1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions Rev. 0 2009 09 22 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 1 of 2 FABRIC, CONNECT PATTERN, FLAT WOVEN WRS-M1H1213-A 25% PIR CONTENT 1. SCOPE The material defined by this specifi
2、cation is a Connect pattern, Jaquard, Flat woven bodycloth of good quality and uniform composition. The fabric has min 25% PIR (Post Industrial Recycled yarn) content and it is backcoated. 2. APPLICATION This specification was released originally for material used as a seat fabric, insert applicatio
3、n for 2012 C557. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of: WSS-M8P18-A1/A4. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Mater
4、ials (WSS-M99P1111-A) 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3775) Warp 324 ends/10 cm Fill 180 picks/10 cm 3.2.2 Fabric Weight, +/- 5% tolerance (FLTM BN 106-01) Face Fabric w/backcoat 368 g/m2 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4. Fab
5、ric 100% Polyester Backcoating Acrylic ENGINEERING MATERIAL SPECIFICATIONWRS-M1HXXXX-A Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 16.5 tex (FT yarn polyester) x 3 Fill 75 tex (AT yarn, polyester) x 1 75 tex (AT y
6、arn 100% PIR polyester) x 1 3.5 METHOD OF DYEING Solution dye/yarn-package dye 3.6 FINISHING OPERATIONS Warping, weaving, washing, acrylic treatment, backcoated, lamination 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase department will ensure that the material defined in this specification and shipped to any one assembly plant will be produced by one supplier only.