1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2009 01 06 N-STATUS No Replacement B. Haggart, FNA 2003 03 31 Revised Para 3.0 inserted; Para 3.1, 3.2, 3.10, 3.11, 4 deleted 1994 12 06 Released NB00I10043054404 B. H. Chen A.J.S. Printed copies are uncontr
2、olled Page 1 of 2 Copyright 2009, Ford Global Technologies, Inc. FABRIC, GENTRY PATTERN, KNIT WSB-M1H682-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a Gentry pattern knit bodycloth of good quality and uniform composition. 2. APPLICATION This specification w
3、as released originally for material used as an interior trim fabric for the 1996 DN 101. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of WSB-M8P1-H. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must
4、conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.3 FABRIC CONSTRUCTION 3.3.1 Fabric Count, +/- 5 % tolerance (ASTM D 3887) Wales 14. wales/cm Courses 23.6 courses/cm 3.3.2 Fabric Weight, min 405.0 g/m2(FLTM BN 106-01) 3.4 COMPOSITION (ASTM D 629) Tolerance a
5、s specified in WSB-M8P1-H Fabric 100 % Polyester ENGINEERING MATERIAL SPECIFICATION WSB-M1H682-A Page 2 of 2 Copyright 2009, Ford Global Technologies, Inc. 3.5 YARN CONSTRUCTION (ASTM D 1244) Face (A) 10.6 tex f24 (polyester, dull, trilobal) (B) 10.6 tex f24 (polyester, bright, round) Middle 7.8 tex
6、 f33 (polyester, semi-dul, round) Back 7.8 tex f3 (polyster,semi-dul, round) 3.6 METHOD OF DYEING Piece dyed 3.7 FINISHING OPERATIONS Dye, dry, nap, shear, heatset 3.8 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute 3.9 STRETCH AND SET, %, range (SAE J855) Fabrics outside this range ma
7、y be accepted provided they have been approved jointly by the Materials Engineering activity and the affected Design Engineering and Development activity. Stretch, range Wales Courses 6 - 30 10 - 35 Set, max* Wales Course 12 14 *At no time shall the set exceed 40 % of the measured stretch unless approved jointly by the Materials Engineering activity and the affected Design Engineering and Development activity.