1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2006 08 16 Revised Inserted 3.0; Deleted 3.2, 3.3 Removed Inactive ESP-M3D136-A1 1983 05 03 Revised Deleted 3.2; Retyped PCR-868469-P 1980 04 15 Released 733721-P2 Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC
2、Page 1 of 1 PHENOLIC COMPRESSION MOLDING COMPOUND ESP-M3D136-A2 1. SCOPE The material defined by this specification is a mineral filled, heat resistant, phenolic material, impact modified with organic fibers. 2. APPLICATION This specification was released originally for material used as thrust washe
3、rs in automatic transmissions. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 COMPRESSION MOLDED TEST SPECIMENS (As molded without postbake.) 3.
4、1.1 Impact Strength, Izod, notched, min 11 J/m (ASTM D 256) 3.1.2 Specific Gravity 1.55 1.59 (ASTM D 792) 3.1.3 Flexural Strength, min 55 MPa (ASTM D 790) 3.1.4 Tensile Strength, min 35 MPa (ASTM D 638) 3.1.5 Compressive Strength, min 155 MPa (ASTM D 695) 3.1.6 Water Absorption, max 0.2% (ASTM D 570) 3.1.7 Hardness, Rockwell “E“, min 80 (ASTM D 785) 3.1.8 Deflection Temperature, min 190 C (ASTM D 648, 1820 kPa) 3.1.9 Ash, min 28% (FLTM BO 006-02)