1、 ENGINEERING MATERIAL SPECIFICATION DATE Action Revisions Rev. 0 2014 03 18 Released M.Dumitrescu, NA Controlled document at www.MATS Copyright 2014, Ford Global Technologies, LLC Page 1 of 2 FABRIC, SWITCHBACK PATTERN, FLAT WOVEN WRS-M1H1175-A1 28% PCR/PIR, UNLAMINATED 1. SCOPE The material defined
2、 by this specification is a dobby woven polyester face fabric. The material contains 28% PIR/PCR (Post industrial/post consumer) recycled yarn. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for seat inserts on 2016MY Explorer (NA). The fabric
3、was originally approved as backcoated and laminated with foam. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). Materials with recycled content as def
4、ined by WRS-M99P42-A2 (Textile Materials, Identification of Recycled Content) should be used whenever technically feasible. 3.1.1 This specification must contain 28% recycled content as defined by WRS-M99P42-A2. The remaining portion of the material can come from virgin sources. 3.1.2 In addition to
5、 the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-B1/B2/B3/B4 as applicable. 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 10 % tolerance (ASTM D3775) Warp 330 / 10 cm Weft 195 / 10 cm 3.2.2 Fabric Weight, +/- 10 % tolerance (FLTM BN 106-01) Face fabric 310 g/m2
6、Backcoat 35 g/m2 Total 345 g/m2 3.3 COMPOSITION (ASTM D629) Fabric 100% polyester Backcoat Acrylic ENGINEERING MATERIAL SPECIFICATION WRS-M1H1175-A1 Copyright 2014, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION* (ASTM D1244) Warp 167dtexf48 (False Twist PET) x 3 Weft 540dtex f144 (
7、AT 100% recycled PET) 167dtex f48 (FT 100% recycled PET) x 3 3.5 METHOD OF DYEING Solution dyed or as approved by Materials Engineering, 3.6 FINISHED OPERATIONS Washing, drying,back coated or as approved by Materials Engineering. 4. GENERAL INFORMATION The information given below is provided for cla
8、rification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 Purchase departments will ensure that the material defined in this specification and shipped to any one assembly plant will be produced by one supplier only. 4.2 If yarn is locally sourced it must meet the above fabric construction, composition and yarn construction. The fabric must also meet the requirements of WSS-M8P18-B1/B2/B3/B4. 4.3 Global strategy for this fabric is to use tri-laminate/foam & scrim construction in all regions