1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 01 09 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, MARTA PATTERN, KNIT WSS-M1H1017-A 1. SCOPE The material defined by this specification is a MARTA PATTERN, 3 ba
2、rs, 28 Gauge, TRICOT knit, body cloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for 2007 P356 seat insert. 3. REQUIREMENTS In addition, to the requirements listed herein, the fabric shall meet all r
3、equirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 38
4、87) Wales 134 wales/10 cm Courses 283 courses/10 cm 3.2.2 Fabric Weight, range, g/m2 (FLTM BN 106-01) Laminated * Face w/no Backcoat 462 - 511 320 - 354 * 3 mm foam thickness 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100% Polyester ENGINEERING MATERIAL SPECIFICATI
5、ONWSS-M1H1017-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 76% 11.1 tex (textured polyester yarn) Middle 3.7% 11.1 tex (textured polyester yarn) Back 21% 11.1tex (textured polyester yarn) 3.5 METHOD OF DYEING Piece Dye and/or solution 3.6 FINISHING OPERATIONS Wash, preset, dye, scutch, heatset, inspect