FORD ESE-M1L100-A-2003 IGNITION CABLE HIGH TENSION RESISTANCE CORE (FIBER GLASS) SILICONE JACKET AND EPDM INSULATION (8 mm) TO BE USED WITH FORD WSS-M99P1111-A 《带电阻芯(玻璃纤维)硅树脂护套和三.pdf

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2003 04 28 Revised Para 3.0 inserted; Para 3.4, 3.5, 3.6, 3.7, 3.8, 4 deleted 1994 04 13 NE01-E-10127076-125 Revised 3.1, 3.2 EPDM cured 15 minutes at 163 C) 3.3.1 Conductor Insulation (EPDM) Aged 70 h As Re

2、ceived at 177 +/- 2 C Tensile Strength, MPa, min 6.21 5.86 Elongation, %, min 250 95 Hardness, Durometer “A“ 70 85 90 max Hardness Change, max - + 7* ENGINEERING MATERIAL SPECIFICATION ESE-M1L100-A Page 4 of 4 Copyright 2003, Ford Global Technologies, Inc. Dielectric Strength, 21.7 21.7 kV/mm AC, mi

3、n *The change shall not exceed the hardness requirement. 3.3.2 Outer Jacket (Silicone) Aged 70 h As Received at 205 +/- 2 C Tensile Strength, MPa, min 5.86 5.17 Elongation, %, min 250 100 Hardness, Durometer “A“ 65 80 90 max Hardness Change, max - + 15* Dielectric Strength, 19.7 19.7 kV/mm AC, min *The change shall not exceed the hardness requirement.