1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 12 20 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, ORACLE PATTERN, WARP KNIT WSS-M1H1105-A 1. SCOPE The material defined by this specification is a ORACLE PATTER
2、N, 3 bars, 56 Gauge, Single Needle bar, body cloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for 2008 D219 seat bolster. 3. REQUIREMENTS In addition, to the requirements listed herein, the fabric sh
3、all meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolera
4、nce (ASTM D 3887) Wales 154 wales/10 cm Courses 177 courses/10 cm 3.2.2 Fabric Weight, +/- 5%, g/m2(FLTM BN 106-01) Face w/ no Backcoat 330 Laminated to 3 mm foam 449 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100% Polyester Backcoat No backcoat ENGINEERING MATERIA
5、L SPECIFICATIONWSS-M1H1105-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 11.1 tex f34 (textured yarn) Middle 11.1 tex f34 (textured yarn) Back 7.77 tex f36 (wd yarn) 3.5 METHOD OF DYEING Piece Dye 3.6 FINISHING OPERATIONS Knit, Heat set, Setmake, Dye, Tenter dry, Inspect