FORD ESF-M4D298-A-2006 POLYPROPYLENE MOLDING COMPOUND EXTRA HIGH IMPACT TO BE USED WITH FORD WSS-M99P1111-A 《超高抗冲性聚丙烯(PP)成型料 与标准FORD WSS-M99P1111-A一起使用 使用WSS-M4D938-A1》.pdf

上传人:deputyduring120 文档编号:746238 上传时间:2019-01-14 格式:PDF 页数:2 大小:67.70KB
下载 相关 举报
FORD ESF-M4D298-A-2006 POLYPROPYLENE MOLDING COMPOUND EXTRA HIGH IMPACT  TO BE USED WITH FORD WSS-M99P1111-A  《超高抗冲性聚丙烯(PP)成型料  与标准FORD WSS-M99P1111-A一起使用  使用WSS-M4D938-A1》.pdf_第1页
第1页 / 共2页
FORD ESF-M4D298-A-2006 POLYPROPYLENE MOLDING COMPOUND EXTRA HIGH IMPACT  TO BE USED WITH FORD WSS-M99P1111-A  《超高抗冲性聚丙烯(PP)成型料  与标准FORD WSS-M99P1111-A一起使用  使用WSS-M4D938-A1》.pdf_第2页
第2页 / 共2页
亲,该文档总共2页,全部预览完了,如果喜欢就下载吧!
资源描述

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2006 10 13 N-STATUS Replaced by WSS-M4D938-A1 R. Lord 2005 01 25 Revised Inserted 3.0; Deleted 3.11 & 4 1969 06 05 Released (was XF-M4DX78), F6Y-249 Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 POL

2、YPROPYLENE MOLDING COMPOUND, EXTRA HIGH IMPACT ESF-M4D298-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a polypropylene molding compound. 2. APPLICATION This specification was released originally for material used for speedometer cable jacketing. 3. REQUIREME

3、NTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 SPECIFIC GRAVITY, min 0.900 (ASTM D 792) 3.2 TENSILE STRENGTH max load, min 3,000 psi (20.7 MPa) (ASTM D 638,

4、 Speed “C“) Elongation, max load, min 10% 3.3 FLEXURAL MODULUS 55,000 - 100,000 psi (ASTM D 790) (380 - 690 MPa) 3.4 IMPACT STRENGTH, Izod, min 16 ft lb/in (854 J/m) (ASTM D 256, notched) 3.5 HARDNESS - ROCKWELL “R“ 40 - 75 (ASTM D 785) 3.6 DEFLECTION TEMPERATURE, min At 66 psi (455 kPa) 85 C At 264

5、 psi (1820 kPa) 53 C 3.7 STIFFNESS IN FLEXURE 85,000 150,000 psi (ASTM D 747) (590 - 1040 MPa) ENGINEERING MATERIAL SPECIFICATION ESF-M4D298-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.8 MELTING POINT, min 160 C (FLTM BO 021-01) 3.9 FLOW RATE 0.5 - 0.8 g/10 min (ASTM D 1238, Condition “L“) 3.10 MOLDED OR EXTRUDED PARTS Specific requirements for physical properties of molded or extruded parts, when required, shall be specified on the engineering drawings.