1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2007 10 17 Activated M. Griebeler/L. Neves Printed copies are uncontrolled Copyright 2007, Ford Global Technologies, LLC Page 1 of 2 FABRIC, KENT EBONY BLACK PATTERN, PILE WARP KNITTED WSS-M1H1125-A POLYESTER, ANTI-STATIC FINISH 1. SCOPE The m
2、aterial defined by this specification is Pile Warp Knitted Polyester fabric. 2. APPLICATION This specification was released originally for material used as an interior trim fabric (seats and door panels) for Ranger 2009 Model Year. 3. REQUIREMENTS In addition to the requirements listed herein, the f
3、abric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count,
4、 range (ASTM D 3775) Warp 14.0 16.0 yarn/cm Fill 8.5 10.5 yarn/cm 3.2.2 Fabric Weight, range (FLTM BN 106-01) 350 450 g/m 3.3 COMPOSITION (ASTM D 629) Fabric 100% Polyester Foam PUR/Polyester D28 Backing Fabric 100% Polyester 65 g/m ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1125-A Printed copies are
5、uncontrolled Copyright 2007, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 200 dtex, Semi Dull, Round, False Twist Polyester 3.5 METHOD OF DYEING Warp Yarn Dyed and Solution Dyed 3.6 FINISHING OPERATIONS Heat Set 3.7 THICKNESS, mm, range (ASTM D 1777) (laminated
6、to 4.5 mm foam + backing fabric) 3.5 - 5.0 mm 3.8 TRIMMABILITY PROPERTIES 3.8.1 Stretch, %, range (SAE J855) Warp 10.0 - 20.0% Fill 30.0 - 40.0% 3.9 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase departments will ensure that material defined in this specification and shipped to anyone assembly plant will be produced by one supplier only.