 g/cm3u d W 3,0 N/mm 0,9 g/cm3 d W 1,7 N/mm EN 13287 Slip resistance bW 0,30 (flat slip) W 0,28 (heel slip) In both cases must be tested using ceramic tiles (floor) and water and detergent (lubricant) aThis requirement is considered essenti
32、al only in multilayer outsoles. bThis test method is only applicable for finished footwear. CEN ISO/TR 20880:200734.2.2 Additional requirements These additional requirements should be agreed by both component supplier and footwear manufacturer. See Table 2. Table 2 Test method and properties for gen
33、eral sports footwear Additional requirements Subclause Test method Property Requirement 4.2.2.1 ISO 20873 Dimensional stability u 2,5 % 4.2.2.2 ISO 20865 Compression energy W 15 J 4.2.2.3 EN 1392 Bondability a, b, c0,9 g/cm3u d W 4,0 N/mm 0,9 g/cm3 d W 3,0 N/mm 4.2.2.4 ISO 20869 Water soluble substa
34、nces content water soluble matter u 18 % sulfated ashed water soluble u 3 % (applicable only for leather) 4.2.2.5 ISO 20872 Tear strength 0,9 g/cm3u d W 8,0 N/mm 0,9 g/cm3 d W 6,0 N/mm 4.2.2.6 EN/ISO 5404 Water resistance a) Water resistant Penetration time W 30 min and after 30 min water absorption
35、 u 25 % b) Highly water resistant Penetration time W 60 min and after 60 min water absorption u 15 % (only applicable for leather and porous materials) 4.2.2.7 ISO 20874 Needle tear strength dW 40 N/mm aA value below the established will be considered as negative independent of the type of failure.
36、bReference adhesives and reference material shall comply with EN 1391. cThe dimensions and number of test pieces for this test method shall be those included in ISO 17709. dThis requirement is applicable only for sewn footwear. CEN ISO/TR 20880:20074 4.3 Performance requirements for outsoles compone
37、nts for school footwear 4.3.1 Essential requirements These essential requirements shall be fulfilled in all cases. See Table 3. Table 3 Test method and properties for school footwear Essential requirements Test method Property Requirement EN ISO 17707 Flex resistance cut growth u 4,0 mm, and no spon
38、taneous crack ISO 20871 Abrasion resistance 0,9 g/cm3u d u 200 mm30,9 g/cm3 d u 150 mg ISO 20875 Delamination resistance or split tear a0,9 g/cm3u d W 3,0 N/mm 0,9 g/cm3 d W 1,7 N/mm EN 13287 Slip resistance bW 0,30 (flat slip) W 0,28 (heel slip) In both cases must be tested using ceramic tiles (flo
39、or) and water and detergent (lubricant) aThis requirement is considered essential only in multilayer outsoles. bThis test method is only applicable for finished footwear. CEN ISO/TR 20880:200754.3.2 Additional requirements These additional requirements should be agreed by both component supplier and
40、 footwear manufacturer. See Table 4. Table 4 Test method and properties for school footwear Additional requirements Subclause Test method Property Requirement 4.3.2.1 ISO 20873 Dimensional stability u 2,5 % 4.3.2.2 ISO 20865 Compression energy W 15 J 4.3.2.3 EN 1392 Bondability a, b, c0,9 g/cm3u d W
41、 4,0 N/mm 0,9 g/cm3 d W 3,0 N/mm 4.3.2.4 ISO 20869 Water soluble substances content water soluble matter u 18 % sulfated ashed water soluble u 3 % (applicable only for leather) 4.3.2.5 ISO 20872 Tear strength 0,9 g/cm3u d W 8,0 N/mm 0,9 g/cm3 d W 6,0 N/mm 4.3.2.6 EN ISO 5404 Water resistance a) Wate
42、r resistant Penetration time W 60 min and after 60 min water absorption u 15 % b) Highly water resistant Penetration time W 30 min and after 30 min water absorption u 25 % (applicable only for leather and porous materials) 4.3.2.7 ISO 20874 Needle tear strength dW 35 N/mm aA value below the establis
43、hed will be considered as negative independent of the type of failure. bReference adhesives and reference material shall comply with EN 1391. cThe dimensions and number of test pieces for this test method shall be those included in ISO 17709. dThis requirement is applicable only for sewn footwear. C
44、EN ISO/TR 20880:20076 4.4 Performance requirements for outsoles components for casual footwear 4.4.1 Essential requirements These essential requirements shall be fulfilled in all cases. See Table 5. Table 5 Test method and properties for casual footwear Essential requirements Test method Property Re
45、quirement EN ISO 17707 Flex resistance cut growth u 5,0 mm, and no spontaneous crack ISO 20871 Abrasion resistance 0,9 g/cm3u d u 250 mm30,9 g/cm3 d u 170 mg ISO 20875 Delamination resistance or split tear a0,9 g/cm3u d W 3,0 N/mm 0,9 g/cm3 d W 1,7 N/mm EN 13287 Slip resistance bW 0,30 (flat slip) W
46、 0,28 (heel slip) In both cases must be tested using ceramic tiles (floor) and water and detergent (lubricant) aThis requirement is considered essential only in multilayer soles. bThis test method is only applicable for finished footwear. CEN ISO/TR 20880:200774.4.2 Additional requirements These add
47、itional requirements should be agreed by both component supplier and footwear manufacturer. See Table 6. Table 6 Test method and properties for casual footwear Additional requirements Subclause Test method Property Requirement 4.4.2.1 ISO 20873 Dimensional stability u 2,5 % 4.4.2.2 ISO 20865 Compres
48、sion energy W 15 J 4.4.2.3 EN 1392 Bondability a, b, c0,9 g/cm3u d W 3,5 N/mm 0,9 g/cm3 d W 3,0 N/mm 4.4.2.4 ISO 20869 Water soluble substances content water soluble matter u 18 % sulphated ashed water soluble u 3 % (applicable only for leather) 4.4.2.5 ISO 20872 Tear strength 0,9 g/cm3u d W 8,0 N/m
49、m 0,9 g/cm3 d W 6,0 N/mm 4.4.2.6 EN ISO 5404 Water resistance a) Water resistant Penetration time W 30 min and after 30 min water absorption u 25 % b) Highly water resistant Penetration time W 60 min and after 60 min water absorption u 15 % (only applicable for leather and porous materials) 4.4.2.7 ISO 20874 Needle tear strength dW 35 N/mm aA value below the established will be considered as negative independent of the type of failure. bReference adhesives and reference material shall com