1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 05 22 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, CALVIN PATTERN, KNIT WSS-M1H1093-A 1. SCOPE The material defined by this specification is a CALVIN PATTERN, 4
2、bars, 28 Gauge, TRICOT knit, body cloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for 2007 V127 Econoline seat insert. 3. REQUIREMENTS Material specification requirements are to be used for initial
3、qualification of materials. In addition, to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Product
4、ion Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Wales 138 wales/10 cm Courses 276 courses/10 cm 3.2.2 Fabric Weight, range, g/m2 (FLTM BN 106-01) Laminated * Face w/no Backcoat 440 - 485 315 - 349 * 3 mm foam thickness 3.3 COMPOSITION (ASTM
5、D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100% Polyester ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1093-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 11.1 tex (textured polyester) Middle 11.1 tex (textured polyester) 11.1 tex (textured polyester Back 7.8 tex (textured polyester) 3.5 METHOD OF DYEING Piece Dye/Solution dye 3.6 FINISHING OPERATIONS Wash, preset, dye, heatset, inspect