1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions Rev. 0 2010 01 15 Activated M. Dumitrescu, NA Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 1 of 2 FABRIC, GREENWICH LT PATTERN, WARP KNIT WSS-M1H1146-A2 DOOR INSERT 1. SCOPE The material defined by this sp
2、ecification is a GREENWICH LT PATTERN, 3 bars, 28 Gauge, warp knit, body cloth of good quality and uniform composition. The fabric is approved as laminated with polyether urethane foam. 2. APPLICATION This specification was released originally for material used for B299N door insert, as light weight
3、 fabric to match the seat fabric appearance. 3. REQUIREMENTS In addition, to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys
4、Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Wales 200 wales/10 cm Courses 130 courses/10 cm 3.2.2 Fabric Weight, +/- 5%, g/m2 (FLTM BN 106-01) Face fabric 180 3.3 COMPOSITION (ASTM D 629) Tolerance as spe
5、cified in WSS-M8P18-A1/A4 Fabric 100% Polyester ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1146-A2 Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 7.5 tex f36 (semi-dull, false twist sol dye yarn) Middle 5 tex f24 (semi
6、-dull, solution dye yarn) Back 5 tex f24 (semi-dull, solution dye yarn) 3.5 METHOD OF DYEING Piece Dye / solution dye 3.6 FINISHING OPERATIONS Washing, heat-setting, heat-setting 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase department will ensure that the material defined in this specification and shipped to any one assembly plant will be produced by one supplier only.