1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 00 2015 01 22 Released L. Sinclair, NA Controlled document at www.MATS Copyright 2015, Ford Global Technologies, Inc. Page 1 of 3 CARPET, POLYESTER, NON WOVEN, DILOUR, WRS-M3H155-A1 LATEX AND LOW DENSITY POLYETHYLENE BACKED, MOLDABLE 350
2、G/M2 (10.0 OZ) NOMINAL FACE 1. SCOPE The materials defined by this specification are dilour, polyester, non-woven carpets of good quality and uniform composition. This carpet is a solid color matched carpet. 2. APPLICATION This specification was originally released for moldable flipper panel, load f
3、loor and seat back applications in Europe, with a solid color matched face. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS 3.1.1 Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1.2 In addition t
4、o the requirements listed herein, the end-item carpet assembly shall meet all requirements of the WSS-M8P16-B. 3.1.3 Materials used in interior applications must meet the requirements outlined in WSSM99P2222-D1/ latest for Vehicle Interior Environment Quality Materials/Component Performance Requirem
5、ents. Test data must to be provided by the Tier 1 at the appropriate program milestone. 3.1.4 Recycled Content This specification must contain 100% recycled content as defined by WRSM99P42- A2 (Textile Materials, Identification of Recycled Content). 3.2 SAMPLE SELECTION All evaluations shall be cond
6、ucted on test specimens taken from finished roll goods prior to any subsequent operations, such as reheating or molding. Unless otherwise specified in the Performance Specification. 3.3 APPEARANCE (FLTM BI 109-01) The color, pattern, and finish shall match the approved Design Center master sample, o
7、r shall be as specified on the engineering drawing. 3.4 COMPOSITION (ASTM D 629) 3.4.1 Face Fiber Polyester (100% PCR) 3.4.2 Binder Latex ENGINEERING MATERIAL SPECIFICATION WRS-M3H155-A1 Copyright 2015, Ford Global Technologies, Inc. Page 2 of 3 3.4.3 Backing Low Density Polyethylene 3.5 METHOD OF D
8、YEING Solution dyed 3.6 CONSTRUCTION 3.6.1 Fiber Size and Description 6.0 denier (ASTM D 1244) (6.7 dex) 3.6.3 Final Total Thickness 3.0 +/- 0.7 mm (ASTM D 1777) 3.7 WEIGHT (FLTM BN 106-01) 3.7.1 Pile Fiber 315 385 g/m2 9.3 11.4 (oz) 3.7.2 Binder 72 88 g/m2 2.1 2.6 (oz) 3.7.3 Backing 81 99 g/m2 2.40
9、 2.92 (oz) 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 DRAWING CALL OUT The following shall be called out on the Engineeri
10、ng drawing to correctly designate the approved material. WRS-M3H155-A1 Supplier Name and Product Code WSS-M8P16-B 5. SUMMARY OF REVISIONS ENGINEERING MATERIAL SPECIFICATION WRS-M3H155-A1 Copyright 2015, Ford Global Technologies, Inc. Page 3 of 3 Non Woven Carpet Construction Supplement Supplier _Sup
11、plier Contact Name_ Number _ Product/ Style Name _ Material Specification _ Performance Specification _ Supplier Product Code _ Manufacturing Location _ Supplier Lab Number _ Supplier Lab Date _ Composition Type Supplier Face Fiber ASTM D276 _ _ Binder Fiber ASTM D276 _ _ Fabric Backing ASTM D276 _
12、_ Pre Coat ASTM D276 _ _ Primary Backing ASTM D276 _ _ Secondary Backing ASTM D276 _ _ Construction Solution or piece dyed (circle one) Percent PIR/PRC _ Denier _ Face Fiber Thickness ISO 1765 _+/- _ mm Binder Fiber Thickness ISO 1765 _+/- _ mm Pre Coating Thickness ISO 1765 _+/- _ mm Primary Thickn
13、ess ISO 1765 _+/- _ mm Secondary Thickness ISO 1765 _+/- _ mm Mass per Unit Area Weight Face Fiber ASTM D5848 _+/- _ g/m2 Binder Fiber ASTM D5848 _+/- _ g/m2 Pre Coating ASTM D5848 _+/- _ g/m2 Primary Backing ASTM D5848 _+/- _ g/m2 Secondary Backing ASTM D5848 _+/- _ g/m2 Materials Engineering Signature _Date _ Comments _ Rolled Goods _ Molded Product _