1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2008 11 06 N-STATUS No Replacement L. Schmalz, FNA / M. Montgomery, FOE 2002 11 21 Para 3.0 inserted; Para 3.1, 3.2, 3.3, 3.9, 4 deleted 1992 05 01 C10210837 RELEASED P. Osman Printed copies are uncontrolled
2、 Page 1 of 3 Copyright 2008, Ford Global Technologies, Inc. FABRIC, SONIC DESIGN, WEFT KNITTED, UNLAMINATED WSD-M1H560-A FABRIC, SONIC DESIGN, WEFT KNITTED, 3 mm LAMINATE WSD-M1H560-B1 FABRIC, SONIC DESIGN, WEFT KNITTED, 6 mm LAMINATE WSD-M1H560-B2 FABRIC, SONIC DESIGN, WEFT KNITTED, 6 mm LAMINATE W
3、SD-M1H560-D2 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by these specifications is a Sonic design weft knitted, Jacquard, 20 gauge velour bodycloth or foam laminate of good quality and uniform composition. 2. APPLICATION These specifications were originally released for material use
4、d as interior trim fabrics for the CDW 27. SONIC PLAIN DESIGN WSD-M1H560-A Unlaminated WSD-M1H560-B1 3.0 mm flame laminated to polyether foam and knitted fabric WSD-M1H560-B2 6.0 mm flame laminated to polyether foam and knitted fabric WSD-M1H560-D2 6.0 mm flame laminated to polyether foam 3. REQUIRE
5、MENTS In addition to the requirements listed herein, the fabric or laminate shall meet all requirements of WSB-M8P1-H. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A)
6、 3.4 FACE FABRIC 3.4.1 Fabric Construction 3.4.1.1 Fabric Count, range (ASTM D 3887) Wales 85 +/- 10/cm ENGINEERING MATERIAL SPECIFICATION WSD-M1H560-A/B1/B2/D2 Page 2 of 3 Copyright 2008, Ford Global Technologies, Inc. Courses 115 +/- 15/cm 3.4.1.2 Fabric Weight, range 305 - 330 g/m2(FLTM BN 106-0
7、1) 3.4.2 Composition (ASTM D 629) Fabric 100 % polyester 3.4.3 Yarn Construction (ASTM D 1244) Ground* 167 dTex x 30 - 34 f (polyester, semi-dull) Pile 290 dTex x 68 - 76 f (polyester, bright, texturised, yarn dyed) * Ground construction based on tricot binding. 3.4.4 Method of Dyeing Yarn dyed 3.4.
8、5 Finishing Operations Shear, heatset, inpect 3.5 REQUIREMENTS FOR POLYETHER FOAM 3.5.1 As specified in WSD-M2D243-A2. 3.6 REQUIREMENTS FOR THE BACKING FABRIC 3.6.1 As specified in WSD-M9H134-B. 3.7 REQUIREMENTS FOR THE FLAME LAMINATED MATERIAL 3.7.1 Thickness, range (ASTM D 1777, circular presser f
9、oot area 645 mm2, 2.8 g force, 43 Pa pressure) WSD-M1H560-B1 3.0 +/- 1.0 mm WSD-M1H560-B2 6.0 +/- 1.0 mmWSD-M1H560-D2 5.5 +/- 1.0 mm ENGINEERING MATERIAL SPECIFICATION WSD-M1H560-A/B1/B2/D2 Page 3 of 3 Copyright 2008, Ford Global Technologies, Inc. 3.7.2 Weight, min (FLTM BN 106-01) WSD-M1H560-B1 470 +/- 60 g/m2WSD-M1H560-B2 580 +/- 60 g/m2WSD-M1H560-D2 520 +/- 60 g/m23.8 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute