1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 10 26 N-STATUS No known use. No Replacement Named D. DiGregorio, NA 2004 05 19 Revised Para 3.0 inserted; para 3.14, 3.15, 3.16 & 4 deleted 1990 02 23 Released NC00E10025638004 (RD) K. Gribble C. Boese Printed copies are uncontrolled Copy
2、right 2009, Ford Global Technologies, LLC Page 1 of 2 LUBRICANT, SYNTHETIC - ELECTRICAL ESA-M2C182-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a synthetic multi-fluid based oil with low capillary action and low evaporation. 2. APPLICATION This specification
3、 was released originally for oil used in the lubrication of electrical and mechanical interfaces of switches. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P
4、1111-A). 3.1 COLOR, max 4 (ISO 2049/ASTM D 1500) 3.2 ODOR Not Unpleasant 3.3 SPECIFIC GRAVITY 0.900 - 0.930 (ISO 2137/ASTM D 217) 3.4 FLASH POINT, min 220 C (ISO 2592/ASTM D 92) 3.5 FIRE POINT, min 230 C (ISO 2592/ASTM D 92) 3.6 POUR POINT, max -40 C (ISO 3016/ASTM D 97) 3.7 KINEMATIC VISCOSITY (ISO
5、 3104/ASTM D 445) 3.7.1 At 40 C 150 - 170 mm2/s 3.7.2 At 100 C, min 19.8 mm2/s 3.8 VISCOSITY INDEX, min 150 (ISO 2909/ASTM D 2270) 3.9 WATER CONTENT, max 0.1% (ISO 3733/ASTM D 95) ENGINEERING MATERIAL SPECIFICATIONESA-M2C182-APrinted copies are uncontrolled Copyright 2009, Ford Global Technologies,
6、LLC Page 2 of 2 3.10 COPPER STRIP CORROSION, max 1b (ISO 2160/ASTM D 130, 3 h at 100 C) 3.11 NEUTRALIZATION NUMBER, max 3.0 (ASTM D 974) 3.12 EVAPORATION LOSS, max 3.0% (ASTM D 972) 3.13 FOAMING CHARACTERISTICS Foaming (ASTM D 892, Sequence 1) Foaming Tendency Stability at at end of 5 min. end of 10 min. blowing period setting period Sequence 1, max 0 mL 0 mL