1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 11 08 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, SHORE RF PATTERN, WARP KNIT WSS-M1H1020-A2 TREATED WITH REPELLANT FINISH 1. SCOPE The material defined by this
2、 specification is a SHORE RF embossed pattern, 4 bars, 56 Gauge, Single Needle bar, body cloth of good quality and uniform composition. The fabric is treated with repellant finish to prevent staining. 2. APPLICATION This specification was released originally for material used as an interior trim fab
3、ric for 2008 U377 MERCURY MARINER seat insert. 3. REQUIREMENTS Material specification requirements are to be used for initial qualification of materials. In addition, to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS
4、 FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Wales 154 wales/10 cm Courses 240 courses/10 cm 3.2.2 Fabric Weight
5、, +/- 5%, g/m2(FLTM BN 106-01) Face w/ no Backcoat 342 Laminated to 3 mm foam 475 ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1020-A2 Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 1
6、00% Polyester Backcoat No backcoat 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 10% 11.1 tex f34 (textured yarn) Middle 10% 11.1 texf34 (textured yarn) Back 56% 11.1 tex f100 (textured yarn) 4th24% 7.8 texf34 (textured yarn) 3.5 METHOD OF DYEING Piece Dye 3.6 FINISHING OPERATIONS Knit, Heat set, Setmake, Dye, Tenter dry, Tenter repellant Emboss, Inspect Note: The fabric is treated with 1% repellant finish to prevent staining caused by water based agents