1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2010 05 25 N-STATUS No replacement named C. Mracna, NA 2004 09 15 Revised Para 3.0 inserted; para 3.1, 3.2, 3.3, 3.10, 3.11 & 4 deleted 1994 12 21 Released C10460355 P. Thomas Printed copies are uncontrolled Copyright 2010, Ford Global Technol
2、ogies, LLC Page 1 of 4 THERMOPLASTIC ELASTOMER (TEO) WSD-M2D379-A4 POLYOLEFIN, EPDM RUBBER MODIFIED 68 DUROMETER A HARDNESS NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a thermoplastic elastomer with a nominal instantaneous Durometer A hardness of 68 having go
3、od long term resistance to heat at temperatures up to 100 C. Being thermoplastic the material will soften and creep at temperatures exceeding 165 C. 2. APPLICATION This specification was released originally for a material used as suspension arm insulator. 3. REQUIREMENTS Material specification requi
4、rements are to be used for initial qualification of materials. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 MOLDED TEST SPECIMEN 3.4.1 Preparation of Test Spe
5、cimens Unless otherwise specified, all tests shall be conducted on specimens die cut from injection molded plaques 150 x 100 x 2.0 +/- 0.2 mm. The plaques shall be molded according to ISO 294 and film gated along the upper 100 mm edge and preceded by a 0.8 mm diameter pin gate. No annealing allowed,
6、 unless specified otherwise. 3.4.2 Density, +/- 0.05 g/cm31.00 (ISO 1183, Method A/ASTM D 792, Method A1) 3.4.3 Hardness, Durometer A 63 - 73 (ISO 868/ASTM D 2240, instantaneous, plied-up specimen.) 3.4.4 Tensile Strength, min 3.3 MPa (ISO R 527, type 2/ASTM D 412, Die C, 500 mm/minute test speed. M
7、easured Parallel to Flow) 3.4.5 Elongation at Break, min 150% (Test acc. to para 3.4.4) ENGINEERING MATERIAL SPECIFICATIONWSD-M2D379-A4 Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 2 of 4 3.4.6 Modulus at 100% Elongation, min 2.5 MPa (Test acc. to para 3.4.4) 3.
8、4.7 Tear Strength, min (ISO 34, Method B, procedure a/ ASTM D 624, Die C, tear direction as below) Parallel to Flow 20 kN/m Perpendicular to Flow 20 kN/m 3.4.8 Compression Set, max (ISO 815, Large Type-plied specimen/ ASTM D 395, Method B, Type 1 plied specimen) 3.4.8.1 22 h at 70 +/- 1 C 70% 3.4.8.
9、2 70 h at 100 +/- 2 C 80% 3.4.9 Brittleness Point, max -50 C (ISO 812, Type B specimen/ ASTM D 2137, Method A) 3.4.10 Ozone Resistance, max Rating 0 (FLTM BP 101-01, Procedure A, tensile specimen, at 20% elongation) 3.5 HEAT AGING (ISO 188/ASTM D 573, 150 +/- 50 air changes/h, 1000 h at 125 +/- 1 C.
10、 Unaged property values shall be determined at the time of the aged properties determination.) 3.5.1 Hardness Change, max +15 3.5.2 Tensile Strength Change, max +/- 25% 3.5.3 Elongation Change, max +/- 30% 3.6 IMMERSION IN OIL NO. 1 (ISO 1817/ASTM D 471, 168 h at 100 +/- 2 C) 3.6.1 Hardness Change,
11、max -50 3.6.2 Tensile Strength Change, max -50% 3.6.3 Elongation Change, max -80% 3.6.4 Volume Change, max +80% ENGINEERING MATERIAL SPECIFICATIONWSD-M2D379-A4 Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 3 of 4 3.7 IMMERSION IN CURRENTLY RELEASED PRODUCTION ENG
12、INE COOLANT 50/50% V/V MIXTURE WITH WATER (FLTM BO 130-01, 1,000 h at 125 +/- 2 C, see Para 5.4) 3.7.1 Hardness Change, max +/- 10 3.7.2 Tensile Strength Change, max +/- 20% 3.7.3 Elongation Change, max -75% 3.7.4 Volume Change, max 0/+10% 3.8 FOGGING (SAE J1756, 3 h at 100 C heating, 21 C cooling p
13、late, post test conditioning 1 h and 16 h) Fog Number, min 70 Formation of clear film, droplets or crystals is cause for rejection. 3.9 FLAMMABILITY (ISO 3795) Burn Rate, max 100 mm/minute The specimen size required for material approval is 355 x 100 x 1.5 +/- 0.1 mm with a smooth surface. 5. GENERA
14、L INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 COEFFICIENT OF LINEAR THERMAL 245 EXPANSION, E-6/C (ASTM D 696) 5.2 MOLD SHRINKAGE (ISO 2577, 150 x 100 x 2.0 +/- 0.2 mm injection molded specimen) ENGINEERIN
15、G MATERIAL SPECIFICATIONWSD-M2D379-A4 Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 4 of 4 5.2.1 Molding Shrinkage After 48 h at 23 +/- 2 C, mm/mm . Length 0.026 . Width 0.019 5.2.2 Post Shrinkage (Separate specimens required for each test) After 48 h at 110 +/-
16、2 C . Length 0.007 . Width 0.007 5.3 HARDNESS, DUROMETER A 60 - 70 (ISO 868/ASTM D 2240, 5 second delay, plied-up specimen) 5.4 For information on currently approved greases for use in this specification contact: Materials Technology Centre, GB 15/GM Fluids Materials Section Product Development Euro
17、pe Greases Dunton Technical Centre Engine Engineering Laindon, Basildon PO BOX 2053 Essex SS15 6EE, England 21500 Oakwood Boulevard Dearborn, MI 48121, USA Materials Engineering Product Engineering Office Ford Motor Co. of Australia Ltd Princes Highway, Norlane Victoria 3214, Australia 5.5 RECYCLING CODE TEO