1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 0 2014 08 29 Released M.Fontes - SA Controlled document at www.MATS Copyright 2014, Ford Global Technologies, LLC Page 1 of 2 FABRIC, VIGO GLOBAL PATTERN, WARP KNITTED, UNLAMINATED WSS-M1H1185-A1 1. SCOPE The material defined by this spe
2、cification is a warp knitted polyester face fabric. 2. APPLICATION This specification was released originally for material used as an interior trim bolster fabric for use in the B-515 program. The fabric was approved laminated with foam and backing fabric/scrim. 3. REQUIREMENTS 3.1 STANDARD REQUIREM
3、ENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.1.1 WSS-M1H1185-A1 is based on virgin materials. 3.1.2 In addition to the requirements listed herein, the fabric shall meet all requirem
4、ents of WSS-M8P18-B1/B2/B3/B4 as applicable. 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 10% (ASTM D3775) Warp 115 ends/10 cm Weft 205 picks/10 cm 3.2.2 Fabric Weight, +/- 10% (FLTM BN 106-01) Face Fabric 228 g/m2 3.3 COMPOSITION (ASTM D629) Fabric 100% polyester ENGINEERING MATERIAL SPECIFICATI
5、ON WSS-M1H1185-A1 Copyright 2014, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D1244) Warp 43 dtex, f24 - Semi dull, round, flat Weft 110 dtex, f48 - Semi dull, round, texturized 3.5 METHOD OF DYEING Solution Dye or as approved by Materials Engineering 3.6 FINISHED OPERATION
6、S Washing / Heat setting or as approved by Materials Engineering 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 Purchase depa
7、rtments will ensure that materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only. 4.2 Global strategy is to use Tri-laminate construction in all regions. 4.3 If yarn is locally sourced it must meet the above Fabric Construction, Composition & Yarn construction requirements. The fabric must also meet the requirements of WSS-M8P18-B1/B2/B3/B4.