1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2016 05 12 N Status No replacement named D. Murtonen, NA 2007 09 14 Activated L. Neves Copyright 2016, Ford Global Technologies, LLC Page 1 of 2 FABRIC, KENT DARK GRAPHITE PATTERN, PILE WARP WSS-M1H1124-A KNITTED POLYESTER NOT TO BE USED FOR
2、NEW DESIGN 1. SCOPE The material defined by this specification is a pile warp knitted polyester fabric. 2. APPLICATION This specification was released originally for material used as an interior trim fabric. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all req
3、uirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, range (ASTM D 3775) War
4、p 14 - 16 yarn/cm Fill 8.5 9.5 yarn/cm 3.2.2 Fabric Weight, range (FLTM BN 106-01) Seat (laminated to 4.5 mm foam + backing fabric) 350 450 g/m 3.3 COMPOSITION (ASTM D 629) Fabric 100% Polyester Foam Seat PUR/Polyether - D28 Backing Fabric 100% Polyester 65 g/m ENGINEERING MATERIAL SPECIFICATION WSS
5、-M1H1124-A Copyright 2016, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 200 dtex, Semi Dull, Round, False Twist Polyester 3.5 METHOD OF DYEING Warp Yarn Dyed and Solution Dyed 3.6 FINISHING OPERATIONS Heat Set 3.7 THICKNESS, mm, range (ASTM D 1777) Seat (laminat
6、ed to 4.5 mm foam + backing fabric) 3.5 5.0 mm 3.8 TRIMMABILITY PROPERTIES 3.8.1 Stretch, %, range (SAE J855) Seat Warp 10 20% Fill 30 40% 3.9 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase departments will ensure that material defined in this specification and shipped to anyone assembly plant will be produced by one supplier only.