1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 05 22 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, ECO-USA PATTERN, FLAT WOVEN 100% POST INDUSTRIAL WSS-M1H1023-A 1. SCOPE The material defined by this specifica
2、tion is an ECO USA pattern, Dobby flat woven bodycloth of good quality and uniform composition. The fabric is made of 100% Post-Industrial yarn. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for the 2007-1/2 U377 Escape Hybrid, seat bolster. 3
3、. REQUIREMENTS Material specification requirements are to be used for initial qualification of materials. In addition to the requirements listed herein, the fabric shall meet all requirements of: WSS-M8P18-A1/A4, as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers an
4、d part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3775) Warp 355 ends/10 cm Fill 245 picks/10 cm 3.2.2 Fabric Weight, +/- 5% tolerance (FLTM BN 106-01) Face Fabric w/ bac
5、kcoat 411 g/m2Laminated to 3mm foam 525 g/m2 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4. Fabric 100% Post- Industrial Polyester Backcoating Acrylic Latex ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1023-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologi
6、es, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp A. 16.7 tex f34 (false twist post industrial polyester yarn) x 2 polyester) x 3 Fill W 16.7 tex f34 (false twist post industrial polyester yarn) x 2 X 33.3 tex f72 (false twist post industrial polyester yarn) x 2 3.5 METHOD OF DYEING Piece Dyed 3.6 FINISHING OPERATIONS Dye, Dry, Backcoat, Dry