1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 05 22 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, SURGE PATTERN, FLAT WOVEN WSS-M1H1085-A 1. SCOPE The material defined by this specification is a SURGE pattern
2、 flat Jacquard woven bodycloth of good quality and uniform composition. The fabric is backcoated. 2. APPLICATION This specification was released originally for material used as a seat fabric, insert application for 2008 C170, Focus. 3. REQUIREMENTS Material specification requirements are to be used
3、 for initial qualification of materials. In addition to the requirements listed herein, the fabric shall meet all requirements of: WSS-M8P18-A1/A4. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Producti
4、on Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5 % tolerance (ASTM D 3775) Warp 279 ends/10 cm Fill 213 picks/10 cm 3.2.2 Fabric Weight, +/- 5% tolerance (FLTM BN 106-01) Face Fabric w/backcoat 313 g/m2Laminated w/3mm foam 448 g/m23.3 COMPOSITION (ASTM D 629) Toleranc
5、e as specified in WSS-M8P18-A1/A4. Fabric 100% Polyester Backcoating Acrylic latex ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1085-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp A. 16.7 tex f36 (textured semi-dull polyester) x 2 Fill W 16.7 tex f34 (textured, semi-dull polyester) x 3 X 16.7 tex f48 (textured, solution dye polyester) x 2 3.5 METHOD OF DYEING piece dye/solution dye 3.6 FINISHING OPERATIONS woven, wash, dye, backcoated