1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 03 2012 02 16 N Status No replacement named N. Benipal, NA 2005 09 13 Revised Inserted 3.0; deleted 3.1, 3.7 and 4 1963 11 04 Released AS1 #1140 Controlled document at www.MATS Copyright 2012, Ford Global Technologies, LLC Page 1 of 2 GLA
2、ZING PASTE, GRAY VINYL ESB-M99J55-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is an air drying vinyl type glazing paste. 2. APPLICATION This specification was released originally for material used for knife glazing metal defects on automotive bodies and sheet
3、metal parts after priming. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 COMPOSITION 3.2.1 Non-Volatile, min 67% (FLTM BI 102-01) 3.2.1.1 Pigme
4、nt 84 - 88% of non-volatile 3.2.1.2 Vehicle Primarily vinyl resin 3.3 PHYSICAL PROPERTIES 3.3.1 Color Gray 3.3.2 Consistency Soft putty 3.3.3 Weight Per Volume, min 12.5 lb/gal (1.5 kg/l) 3.3.4 Reduction The glaze shall be capable of being reduced to knifing consistency with M-1071, Butyl Alcohol, o
5、r M-97B10, Butyl Cellosolve. ENGINEERING MATERIAL SPECIFICATION ESB-M99J55-A Copyright 2012, Ford Global Technologies, LLC Page 2 of 2 3.4 PANEL PREPARATION (FLTM BI 103-02, Method “C“) Apply subject test material after primer surfacer and before enamel. Sand subject material before spraying enamel.
6、 3.4.1 Drying The glazed surfaces shall air dry satisfactorily for sanding in 5 min. 3.5 ADHESION The material shall adhere firmly to the primer surfacer, and after drying and sanding shall be suitable for receiving and holding enamel color coats. 3.6 WATER IMMERSION, min 240 h (FLTM BI 104-01) The test panel shall not blister, peel, or badly roughen in the glazed area.