1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 01 05 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, HIRISE PATTERN, KNIT WSS-M1H1012-A 1. SCOPE The material defined by this specification is a HIRISE PATTERN, 6
2、bars, 44 Gauge, double needle bar knit, body cloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for U387 2007 MY, seat insert. 3. REQUIREMENTS In addition, to the requirements listed herein, the fabric
3、 shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tol
4、erance (ASTM D 3887) Wales 98 wales/10 cm Courses 138 courses/ 10 cm 3.2.2 Fabric Weight, +/- 5% tolerance (FLTM BN 106-01) Laminated * Face w/no Backcoat 547 g/m2441 g/m2* 3 mm foam thickness 3.3 COMPOSITION (ASTM D 629) Fabric 100% Polyester ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1012-A Printed
5、copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 31% 16.7 tex f36 (text polyester) x 1 Middle 19% 16.7 tex f36 (text polyester) x1 11% 3.3 tex f1 Monofilament Back 12% 11.1 tex f34 (text polyester) x 1 27% 11.1 tex f34 (text polyester) x1 3.5 METHOD OF DYEING Piece Dye 3.6 FINISHING OPERATIONS Knit, Heat Set, Setmake, Dye, Tenter dry, Inspect