1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 05 22 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, TITANIUM II PATTERN, FLAT WOVEN WSS-M1H1087-A 1. SCOPE The material defined by this specification is a TITANIU
2、M II pattern, Dobby woven, bodycloth of good quality and uniform composition. The fabric is backcoated. 2. APPLICATION This specification was released originally for material used as a seat fabric, bench rear seat insert and side facings application for 2007 P356 Super Duty. 3. REQUIREMENTS Material
3、 specification requirements are to be used for initial qualification of materials. In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Co
4、mpanys Standard Requirements for Production Materials (WSS-M99P1111-A) 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3775) Warp 335 ends/10 cm Fill 193 picks/10 cm 3.2.2 Fabric Weight, +/- 5% tolerance (FLTM BN 106-01) Face Fabric w/backcoat 400 g/m23.3 COMPOSITION (ASTM D 629
5、) Tolerance as specified in WSS-M8P18-A1/A4. Fabric 100% Polyester Backcoating Latex ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1087-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp A. 16.7 tex f34 (false twist polyester) x 3 Fill W 16.7 tex f68 (air textured polyester) x 3 X 16.7 tex f34 (solution dye polyester) x 3 3.5 METHOD OF DYEING piece dye/solution dye 3.6 FINISHING OPERATIONS woven, wash, dye, backcoated