1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 01 29 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 1 of 2 FABRIC, CARA PATTERN, KNIT WSS-M1H1141-A 1. SCOPE The material defined by this specification is CARA PATTERN, 4 bars,
2、28 Gauge, TRICOT knit, body cloth of good quality and uniform composition. The fabric is printed for a special pattern. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for 2010 CD334 Mercury Lux seat insert. 3. REQUIREMENTS In addition, to the r
3、equirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTR
4、UCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Wales 133 wales/10 cm Courses 196 courses/10 cm 3.2.2 Fabric Weight, range, g/m2 (FLTM BN 106-01) Laminated * Face w/no Backcoat 456 - 504 370 - 335 * 3 mm foam thickness 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4
5、Fabric 100% Polyester ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1141-A Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Face (A) 13.3 tex( natural polyester) (B) 7.78 tex( natural polyester) Middle 7.78 tex (natural polyester) Back 7.78 tex (natural polyester) 3.5 METHOD OF DYEING Piece Dye 3.6 FINISHING OPERATIONS Wash, preset, dye, set, print, set, inspect