1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 01 06 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, DUKE II PATTERN, WARP KNIT WSS-M1H1022-A 1. SCOPE The material defined by this specification is a DUKE II patt
2、ern, 4 bars, 56 Gauge, Single Needle bar, body cloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for 2007 P356 seat bolster. 3. REQUIREMENTS In addition, to the requirements listed herein, the fabric
3、shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tole
4、rance (ASTM D 3887) Wales 149 wales/10 cm Courses 195 courses/10 cm 3.2.2 Fabric Weight, +/- 5%, g/m2(FLTM BN 106-01) Face w/ no Backcoat 427 Laminated to 3 mm foam 555 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100% Polyester Backcoat No backcoat ENGINEERING MATER
5、IAL SPECIFICATIONWSS-M1H1022-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 17% 16.7 tex f36 (textured yarn) Middle 17% 16.7 texf36 (textured yarn) Back 42% 16.7 tex f36 (textured yarn) 4th24% 7.8 texf36 (textured yarn) 3.5 METHOD OF DYEING Piece Dye 3.6 FINISHING OPERATIONS Knit, Dye, Heat set, Setmake, Tenter dry, Inspect