1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 0 2012 05 21 Activated R.Kyle, EU Controlled document at www.MATS Copyright 2012, Ford Global Technologies, LLC Page 1 of 2 FABRIC, BIRCH PATTERN, WOVEN JACQUARD, WSS-M1H1073-A UNLAMINATED 1. SCOPE The material defined by this specificat
2、ion is a jacquard woven polyester face fabric. 2. APPLICATION This specification was released originally for material used as an interior trim insert fabric for use in the T6 program. Fabric was developed as a Tri-Laminate. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric sh
3、all meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 10%
4、 (ASTM D3775) Warp 350 ends/10 cm Weft 209 picks/10 cm 3.2.2 Fabric Weight, +/- 10% (FLTM BN 106-01) Face Fabric 369 g/m2 Back Coat 45 g/m2 Total Weight 414 g/m2 3.3 COMPOSITION (ASTM D629) Fabric 100% polyester 3.4 YARN CONSTRUCTION (ASTM D1244) Warp 450dtex f 120 (Air Jet Texturised) ENGINEERING M
5、ATERIAL SPECIFICATION WSS-M1H1073-A Copyright 2012, Ford Global Technologies, LLC Page 2 of 2 Weft 450dtex f 120 300dtex f 72 884dtex f1 (Monofilament) (Air Jet Texturised) 3.5 METHOD OF DYEING Yarn dyed or as approved by Materials Engineering 3.6 FINISHED OPERATIONS Washing, Finishing 4. GENERAL IN
6、FORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 Purchase departments will ensure that materials defined in this specification and shipped t
7、o any one assembly plant will be produced by one supplier only. 4.2 Global strategy is to use Tri-laminate construction in all regions. 4.3 If yarn is locally sourced it must meet the above Fabric Construction, Composition & Yarn construction requirements. The fabric must also meet the requirements of WSS-M8P18-A1/A2/A3/A4.