1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2015 02 03 N Status No replacement named L. Sinclair, NA 2003 01 23 Revised Para 3.0 inserted ; Para 3.1, 3.2, 3.3, 3.10, 3.11, 4 deleted 1992 07 08 DF00E00107002190 Revised para 3.4, 3.5, Updated 1991 01 31
2、 DE00E00107002086 Released J.B. Huebner Page 1 of 2 Copyright 2015, Ford Global Technologies, Inc. ADHESIVE, SILICONE, ADDITION CURING ESF-M2G356-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a one component, primerless, addition curing, silicone adhesive. 2.
3、 APPLICATION This specification was released originally for material used for bonding aluminum to glass-filled polyethylene terephthalate (PET). Other identified applications include bonding alumina ceramics to brass. This adhesive is suitable for bonding adherents with different coefficients of the
4、rmal expansion. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 APPEARANCE/COLOR As specified on Engineering Drawing 3.5 VISCOSITY 100,000 - 200,
5、000 (ASTM D 1084, Brookfield model RVF, mPa.s #6 spindle at 5 rpm) 3.6 TENSILE STRENGTH, min 2.4 MPa (ASTM D 412) Note: Specimens for tensile, elongation, and hardness are to be cured as follows: . Press sheets in ASTM mold 100 mm x 125 mm x 2 mm. . Use a suitable non-silicone mold release to keep c
6、ured rubber from sticking to mold. . Press for one hour at 150 C (1.4 MPa on press). 3.7 ELONGATION, min 150 % (ASTM D 412) ENGINEERING MATERIAL SPECIFICATION ESF-M2G356-A Page 2 of 2 Copyright 2015, Ford Global Technologies, Inc. 3.8 HARDNESS (ASTM D 2240, Shore A scale) 39 - 49 3.9 SHEAR ADHESION 1380 - 3100 kPa (ASTM D 1002) Note: Aluminum specimens for the shear adhesion test shall be degreased and FLP etched. The bond thickness shall be 0.025 - 0.051 mm. Specimens shall be cured for one hour at 150 C.