1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2016 05 16 N Status No replacement named D. Murtonen, NA 2009 05 28 Activated V. Demarchi Copyright 2016, Ford Global Technologies, LLC Page 1 of 2 FABRIC, MUNIQUE PATTERN, WOVEN JACQUARD, UNLAMINATED WSS-M1H1204-A NOT TO BE USED FOR NEW DESI
2、GN 1. SCOPE The material defined by this specification is a woven jacquard polyester face fabric. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for 2010 BV226 Seat. 3. REQUIREMENTS In addition, to the requirements listed herein, the fabric sha
3、ll meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% toleran
4、ce (ASTM D 3887) Warp 30.0 yarn/cm Fill 19.0 yarn/cm 3.2.2 Fabric Weight, +/- 10%, g/m 316 (face fabric) (FLTM BN 106-01) Face w/no Back coat 284 348 Laminated* 427 523 * 1,5 mm thickness ( foam + backing fabric ) 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100% Pol
5、yester Backing Fabric (Seats only) 100% Polyester ENGINEERING MATERIAL SPECIFICATION WSS-M1H1204-A Copyright 2016, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 598 dtex, Semi dull, Round, Air Textured, Polyester Weft 390 dtex, Semi dull, Round, False Twist Polye
6、ster Weft 390 dtex, Bright, Multilobal, False Twist Polyester 3.5 METHOD OF DYEING Warp Solution Dye Weft Solution Dyed and Yarn Dyed 3.6 FINISHING OPERATIONS Heat-Setting 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only